DOE OSTI2022

Design, Construction, and Testing of 0.5-m, 18-mm Period Nb 3 Sn Superconducting Undulator Magnets

We report design and fabrication of a new Nb 3 Sn-based superconducting undulator (SCU) are underway at the Advanced Photon Source (APS) of Argonne National Laboratory in collaboration with Fermilab and Lawrence Berkeley National Laboratory. To develop a robust and reliable fabrication process, the magnet development consists of several steps. First, magnetic and mechanical simulations were performed to optimize the magnet design; then, the design matured further by fabricating and testing a series of very short prototypes, ~8 cm long with a period length of 18 mm. These short prototype studies were previously reported. Second, the design was scaled to an intermediate length of ~0.5 m. These two steps led to the final design of ~1.1–m-long magnets, which are currently being fabricated. The quench behavior of each 0.5-m-long undulator magnet, as well as undulator assemblies from these magnets, was studied. The first SCU magnet assembly did not meet the design specifications due to the breakdown of the insulation. With an improved design and fabrication process based on lessons learned, the second SCU assembly achieved the design undulator field of 1.2 T. The design was further optimized, and the third set of magnets was fabricated and successfully tested.

43 PARTICLE ACCELERATORS↗

DOE OSTI2021

Vertical Septum Magnet Design for the APS Upgrade

The vertical injection scheme proposed for the APS Upgrade (APS-U) Project requires a challenging septum magnet that must meet stringent beam physics, magnetic field leakage, and vacuum requirements. The current iteration of this magnet design includes an enlarged stored-beam chamber aperture of 9 mm x 12 mm and a reduction of the septum thickness to 1.5 mm. The enlarged aperture accommodates a non-evaporable getter (NEG)-coated stored beam chamber to better achieve the required vacuum. A prototype septum magnet has been built and measurements confirm the cancellation of a peak leakage field even though the value is six times larger than the design. The leakage field measured at the upstream (US) end cancels the downstream (DS) end as was expected by design. The measured and simulated leakage field and the stored beam trajectories are reported.

43 PARTICLE ACCELERATORS↗

DOE OSTI2021

Helical superconducting undulator for 3rd and 4th generation of synchrotron light source and FELs

A helical superconducting undulator includes a cylindrical magnetic core through which a bore hole allows the passage of charged particles. A single superconducting wire wraps the magnetic core guided by helical flights and cylindrical protrusions, to create interleaved helical windings on the magnetic core. An electrical current may be supplied to the superconducting wire to generate a periodic helical magnetic field in the bore. The helical superconducting undulator also includes a strong-back enclosure that acts as an epoxy mold during epoxy impregnation, a structural support to ensure straightness of the undulator after epoxy impregnation, and assists in cooling and thermal control of the magnetic core and superconducting wire during device operation.

Gluskin, Efim↗

DOE OSTI2021

Fabrication and Testing of 18-mm-Period, 0.5-m-Long Nb 3 Sn Superconducting Undulator

The Advanced Photon Source at Argonne National Laboratory, in collaboration with FNAL and LBNL, is developing a Nb 3 Sn superconducting undulator with the goal of installing this device on the APS storage ring and providing APS users with the novel radiation source. A series of short, similar to ~ 8-cm-long, 18-mm-period undulator prototype magnets have been designed, fabricated, and tested. The same design was scaled to fabricate a 0.5-m-long undulator prototype. Tests of this prototype showed that the designed peak magnetic field of 1.2 T at 850 A was successfully achieved. It represents at least a 20% improvement in comparison with a NbTi SCU having the same period and magnetic gap. Test results and lessons learned from the design process are reported here.

43 PARTICLE ACCELERATORS↗

DOE OSTI2020

Heat Treatment Studies of Nb3Sn Wires for Superconducting Planar Undulators

A project aiming to fabricate a full-length 2.8-m long Nb 3Sn superconducting undulator for the storage ring was started last year at the ANL APS. These Nb 3 Sn undulators operate at a maximum magnetic field on the conductor of about 5 T. To address instabilities at this field, two Nb 3 Sn wires with small subelement size were used. Specifically, Restacked Rod Processed wires of 0.6mmin diameter and with 144 and 150 superconducting subelements respectively, over 169 total. The equivalent subelement diameter, DS, of thesewires is35 mu m. At these smallDS values, the critical current density is known to deteriorate, and the Residual Resistivity Ratio is very sensitive to heat treatment. A delicate balance has therefore to be found to obtain parameters within operation specifications. In this paper we showperformance results from different heat treatments.

critical current density↗