Evaluation of Low-Energy Hydrogen Separation Method Using Metal-Organic Frameworks (MOFs) for Closed-Loop ECLSS Air Revitalization (CLEAR)

The State-of-the-Art (SOA) air revitalization architecture onboard the International Space Station (ISS) recovered approximately 50% of the oxygen (O 2 ) from metabolic carbon dioxide (CO 2 ) via the Sabatier process from 2011 to 2017. O 2 recovery is currently constrained by the limited availability of reactant hydrogen (H 2 ) preventing complete conversion of CO 2 to H 2 O. Increasing O 2 recovery within Closed-Loop ECLSS is essential to reducing resupply mass for long-duration manned missions; specifically focusing on water (H 2 O) which supplies H 2 for Sabatier via water electrolysis. Past ground test endeavors at Marshall Space Flight Center (MSFC) have attempted to recover H 2 from Sabatier-produced CH 4 using technologies such as carbon vapor deposition (CVD) and plasma pyrolysis. The byproducts of these technologies can act as a catalyst poison or reactor deadload to the Sabatier reactor. Hydrogen separation techniques must be utilized to maintain the Sabatier catalyst during gas recycling and must be scalable, non-energy intensive, and safe to operate in a habitation setting. Research indicated that metal-organic frameworks (MOFs) could meet these criteria and were tested for their capability to capture the various carbon-based gaseous products of CVD and plasma pyrolysis such as acetylene (C 2 H 2 ), ethylene (C 2 H 4 ), ethane (C 2 H 6 ), and carbon monoxide (CO) which would purify the hydrogen gas stream passing through the MOF. A sub-scale adsorption column was developed by Marshall Space Flight Center to test three MOF candidates against a synthetic gas mixture comprised of process-relevant carbonous gases and hydrogen to evaluate the separation capability of the MOFs. The results of the hydrogen separation capability, isothermal desorption capability, and demonstrated cyclic reuse of the MOF are presented in this paper.

Kagen Crawford↗

NASA NTRSDate not supplied

Bosch Carbon Catalyst Regeneration in Water I: Bosch Carbon Removal from Reacted Beads Utilizing Mechanical Agitation

The ability to recover oxygen from metabolic carbon dioxide is crucial for crewed long duration missions in which the atmosphere must be recycled. Two physiochemical methods are primarily employed for this purpose: the Bosch process and the Sabatier reaction. This paper focuses on the Bosch process. It utilizes hydrogen in the presence of a catalyst to form water and solid carbon out of metabolic carbon dioxide. The solid carbon product deposits onto the catalyst and eventually causes reactor over pressurization issues. Multiple methods are currently being investigated to regenerate the catalyst’s surface and break up the pressure causing carbon clogs. This paper explores whether water and mechanical abrasion would work to remove Bosch carbon by testing multiple washing conditions. The different washing conditions involved agitation intensity, heating, duration, and volume of water. It was found that it is possible to break up the clumps of carbon formed in the reactor through agitation with room temperature water in one hour and shows promise for completely cleaning the carbon off the beads’ surface.

Agitation↗

NASA NTRSDate not supplied

Bosch Carbon Catalyst Regeneration in Water II: Analysis of Bosch Catalyst Beads Throughout the Initial Regeneration Process

Catalyst integrity is an important factor in reactor longevity since it changes the effectiveness of a reaction. A Carbon Formation Reactor (CFR), used within Series Bosch (S-Bosch), utilizes an iron alloy catalyst to convert carbon monoxide and hydrogen into water and solid carbon. The catalyst promotes the formation of carbon to such an extent that pressure-causing clogs form within the reactor and reaction sites on the catalyst become limited. To remove carbon from both the reactor and the surface of the iron alloy catalyst, a technique was developed that utilizes water, an In-Situ Resource Utilization (ISRU) Resource, and agitation to regenerate the reactor. To ascertain catalyst integrity throughout this regenerative process, sample catalyst beads were taken before and after the carbon formation reaction, and then after the regeneration process. Additionally, wastewater from the regeneration process was sampled. The sampled beads and wastewater were observed under a Scanning Electron Microscopy (SEM) microscope and the beads were chemically etched to determine if the catalyst had degraded at any point during this process, and if catalyst was lost. Minimal catalyst degradation was observed after carbon formation in the CFR.

regeneration↗

NASA NTRSDate not supplied

Bosch Carbon Catalyst Regeneration in Water III: Experiments for and Related to Thermal Shock

Bosch technology has the potential to close the atmospheric revitalization loop by providing theoretically 100% regeneration of metabolic carbon dioxide into oxygen. The main obstacle to using Bosch technology is over-pressurization issues in the carbon formation reactor. Prior work on Bosch catalyst regeneration established that agitating carbon coated beads in water broke up pressure causing clogs and regenerated the catalyst surface. This process proved to be time consuming with experiments taking at least one hour to regenerate ten grams of carbon coated beads. In an attempt to shorten the processing time, thermally shocking the carbon coated beads prior to mechanical agitation was tested. Agitating the carbon coated beads after exposure to a saturated steam environment was also tested to ensure that the steam generated by thermally shocking the carbon coated beads would not cause adverse effects. The rationale behind thermally shocking the carbon coated beads is that the bead would pull away from the carbon shell due to a difference in the thermal expansion coefficients. The results of this project show that the processing time can be cut in half when compared to previous work, and that saturated steam has little to no effect on regeneration.

Bosch Process↗

NASA NTRSDate not supplied

Bosch Carbon Catalyst Regeneration in Water II: Analysis of Bosch Catalyst Beads Throughout the Initial Regeneration Process

Catalyst integrity is an important factor in reactor longevity since it changes the effectiveness of a reaction. A Carbon Formation Reactor (CFR), used within Series Bosch (S-Bosch), utilizes an iron alloy catalyst to convert carbon monoxide and hydrogen into water and solid carbon. The catalyst promotes the formation of carbon to such an extent that pressure-causing clogs form within the reactor and reaction sites on the catalyst become limited. To remove carbon from both the reactor and the surface of the iron alloy catalyst, a technique was developed that utilizes water, an In-Situ Resource Utilization (ISRU) Resource, and agitation to regenerate the reactor. To ascertain catalyst integrity throughout this regenerative process, sample catalyst beads were taken before and after the carbon formation reaction, and then after the regeneration process. Additionally, wastewater from the regeneration process was sampled. The sampled beads and wastewater were observed under a Scanning Electron Microscopy (SEM) microscope and the beads were chemically etched to determine if the catalyst had degraded at any point during this process, and if catalyst was lost. Minimal catalyst degradation was observed after carbon formation in the CFR.

Series Bosch↗