The evolution of pit morphology and growth kinetics in aluminum during atmospheric corrosion

Abstract Assessing the lifetimes of alloys in humid, corrosive environments requires growth kinetic information regarding individual instances of damage, e.g. pit growth rates. Corrosion rates measured at the continuum scale using mass change convolute the rate of pit nucleation and growth, providing limited information on local kinetics. The current study used in-situ X-ray computed tomography to measure growth rates of individual pits in aluminum over 100 h of exposure in a humid, chloride environment. While pits grew at relatively constant rates over the first hours after nucleation, significant growth-rate nonlinearities subsequently occurred. These were linked to both droplet spreading, which altered the cathode size, and changes in the mode of pit growth. Pit morphology appeared to influence the dominant growth mode and the duration of pit growth. Post-mortem serial sectioning revealed pits preferentially attacked grain-boundary triple junctions and dislocation boundaries.

Noell, Philip J. (ORCID:0000000346998999)↗
DOE OSTI2022

FY2022 Status Report: Cold Spray for Canister SCC Mitigation and Repair

This progress report describes work performed during FY22 at Sandia National Laboratories (SNL) to assess the corrosion performance of cold spray coatings to enable optimization of cold spray for the purposes of mitigation and/or repair of potentially susceptible regions, corrosion, or stress corrosion cracking (SCC) in austenitic stainless steel for spent nuclear fuel (SNF) storage. Of particular concern is SCC, by which a through-wall crack could potentially form in a canister outer wall over time intervals that may be shorter than possible dry storage times. In FY21, initial corrosion explorations of cold spray coating were evaluated and in FY22, an expanded set of cold spray coatings with in-depth analysis of post-exposure accelerated testing was explored. Additionally, relevant atmospheric exposure testing was carried out and initial results are presented herein. The corrosion attack from the accelerated testing and more realistic atmospheric exposures environments were compared to identify potentially deleterious factors for corrosion as well as help to understand the applicability of accelerated testing for cold spray optimization. This initial analysis will help to enable optimization of the corrosion resistance cold spray, one of the more promising coating and repair techniques, for potential application in an SNF environment. Learnings from both are summarized, and implications and future work are presented in this report.

36 MATERIALS SCIENCE↗