DOE OSTI2020

Post-Irradiation Evaluation of Eurofer97 Fracture Toughness Using Miniature Multinotch Bend Bar Specimens

In this study, we performed fracture toughness characterization of ten neutron-irradiated Eurofer97 variants using precracked miniature multi-notch bend bar (M4CVN) specimens based on the Master Curve method in the ASTM E1921 standard. The neutron irradiation was performed in the flux trap position of the High Flux Isotope Reactor (HFIR) of the Oak Ridge National Laboratory (ORNL) with the nominal irradiation temperature of 300°C and irradiation dose of 2.5 displacements per atom (dpa). Depending on the irradiation temperature and materials, we observed different degrees of irradiation hardening and embrittlement for ten Eurofer97 variants. The upper shift in the Master Curve reference temperature T0Q vs. the increase in Vickers microhardness values showed a liner relationship for only a few materials indicating different irradiation responses of the Eurofer97 variants.

Chen, Xiang↗

DOE OSTI2020

Determination of neutron irradiation temperatures of SiC using electrical resistivity method

The irradiation temperature of silicon carbide (SiC) was determined post-irradiation by examination of the recovery of the electrical resistivity due to thermal annealing in a rapid heating/cooling optical furnace. High-purity, high-resistivity grade SiC is routinely used as a passive temperature monitor in neutron irradiation studies at the High Flux Isotope Reactor (HFIR), and this paper presents an alternative automated technique for determination of the irradiation temperature the SiC experienced. Neutron collisions with the atoms results in displaced lattice atoms (interstitials) that act as electron donors yielding a significant decrease in electrical resistivity. The irradiation defects become thermodynamically unstable and start to recombine, when annealed above the irradiation temperature, resulting in a recovery of the electrical resistivity. The resistivity is measured at a fixed elevated temperature above ambient, which is below the target irradiation temperature. When the resistivity is plotted as a function of annealing temperatures, a clear increase is observed due to the recovery of irradiation defects. We have demonstrated that this electrical resistivity measurement of SiC is effective to determine irradiation temperature of SiC. In conclusion, energy levels of various defects in SiC were calculated from Arrhenius plots of electrical conductivity versus inverse temperature.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Plasma-arc lamp high heat flux cycling exposure of neutron irradiated tungsten materials

Thick plate, unalloyed W was neutron irradiated in the High Flux Isotope Reactor (HFIR) at 550 °C to a fast fluence of 1.24 × 10 25 n m -2 E > 0.1 MeV (~0.24 dpa). Unirradiated and irradiated specimens of the material were high heat flux (HHF) tested in the Plasma Arc Lamp (PAL) facility. The PAL uses a high-power photon source to provide a broad and even heat distribution on the sample surface. To simulate on/off cycling of normal operating plasma, the samples were exposed to approximately 800 cycles at 4.73 MW m -2 absorbed heat flux (incident heat fluxes of 10.95 MW m -2 ). Additionally, after PAL exposure, slight changes were observed on the surfaces of the samples with SEM. The samples showed some annealing in the near surface polished region, but they were all below the damage threshold for cracking or other destructive features. The PAL has a large parameter space for future testing. The use of the HFIR and PAL to sequentially expose neutron irradiated samples to HHF will be a powerful tool for understanding materials behavior in a fusion-like environment.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Design and strategy for next-generation silicon carbide composites for nuclear energy

Silicon carbide (SiC) ceramic-based composites continue to be attractive material options for fusion in-vessel components and fission reactor core structures because of their exceptional high-temperature capability and favorable neutronic properties. As performance data accumulates, the limitations of the current generation of nuclear-grade SiC composites are becoming more apparent. These limitations mainly involve strength degradation during high-dose neutron irradiation. In this paper, we discuss several options for improving the performance of the next generation of SiC composites to enhance the radiation resistance, along with new experimental results on neutron irradiation resistance. The main emphasis is on the selection of the fibers and the design and development of alternative interphase layers for advanced composites.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2020

Perspectives on the FESAC transformative enabling capabilities: Priorities, plans, and Status

In early 2017, the Fusion Energy Sciences Advisory Committee (FESAC), an advisory committee to the United States Department of Energy, was charged with identifying transformative enabling capabilities (TECs) “that could promote efficient advance toward fusion energy, building on burning plasma science and technology.” A subcommittee with broad expertise was formed and sought feedback from scientific experts, including experts from outside the fusion community. Three workshops were conducted, and a report was approved by FESAC in 2018 that identified four of the “most promising” TECs: advanced algorithms, high-critical-temperature superconductors, advanced materials and manufacturing, and novel technologies for tritium fuel cycle control. In addition, one “promising” TEC was identified: fast flowing liquid metal plasma-facing components. This paper will give details on the promising TECs and an overview on considerations of these TECs in the United States since the publication of the report.

Lumsdaine, Arnold↗

DOE OSTI2020

Impact of control blade insertion on the deformation behavior of SiC-SiC channel boxes in BWRs

This article describes the analysis of distortion of a silicon carbide fiber-reinforced, silicon carbide matrix (SiC-SiC) composite channel box under in-reactor conditions of a boiling water reactor (BWR). The BWR core has significant gradients in the fast neutron flux across the channel box due to the presence of water rods within the fuel assemblies, and these gradients increase further with the insertion of control blades. As a result of the temperature and neutron flux dependent irradiation-induced swelling of SiC, the SiC-SiC composite channel box can undergo distortion. In this work, we evaluate the SiC-SiC channel box distortion for three different control blade positions. This analysis is based on the neutron flux and temperature distributions in the BWR core calculated using the neutronics code MPACT and thermal-hydraulics code CTF. This calculation is coupled through temperature feedback. Subsequently, we have performed structural analysis based on the calculated neutron flux and temperature distributions to determine the deformation and stress development in the channel box. The structural analysis was performed using the fuel performance modeling code BISON and the commercial finite element analysis software Abaqus. The results indicate that large gradients in fast neutron flux (up to 35–40% across a single axial level) will develop across the channel box. Due to these gradients, the channel box will undergo time-dependent bending for all the control blade positions in the assembly. The time-dependent bowing behavior is dominated by the transient swelling of SiC-SiC material under non-uniform neutron flux, and changes with variation in the control blade position. The bending will cause temporary interference between the channel box and control blade, and the interference is expected to be most severe for the fully inserted control blade position. The developed stresses due to differential swelling in the channel box exceed the proportional limit stress of the material, which may cause matrix microcracking in the channel box. However, the stresses remain below the tensile strength of the material, and therefore, development of a full, through-thickness crack in the channel box is not expected. Finally, further work is recommended to explore and evaluate the mitigation strategies.

42 ENGINEERING↗

DOE OSTI2020

Protection of graphite from salt and gas permeation in molten salt reactors

The reactor core, moderator and reflectors of a thermal spectrum advanced molten salt reactor will constitute multi-tons of graphite. Porous reactor-grade graphite, if unprotected, can be permeated by molten salt depending on the infiltrating pressure differential and entrance diameters of accessible graphite pores. Salt and gas permeation of graphite can affect microstructural properties and radiation behavior but also facilitate diffusion, deposition and retention of fission products and tritium. Because of the significant void volume of nuclear graphite, fission products and tritium retention due to salt permeation necessitates seal coatings or pore impregnation to reduce open porosity. Alternatively, very fine-grained graphite grades with low Xe permeability are being developed. In this work, we survey the current technologies for mitigating salt and gas transport into graphite.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Fusion Materials Research at Oak Ridge National Laboratory in FY2019

This is the eighth Annual report of the Oak Ridge National Laboratory (ORNL) program aimed at developing and qualifying materials that can meet the application requirements of fusion power systems, especially the near-plasma regions of those systems. Earlier issues of these annual reports can be found at the Fusion Materials Program website; more detailed reporting for those and many earlier years are contained in the series of Semiannual Progress reports at the same website, and the detailed results of the program are contained in the published scientific literature.

36 MATERIALS SCIENCE↗