Evaluation of an Al-Cu-Zn-Mg Alloy for Wire-Fed Additive Manufacturing

A collaborative research study was conducted to evaluate an experimental Al-Cu-Zn-Mg alloy, designated Al C380H, developed by Arconic Corporation for wire-fed additive manufacturing (AM) techniques such as NASA’s electron beam freeform fabrication (EBF 3 ) process and the wire arc additive manufacturing (WAAM) process. The goal of the study was to determine, based upon metallurgical properties, whether additively manufactured Al C380H represented a viable alternative for applications currently using wrought 7xxx series aluminum. Al 2319 and Al 7075 were also deposited as AM-compatible and non-AM-compatible baselines, respectively. Evaluation was based on tensile, fracture, and corrosion properties. The strength and ductility of Al C380H-T6 materials produced by EBF3 and WAAM were sufficiently lower than typical values for Al 7050-T7 to indicate that additively manufactured Al C380H is not a viable replacement for current parts fabricated with Al 7050, due largely to the significant losses in Zn and Mg and development of porosity during deposition. EBF 3 parameters that reduced porosity, such as increasing electron beam current, higher raster frequency, sharper beam focus, and slower travel speed, augmented de-alloying of fugitive solute. Further enhancement of Zn and Mg content in Al C380H feedstock wire combined with adjustments to deposition conditions to minimize porosity may enable production of Al C380H parts by EBF 3 or WAAM that are viable replacements for current Al 7050 wrought products.

electron beam freeform fabrication (EBF3)↗
NASA NTRS2023

Hot Cracking Behavior and Beam-Induced Grain Refinement in Electron Beam Freeform Fabricated Al 7075

Electron beam freeform fabrication (EBF 3 ) is a high deposition rate, wire-based directed energy deposition (DED) additive manufacturing (AM) process used to print metallic parts in a vacuum environment. While high specific strength 7xxx-series Al alloys are of interest in the aerospace and automotive industries, these alloys suffer from hot cracking issues during fusion welding and AM. In this work, linear deposits of Al 7075 were fabricated with EBF 3 to study the effects of baseplate thickness, preheat temperature, and beam focus on hot cracking behavior. Solidification cracks were observed in the first deposition layer, and by the third layer coalesced into large “macrocracks” running vertically through the build height. Fine, intergranular liquation “microcracks” appeared between macrocracks below the root of the final deposit layer fusion zone. Increasing the substrate preheat temperature from 165°C to 320°C deepened the partially melted zone and resulted in a more than twofold increase in the liquation microcrack density. Analysis of Scheil solidification diagrams revealed that fugitive losses of Zn and Mg during deposition increased the susceptibility to solidification cracking and promoted substrate liquation cracking. Focused electron beam (EB) conditions combined with a high aspect ratio elliptical raster pattern resulted in bands of refined, equiaxed grains. The refined microstructure suppressed solidification macrocracking and caused a nearly fivefold reduction in liquation crack density, demonstrating that beam-induced grain refinement may be a promising low-cost method for reducing hot cracking during AM.

aluminum↗
NASA NTRSDate not supplied

TPSAS-NF1676L-35894-DND

Vision: Enable aircraft with dramatically improved energy efficiency, environmental compatibility, and economic impact for the nation. Mission: Explore and develop viable game-changing concepts, technologies, and tools to improve vehicle and propulsion system energy efficiency and environmental compatibility. Scope: Subsonic fixed-wing commercial transport aircraft.

Karen Taminger↗
NASA NTRSDate not supplied

Developing Materials and Coating Technologies for Mitigation of Lunar Dust Adhesion and Abrasion

In order to support long duration missions on the Moon’s surface, materials resistant to the harsh lunar environment are critically needed. Lunar dust poses a major threat to the durability of components and vehicles due to its fine, jagged morphology and highly abrasive nature, enabling the particles to adhere and embed onto surfaces of components and devices and potentially leading to premature failure. There is significant effort within NASA to develop novel materials and coating technologies to mitigate lunar dust adhesion and abrasion. This effort has been exploring a variety of production routes and examining properties of candidate material systems, including ceramic, metallic and polymeric. Manufacturing methods investigated include ceramic powder processing, additive manufacturing and surface modification via laser ablation patterning of bulk materials and coatings. An overview of ongoing NASA materials and coating research and development efforts to enable lunar surface exploration will be presented.

Materials, Coatings, lunar dust mitigation↗
NASA NTRSDate not supplied

Development and Characterization of the Integrally Stiffened Cylinder (ISC) Process for Launch Vehicles and Aircraft Fuselage Structures

Over the past decade, NASA Langley has led development of the Integrally Stiffened Cylinder (ISC) Process, a near-net shape, flow-forming technology. This innovative process is being evaluated for launch vehicle and commercial aircraft manufacturing. A thick-walled, cylindrical preform is flow-formed in a single operation into a thin-walled barrel with longitudinal stiffeners. The one-piece, stiffened barrels offer a direct replacement for conventional multi-piece welded or riveted structures. A cost-benefit analysis for launch vehicles estimated that the ISC process offers up to a 50% reduction in manufacturing costs and a 10% reduction in mass. NASA, the European Space Agency (ESA), and industry partners have teamed to manufacture 10-ft. diameter aluminum ISCs. The intent is to demonstrate the commercial viability of the process at a scale relevant to the commercial launch and aircraft industries. Development activities will be presented, including process scale-up, formability assessment, microstructural analysis, and mechanical property testing.

ISC, flow forming, near net shape↗
NASA NTRSDate not supplied

Al-Cu-Zn-Mg Alloy for Additive Manufacturing by Electron Beam Deposition

The application of fusion-based additive manufacturing (AM) to aircraft structural components is limited by the lack of high-strength aluminum alloys optimized for AM processing. High strength aluminum alloys (such as 7050-T7451) are difficult to process by AM because of their solidification cracking susceptibility and loss of volatile alloying elements such as Zn and Mg. The performance of a proprietary Al-Cu-Zn-Mg alloy wire feedstock was evaluated for AM utilizing electron beam deposition. Deposit microstructure, composition, occurrence of porosity and cracking, and post-heat treatment tensile and fracture toughness were correlated with deposition parameters. Post-heat treatment strength, ductility, and fracture toughness were lower than typical values for wrought 7050-T7451, related to significant losses of Zn and Mg and to porosity. Recommendations are offered for modifications to wire feedstock composition and adjustments to deposition conditions and heat treatment to enable AM of electron beam deposited material that has strength comparable to 7050-T7451 wrought products.

Al-Cu-Zn-Mg alloy, electron beam deposition, mecha↗
NASA NTRSDate not supplied

Development and Characterization of the Integrally Stiffened Cylinder (ISC) Process for Launch Vehicles and Aircraft Fuselage Structures

Over the past decade, NASA Langley has led development of the Integrally Stiffened Cylinder (ISC) Process, a near-net-shape, flow-forming technology. This innovative process is being evaluated for launch vehicle and commercial aircraft manufacturing. A thick-walled, cylindrical preform is flow-formed using a single operation into a thin-walled barrel with integral longitudinal stiffeners. The one-piece, stiffened barrels offer a direct replacement for conventional multi-piece, welded or riveted structures. A cost-benefit analysis for launch vehicle cryogenic propellant tanks estimated that the ISC process offers up to a 50% reduction in manufacturing costs and a 10% reduction in mass. NASA, the European Space Agency (ESA), and industry partners have teamed to manufacture 3-m(10-ft.) diameter aluminum ISCs. The intent is to demonstrate the commercial viability of the process at a scale relevant to the commercial launch and aircraft industries. Development activities will be presented, including process scale-up, formability assessment, and mechanical property testing.

ISC, flow forming, near net shape↗
NASA NTRSDate not supplied

Developing Materials and Coating Technologies for Mitigation of Lunar Dust Adhesion and Abrasion

In order to support long duration missions on the Moon’s surface, materials resistant to the harsh lunar environment are critically needed. Lunar dust poses a major threat to the durability of components and vehicles due to its fine, jagged morphology and highly abrasive nature, which enables the particles to adhere and embed into surfaces of components and devices potentially leading to premature failure. Consequently, significant effort within NASA aims to develop novel materials and coating technologies to limit lunar dust adhesion and abrasion by exploring a variety of production routes and examining properties of candidate material systems, including ceramic, metallic and polymeric. Manufacturing methods investigated include traditional powder processing, additive manufacturing and surface modification via laser ablation patterning of bulk materials and coatings. An overview of ongoing NASA materials and coating research and development to enable lunar exploration will be presented.

Materials↗
NASA NTRSDate not supplied

NASA’S Current Efforts and Applications of NDE to Improve Space Flight Safety

National Aeronautics and Space Administration (NASA) continues to push the boundary of manned flight. Current mission profiles include flights to the moon and mars. Many of these missions require advance manufacturing and planned off planet resource utilization. As NASA continues to develop highly advance materials and manufacturing techniques to meet these mission profiles, inspection of these increasingly complex parts has had to evolve as well. Additive manufacturing is coming to the forefront as a primary manufacturing technique but offers unique challenges when inspection and certification are required. NASA has been working diligently to be a leader in developing and utilizing inspection techniques capable of inspecting these highly advanced parts. Additionally additive manufacturing techniques can also be used to build parts in space and provides a vehicle for in-situ resource utilization for off world missions. As NASA and its commercial crew partners move forward inspection techniques will need to continue to advance to ensure safe manned space flight. In this talk NASA will highlight many of the advanced nondestructive evaluation efforts going on across the agency. As well as highlights for points of infusion for helping NASA meet it’s future missions.

NDE↗