Two-dimensional perovskite templates for durable, efficient formamidinium perovskite solar cells

We present a design strategy for fabricating ultrastable phase-pure films of formamidinium lead iodide (FAPbI 3 ) by lattice templating using specific two-dimensional (2D) perovskites with FA as the cage cation. When a pure FAPbI 3 precursor solution is brought in contact with the 2D perovskite, the black phase forms preferentially at 100°C, much lower than the standard FAPbI 3 annealing temperature of 150°C. X-ray diffraction and optical spectroscopy suggest that the resulting FAPbI 3 film compresses slightly to acquire the (011) interplanar distances of the 2D perovskite seed. The 2D-templated bulk FAPbI 3 films exhibited an efficiency of 24.1% in a p-i-n architecture with 0.5–square centimeter active area and an exceptional durability, retaining 97% of their initial efficiency after 1000 hours under 85°C and maximum power point tracking.

14 SOLAR ENERGY↗
DOE OSTI2024

Structural Evolution and Photoluminescence Quenching across the FASnI 3– x Br x ( x = 0–3) Perovskites

One of the primary methods for band gap tuning in metal halide perovskites has been halide (I/Br) mixing. Despite widespread usage of this type of chemical substitution in perovskite photovoltaics, there is still little understanding of the structural impacts of halide alloying, with the assumption being the formation of ideal solid solutions. The FASnI 3–x Br x (x = 0–3) family of compounds provides the first example where the assumption breaks down, as the composition space is broken into two unique regimes (x = 0–2.9; x = 2.9–3) based on their average structure with the former having a 3D and the latter having an extended 3D (pseudo 0D) structure. Pair distribution function (PDF) analyses further suggest a dynamic 5s 2 lone pair expression resulting in increasing levels of off-centering of the central Sn as the Br concentration is increased. These antiferroelectric distortions indicate that even the x = 0–2.9 phase space behaves as a nonideal solid-solution on a more local scale. Solid-state NMR confirms the difference in local structure yielding greater insight into the chemical nature and local distributions of the FA + cation. In contrast to the FAPbI 3–x Br x series, a drastic photoluminescence (PL) quenching is observed with x ≥ 1.9 compounds having no observable PL. In conclusion, our detailed studies attribute this quenching to structural transitions induced by the distortions of the [SnBr 6 ] octahedra in response to stereochemically expressed lone pairs of electrons. This is confirmed through density functional theory, having a direct impact on the electronic structure.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2023

Ultrafast relaxation of lattice distortion in two-dimensional perovskites

Direct visualization of ultrafast coupling between charge carriers and lattice degrees of freedom in photoexcited semiconductors has remained a long-standing challenge and is critical for understanding the light-induced physical behaviour of materials under extreme non-equilibrium conditions. Here we obtain a direct visualization of the structural dynamics in monocrystalline 2D perovskites. We achieve this by monitoring the evolution of wavevector-resolved ultrafast electron diffraction intensity following above-bandgap high-density photoexcitation. Our analysis reveals a light-induced ultrafast reduction in antiferro-distortion resulting from a strong interaction between the electron–hole plasma and perovskite lattice, which induces an in-plane octahedra rotation towards a more symmetric phase. Correlated ultrafast spectroscopy performed at the same carrier density as ultrafast electron diffraction reveals that the creation of a dense electron–hole plasma triggers the relaxation of lattice distortion at shorter timescales by modulating the crystal cohesive energy. Then we show that the interaction between carrier gas and lattice can be altered by tailoring the rigidity of the 2D perovskite by choosing an appropriate organic spacer layer.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Nonequilibrium Lattice Dynamics in Photoexcited 2D Perovskites

Abstract Interplay between structural and photophysical properties of metal halide perovskites is critical to their utility in optoelectronics, but there is limited understanding of lattice response upon photoexcitation. Here, 2D perovskites butylammonium lead iodide, (BA) 2 PbI 4 , and phenethylammonium lead iodide, (PEA) 2 PbI 4 , are investigated using ultrafast transient X‐ray diffraction as a function of optical excitation fluence to discern structural dynamics. Both powder X‐ray diffraction and time‐resolved photoluminescence linewidths narrow over 1 ns following optical excitation for the fluence range studied, concurrent with slight redshifting of the optical bandgaps. These observations are attributed to transient relaxation and ordering of distorted lead iodide octahedra stimulated mainly by electron–hole pair creation. The c axis expands up to 0.37% over hundreds of picoseconds; reflections sampling the a and b axes undergo one tenth of this expansion with the same timescale. Post‐photoexcitation appearance of the (110) reflection in (BA) 2 PbI 4 would suggest a transient phase transition, however, through new single‐crystal XRD, reflections are found that violate glide plane conditions in the reported Pbca structure. The static structure space group is reassigned as P 2 1 2 1 2 1 . With this, a nonequilibrium phase transition is ruled out. These findings offer increased understanding of remarkable lattice response in 2D perovskites upon excitation.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Deterministic fabrication of 3D/2D perovskite bilayer stacks for durable and efficient solar cells

Realizing solution-processed heterostructures is a long-enduring challenge in halide perovskites because of solvent incompatibilities that disrupt the underlying layer. By leveraging the solvent dielectric constant and Gutmann donor number, we could grow phase-pure two-dimensional (2D) halide perovskite stacks of the desired composition, thickness, and bandgap onto 3D perovskites without dissolving the underlying substrate. Characterization reveals a 3D–2D transition region of 20 nanometers mainly determined by the roughness of the bottom 3D layer. Thickness dependence of the 2D perovskite layer reveals the anticipated trends for n-i-p and p-i-n architectures, which is consistent with band alignment and carrier transport limits for 2D perovskites. Here we measured a photovoltaic efficiency of 24.5%, with exceptional stability of T 99 (time required to preserve 99% of initial photovoltaic efficiency) of >2000 hours, implying that the 3D/2D bilayer inherits the intrinsic durability of 2D perovskite without compromising efficiency.

14 SOLAR ENERGY↗
DOE OSTI2022

Tolerance Factor for Stabilizing 3D Hybrid Halide Perovskitoids Using Linear Diammonium Cations

Three-dimensional (3D) halide perovskites have attracted enormous research interest, but the choice of the A-site cations is limited by the Goldschmidt tolerance factor. In order to accommodate cations that lie outside the acceptable range of the tolerance factor, low-dimensional structures usually form. To maintain the favorable 3D connection, the links among the metal-halide octahedra need to be rearranged to fit the large cations. This can result in a departure from the proper corner-sharing perovskite architectures and lead to distinctly different perovskitoid motifs with edge- and face-sharing. In this work, we report four new 3D bromide perovskitoids incorporating linear organic diammonium cations, A'Pb 2 Br 6 (A' is a +2 cation). We propose a rule that can guide the further expansion of this class of compounds, analogous to the notion of Goldschmidt tolerance factor widely adopted for 3D AMX 3 perovskites. The fundamental building blocks in A'Pb 2 Br 6 consist of two edge-shared octahedra, which are then connected by corner-sharing to form a 3D network. Different compounds adopt different structural motifs, which can be transformed from one to another by symmetry operations. Electronic structure calculations suggest that they are direct bandgap semiconductors, with relatively large band dispersions created by octahedra connected by corner-sharing. They exhibit similar electronic band structures and dynamic lattice characteristics to the regular 3D AMX 3 perovskites. Structures with smaller Pb–Br–Pb angles and larger octahedra distortion exhibit broad photoluminescence at room temperature. Furthermore, the emerging structure–property relationships in these 3D perovskitoids set the foundation for designing and investigating these compounds for a variety of optoelectronic applications.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Expanding the Cage of 2D Bromide Perovskites by Large A-Site Cations

Two-dimensional (2D) halide perovskites have outstanding optoelectronic properties, and they feature a variety of organic cation spacers and cage A-site cations that can be incorporated into their structures. It has recently been reported that the Goldschmidt tolerance factor can be relaxed and expanded in iodide 2D perovskites. Bromide 2D perovskites, whose multilayer structures and optical properties are much less studied, provide a great platform for studying structure-property relationships for 2D perovskites with large Asite cations. Herein, we report the synthesis and structure of three new 2D bromide perovskites-(BA)(2)(MHy)(2)Pb3Br10 (BA, butylammonium; MHy, methylhydrazinium), (BA)(2)(EA)(2)Pb3Br10 (EA is ethylammonium), and (BA)(2)(DMA)Pb2Br7 (DMA is dimethylammonium). We compared them with other 2D perovskites with different A-site cations but with the same spacer and layer thickness. Single-crystal structures show that the Pb-Br bonds are elongated to accommodate the large A-site cations. Additionally, the octahedra in (BA)(2)(MHy)(2)Pb3Br10 and (BA)(2)(EA)(2)Pb3Br10 are highly distorted, and their different stacking patterns of the inner and outer layers lead to the formation of the n = 3 phases. Density functional theory calculations show that 2D perovskites with larger A-site cations (e.g., DMA, MHy, and EA) have smaller band dispersions and larger effective masses than those with Cs+ and MA. (BA)(2)(MHy)(2)Pb3Br10 also exhibits one of the largest Rashba splittings in the literature. Structures with large cage cations also exhibit high band gaps within the same n number and short photoluminescence (PL) lifetimes. Temperature- and power-dependent PL measurements reveal that the broad shoulder in the PL peak originates from the trap states.

Emission↗
DOE OSTI2021

Interstitial Nature of Mn 2+ Doping in 2D Perovskites

Halide perovskites doped with magnetic impurities (such as the transition metals Mn 2+ , Co 2+ , Ni 2+ ) are being explored for a wide range of applications beyond photovoltaics, such as spintronic devices, stable light-emitting diodes, single-photon emitters, and magneto-optical devices. However, despite several recent studies, there is no consensus on whether the doped magnetic ions will predominantly replace the octahedral B-site metal via substitution or reside at interstitial defect sites. Here, by performing correlated nanoscale X-ray microscopy, spatially and temporally resolved photoluminescence measurements, and magnetic force microscopy on the inorganic 2D perovskite Cs 2 PbI 2 Cl 2 , we show that doping Mn 2+ into the structure results in a lattice expansion. The observed lattice expansion contrasts with the predicted contraction expected to arise from the B-site metal substitution, thus implying that Mn 2+ does not replace the Pb 2+ sites. Photoluminescence and electron paramagnetic resonance measurements confirm the presence of Mn 2+ in the lattice, while correlated nano-XRD and X-ray fluorescence track the local strain and chemical composition. Density functional theory calculations predict that Mn 2+ atoms reside at the interstitial sites between two octahedra in the triangle formed by one Cl – and two I – atoms, which results in a locally expanded structure. These measurements show the fate of the transition metal dopants, the local structure, and optical emission when they are doped at dilute concentrations into a wide band gap semiconductor.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2021

Light-activated interlayer contraction in two-dimensional perovskites for high-efficiency solar cells

Understanding and tailoring the physical behaviour of halide perovskites under practical environments is critical for designing efficient and durable optoelectronic devices. Here, we report that continuous light illumination leads to >1% contraction in the out-of-plane direction in two-dimensional hybrid perovskites, which is reversible and strongly dependent on the specific superlattice packing. X-ray photoelectron spectroscopy measurements show that constant light illumination results in the accumulation of positive charges in the terminal iodine atoms, thereby enhancing the bonding character of inter-slab I–I interactions across the organic barrier and activating out-of-plane contraction. Correlated charge transport, structural and photovoltaic measurements confirm that the onset of the light-induced contraction is synchronized to a threefold increase in carrier mobility and conductivity, which is consistent with an increase in the electronic band dispersion predicted by first-principles calculations. Flux-dependent space-charge-limited current measurement reveals that light-induced interlayer contraction activates interlayer charge transport. Lastly, the enhanced charge transport boosts the photovoltaic efficiency of two-dimensional perovskite solar cells up to 18.3% by increasing the device’s fill factor and open-circuit voltage.

36 MATERIALS SCIENCE↗