Kaoumi, Djamel

Publications and source records attributed to Kaoumi, Djamel.

29 records · Page 2
All sourcesNASA NTRSDOE OSTI
DOE OSTI2021

Creep properties of advanced austenitic steel 709 determined through short experiments under in-situ neutron diffraction followed by TEM characterization

Here in this study, the creep mechanisms at play in Alloy 709 (Fe-20Cr-25Ni) are investigated by performing short-term creep-type tests under in-situ neutron diffraction experiments. Short tests are performed in the temperature range of 500 to 900 °C under constant load with a load ranging from 50 to 150 MPa. The creep exponent and activation energy are determined using the Bird-Mukherjee-Dorn relation and compared to that obtained from conventional longer creep tests from the literature. Scanning transmission electron microscopy (S/TEM) of the post-creep microstructure indicates that interaction of dislocations with precipitates are a dominant mechanism at play. Furthermore, local elemental mapping indicated chemical segregation at grain boundaries and formation of complex precipitates.

36 MATERIALS SCIENCE↗
DOE OSTI2021

In Situ Grain Growth of Nanograined Magnetite under Ion Irradiation at Room Temperature and 500 ℃

Grain growth studies of nanograined metals under both thermal and ion irradiation conditions has been studied extensively. Oxides, on the other hand, have not been studied as extensively, especially under irradiation. Some studies have focused on nanograined oxide grain growth on ZnO under thermal conditions only and on SnO 2 and CeO 2 using 250 keV Ar 2+ and 3 MeV Au + ions at 300 K, respectively. There does not appear to be any studies on grain growth of nanosized oxides which are commonly found to form under light water reactor conditions. Oxides such as magnetite (Fe 3 O 4 ), hematite (α-Fe 2 O 3 ), maghemite (γ-Fe 2 O 3 ), and wustite (FeO) are examples of common oxides which have not been studied. Here, this study focused on the grain growth of nanograined Fe 3 O 4 under both thermal and ion irradiation conditions in situ inside a Transmission Electron Microscope (TEM) to better understand the kinetics of grain growth of oxides.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Electrochemical study of the dissolution of oxide films grown on type 316L stainless steel in molten fluoride salt

The corrosion behavior of oxide films grown on Type 316L stainless steel (SS) in molten FLiNaK (LiF-NaF-KF: 46.5−11.5−42 mol.%) salt was investigated. The results show that the oxide film formed on Type 316L SS is unstable and can only temporarily protect materials from corrosion in molten FLiNaK salt. Based on the electrochemical impedance spectroscopy, the oxide dissolution rate is calculated to be 0.85 nm/h at 700 °C in molten FLiNaK salt. Finally, after the oxide film dissolved, Cr and Fe are selective dealloyed from the steel, leading to intergranular corrosion of Type 316L SS in molten fluoride salt.

EIS↗
DOE OSTI2021

Helium bubble nucleation and growth in alloy HT9 through the use of in situ TEM: Sequential he-implantation and heavy-ion irradiation versus dual-beam irradiation

The formation of He bubbles in Ferritic/Martensitic steel HT9 is investigated through the use of in situ Transmission Electron Microscopy coupled with He implantation and heavy ion irradiation. Of particular interest is the effect of increasing He appm/dpa ratio on the formation and growth of the bubbles, as well as the effect of the sequential order of ion irradiation i.e. He-pre-implantation followed by heavy-ion irradiation versus true dual-beam irradiation. Finally, the role of He is discussed.

Duemmler, Kai↗
DOE OSTI2020

A pathway to synthesizing single-crystal Fe and FeCr films

Nuclear reactor environments provide a unique scientific and engineering challenge wherein materials must tolerate prolonged exposure to concurrent irradiation, elevated temperatures, and corrosive media. However, uncontrolled variability in material composition and structure often prohibits truly single-variable experiments that can reveal basic aspects of environmental damage. Here, Magnetron sputtering is used to provide a more controlled model system for these fundamental studies, yielding reproducible single-crystal Fe and FeCr thin films containing 8 and 18 at.% Cr. Electron microscopy is used to determine the systematic correlations between growth conditions and the resulting film microstructure and surface morphology. It is found that the substrate temperature and applied radio frequency (RF) bias can be tuned to obtain consistent homogeneous and single crystal films with a minimal amount of Ar impurities from the RF bias process. Epitaxial, single-crystal Fe films are obtained on MgO substrates at 500 °C with 10 Watt (W) RF bias deposition. However, when Cr is alloyed with Fe, higher substrate temperatures (600 °C) and applied RF biases (15 W) are required to achieve a similar epitaxial single-crystal FeCr film. Accelerated molecular dynamics simulations reveal that Cr impedes surface transport, explaining the need for higher temperature and bias during the growth of the Cr-bearing films.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Electrical properties of thermal oxide scales on pure iron in liquid lead-bismuth eutectic

Here, the impedance behavior of pre-oxidized iron in liquid lead-bismuth eutectic (LBE) at 200 °C is studied using electrochemical impedance spectroscopy. The structures and resistance of oxide grown on iron oxidized in air at different temperatures and durations are compared. The results show that the resistance of the oxide film increases with increasing oxidizing temperature, due to the formation of a thicker scale and fewer defects. At the same temperature (600 °C), increasing the oxidation time can also reduce the defect concentration in the oxide film and improve the impedance of the oxide scale in LBE.

42 ENGINEERING↗
DOE OSTI2020

Tensile behavior and microstructural evolution of a Fe-25Ni-20Cr austenitic stainless steel (alloy 709) from room to elevated temperatures through in-situ synchrotron X-ray diffraction characterization and transmission electron microscopy

Uniaxial tensile tests were done on Fe-25Ni-20Cr Austenitic Stainless Steel (Alloy 709) along with in-situ synchrotron measurement at different temperatures (25 degrees C, 500 degrees C, 700 degrees C and 900 degrees C). The X-Ray diffraction data was collected in-situ in order to follow the phases present as well as to derive the dislocation density as a function of strain through peak broadening analysis based on the modified Williamson-Hall method and see how trends are affected as a function of temperature. The XRD data were complemented by TEM and STEM-EDX characterization done on the post-experiment samples to observe the deformed microstructures. Finally, the paper presents a depiction of the tensile behavior of this advanced steel by interpreting the stress-strain curves and the effect of temperature through the information gained by in-situ XRD and TEM observations as well as fractography done ex-situ on the samples tested to rupture.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Dislocation loop evolution in F/M steel T91 under in-situ ion irradiation: Influence of the presence of initial dislocations

Ferritic/Martensitic (F/M) steel T91 was irradiated in-situ to 4 and 10 dpa at 470 °C using 1 MeV Kr 2+ . Additionally, the microstructure evolution under irradiation was followed and characterized by in-situ Transmission Electron Microscopy (TEM), in terms of dislocation loop Burgers vector, average size and density as a function of dose. Furthermore, the influence of the presence of dislocations in the pre-irradiated matrix was investigated by comparing the radiation induced defect evolution in grains with and without initial dislocations.

36 MATERIALS SCIENCE↗
DOE OSTI2020

In situ synchrotron X-ray tomography of 304 stainless steels undergoing chlorine-induced stress corrosion cracking

To understand the mechanisms behind chlorine-induced stress corrosion cracking (CISCC) in 304 stainless steel, synchrotron high energy x-rays were used to perform in-situ x-ray microtomography on a pre-cracked sample under load in a corrosive simulated marine environment. The tomography scans showed the crack morphology evolving into a branching crack around the surface of the sample. Finite element analysis and stress intensity analysis are conducted to explain the observed crack branching.

304 Stainless Steel↗