Katoh, Yutai

Publications and source records attributed to Katoh, Yutai.

At least 19 records
All sourcesNASA NTRSDOE OSTI
DOE OSTI2024

Microstructure, electrical resistivity, and tensile properties of neutron-irradiated Cu–Cr–Nb–Zr

High strength, high conductivity copper alloys that can resist creep at high temperatures are one of the primary candidates for efficient heat exchangers in fusion reactors. Cu–Cr–Nb–Zr (CCNZ) alloys, which were designed to improve the strength and creep life of ITER Cu–Cr–Zr (CCZ) reference alloys, have been found to have comparable electrical conductivity and tensile properties to CCZ alloys. The measured creep rupture times for these improved alloys is about ten times higher than the ITER reference alloys at 90–125 MPa at 500 °C. However, the effects of neutron irradiation on these alloys, and the ensuing material properties, have not been studied; thus, their utility in a fusion reactor environment is not well understood. This study characterizes the room temperature mechanical and electrical properties of a neutron-irradiated CCNZ alloy and compares them to a neutron-irradiated ITER reference heat sink CCZ alloy. Tensile specimens were neutron irradiated in the High Flux Isotope Reactor (HFIR) to 5 dpa between 250 °C and 325 °C. Post-irradiation characterization included electrical resistivity measurements, hardness, and tensile tests. Microstructural evaluation used scanning electron microscopy, energy dispersive x-ray spectroscopy, and atom probe tomography to characterize the irradiation-produced changes in the microstructure and investigate the mechanistic processes leading to post-irradiation properties. Transmutation calculations were validated with composition measurements from atom probe data and used to calculate contributions to the increased electrical resistivity measured after irradiation. Comparisons with CCZ alloys in the same irradiation heat found that the post-irradiated CCNZ and CCZ alloys had comparable electrical resistivity. Although CCNZ alloys suffered more irradiation hardening than CCZ, the overall tensile behavior deviated very little from non-irradiated values in the temperature range studied.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Determining reference standard strength for neutron-irradiated reduced activation ferritic/martensitic steel F82H by Bayesian method

The deterministic approach widely adopted in the design of structural components relies on systematically defined design limits using empirically determined safety factors. However, this approach is not always appropriate because structures are subjected to a variety of loads in the practical environment, which may result in excessively conservative design limits. In recent years, a more rigorous probabilistic approach that incorporates material strength distributions has become an important solution. In the probabilistic approach, the probability density functions of material strength properties underpin the design criteria. Here, the objective of this study is to identify the density distribution functions that best describe tensile properties of irradiated F82H to define a reference strength for DEMO design. Due to the limited number of existing data, this study specifically employs a Bayesian prediction method based on Monte Carlo simulations to determine a material reference value with statistical reliability and to investigate its effectiveness. For example, the dependence of tensile properties of 300 °C irradiated materials on irradiation damage and the range predicted by 95% Bayesian estimation was evaluated. As a statistical model for the dose dependence of statistical parameters, the normal distribution exhibited a better fit for 0.2% proof strength and tensile strength, whereas the distribution of total elongation data gave comparable reference values for both the normal and Weibull distribution models. Both models gave comparable criteria for the distribution of total elongation data. The Weibull model also gave better results for uniform elongation. The function best describing the model was a logarithmic law for both 0.2% proof strength and tensile strength, while a power law for both total and uniform elongation, which allowed for more comprehensive data prediction of irradiation data with statistical accuracy for DEMO reactor design.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Comprehensive characterization of the irradiation effects of glassy carbon

Carbon materials have become increasingly diverse, finding applications in high-temperature and high-radiation environments. Glassy carbon, an allotrope known for its exceptional chemical inertness and desirable mechanical properties. However, understanding neutron irradiation effects in glassy carbon has proven challenging, primarily because of its unique nanopore structure. Here, this study presents a highly detailed microstructural characterization investigation of neutron-induced changes in glassy carbon, revealing how changes in nanopore structure and crystallinity impact the irradiation-induced shrinkage. Aberration-corrected scanning transmission electron microscopy (STEM) reveals pore closure that leads to material densification in the irradiated samples. Dimensional analysis combined with comparison to historical data suggest significant length shrinkage to occur. Neutron and in situ electron irradiation experiments suggest that glassy carbon transforms into so-called carbon onions, supporting the concept of shrinkage saturation. Investigating irradiation temperature effects using STEM, electron energy loss spectroscopy, x-ray diffraction, and Raman spectroscopy revealed partial amorphization at 210 °C–230 °C and preserved order in glassy carbon at 860 °C, coinciding with pore closure. Thermal property measurements were also conducted to assess the effects of densification and other changes in the atomic structure of glassy carbon. The results of this study have broad implications in the deployment of glassy carbon to nuclear environments, based around the observed changes in the thermal properties, and demonstrates the operational window for the onset of densification.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Response of 11 B enriched ZrB 2 ultra-high temperature ceramic to neutron irradiation at elevated temperatures

ZrB 2 , an ultra-high temperature ceramic (UHTC) is being considered for use in fusion reactor first-wall structures, yet its response to irradiation remains poorly understood. This study employed scanning/transmission electron microscopy (S/TEM), synchrotron X-ray diffraction (XRD), finite element calculations, and thermal property measurements to thoroughly investigate the neutron-irradiation effects on 11 B-enriched ZrB 2 . Neutron irradiations were conducted at 220 °C and 620 °C, with a neutron fluence of 2.2 × 10 25 neutron/m 2 (energy > 0.1 MeV), resulting in 3.9 dpa and 4200 appm He. The study revealed the unusual prevalence of prism loops and a > c anisotropic lattice swelling, likely linked to the low c/a ratio of ZrB 2 , leading to grain boundary microcracking. Reducing the grain sizes was effective in reducing intergranular cracking and macroscopic swelling. The observation of cavities in ZrB 2 irradiated at 620 °C, as opposed to 220 °C, prompts questions about the temperature at which vacancies in ZrB 2 become mobile, and the role of neutron absorption by 10 B in elevating irradiation temperatures. Isotopic enrichment in 11 B proves to be a viable strategy for mitigating helium production in transition-metal diborides, which is a critical consideration for nuclear applications. Irradiation-induced defects reduce the thermal diffusivity and conductivity of ZrB 2 by a factor of 4–9, which has important implications for its role as a plasma-facing material in fusion reactors that drive high heat fluxes through first-wall materials. Here, this comprehensive study lays the foundation for understanding ZrB 2 behavior under neutron irradiation and highlights important phenomena to consider for various material applications.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Emerging continuous SiC fibers for high-temperature applications

Silicon carbide (SiC) fibers are responsible for the ultimate strength and toughness of SiC-fiber reinforced composites in harsh environments. The development of a new generation of continuous SiC fibers continues to advance the mechanical properties of composite materials. Tyranno™ SA4 fiber was recently released as a successor of Tyranno™ SA3 fiber. Laser-driven chemical vapor deposition (LCVD) has been adopted as an alternative fiber processing route to synthesizing high-strength SiC fiber with tailorable small diameters and chemical compositions. Both Tyranno™ SA4 and laser-driven CVD fibers show very high tensile strength, about 4 GPa in the as-fabricated condition. The degradation of thermal stability and strength due to annealing in an inert environment were similar for Tyranno™ SA3 and SA4 fibers because of their similar carbon-rich, crystalline microstructure. Silicon-rich fibers produced by LCVD possessed heterogeneous crystallinity, which was attributed to laser power distribution and showed microstructural instability at 1500 °C and above. Finally, the new SiC fibers demonstrated an increase in as-fabricated strength but faced the same challenges in environmental resistance as the traditional SiC fibers do.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Mechanical degradation of duplex SiC-fiber reinforced SiC matrix composite tubes under a controlled high-temperature steam environment

This paper describes results from the mechanical evaluation of unirradiated SiC fiber–reinforced SiC matrix composite tubes under a controlled high-temperature steam environment. The experiments were aimed at identifying key material degradation behavior under environments relevant to loss-of-coolant accidents of light water reactors. Mechanical tests of the SiC composite tubes at 1000 °C under steam and inert environments were conducted using a unique test capability. Further, the material tested was a duplex tube with a thick monolithic SiC layer on the outer surface. The tubes were subjected to preloading at ~100 MPa in tension before exposure to high-temperature steam with up to 75% of the preload at a constant displacement. In the presence of matrix cracks, the steam exposure caused embrittlement of the SiC composite tubes and failure at a stress level below the pretest stress. The material degradation was explained by a fiber oxidation model, which can be applied to various SiC cladding concepts. The embrittlement could be a limiting factor for using SiC cladding subjected to loss-of-coolant accident conditions.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Phase separation during the direct powder bed fusion of SiC

Powder bed fusion (PBF) is an attractive additive manufacturing option for fabrication of SiC object with complex geometries. However, the density and microstructure controls remain a challenge. This study is aimed at understanding laser–SiC interactions, with emphasis on microstructure-processing relationships, to identify potential solutions for the process improvement. SiC tubes were fabricated by PBF of pure SiC powders without sintering additives. Further, comprehensive analysis by X-ray diffraction, Raman spectroscopy, and electron microscopy indicated that binding of SiC particles was achieved by incongruent melting of SiC to a Si/C mixture containing SiC micro- and nanocrystallites. The phase evolution under laser irradiation of SiC was explained by phase diagrams. This study uncovered the PBF SiC microstructure at different length scales and the relationship between the microstructure and the processing parameters.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Hermeticity of SiC/SiC composite and monolithic SiC tubes irradiated under radial high-heat flux

Demonstration of hermetic SiC fiber–reinforced SiC matrix composite cladding under normal operating environments has been identified as one of the most critical feasibility issues for accident-tolerant fuel cladding in light-water reactors. This study provides critical experimental data needed for understanding the effects of irradiation on hermeticity. SiC composite and monolithic tubes were neutron-irradiated to 2 displacements per atom with and without a nominal radial heat flux of 0.6 MW/m2 to produce a simulated in-pile stress state for the normal operation of a light-water reactor. The through-thickness temperature gradient under irradiation results in a gradient in swelling, which causes a significant stress buildup. Such irradiation-induced stress was modeled using a commercial finite element analysis code. The radial heat flux–irradiation synergism was experimentally investigated by constructing a special irradiation capsule and evaluating the helium hermeticity of the specimens. The simulated stress state exhibited a near equi-biaxial tensile axial and hoop stress of ~150 MPa at the inner surface of the SiC composite tube. This stress level is potentially beyond the matrix cracking stress. Degradation of hermeticity of the SiC composite tubes was observed after irradiation, indicating irradiation-induced cracking, whereas the irradiated monolithic SiC tubes remained hermetic. In conclusion, the results indicate that loss of hermeticity caused by radiation-induced microcracking is a potential issue for SiC composite cladding, depending on the magnitude of the temperature gradients. Coating the outer surface of the cladding was identified as a mitigation strategy that might overcome the cracking issue.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Evaluation of Tungsten—Steel Solid-State Bonding: Options and the Role of CALPHAD to Screen Diffusion Bonding Interlayers

Critical aspects of innovative design in engineering disciplines like infrastructure, transportation, and medical applications require the joining of dissimilar materials. This study investigates the literature on solid-state bonding techniques, with a particular focus on diffusion bonding, as an effective method for establishing engineering bonds. Welding and brazing, while widely used, may pose challenges when joining materials with large differences in melting temperature and can lead to mechanical property degradation. In contrast, diffusion bonding offers a lower temperature process that relies on solid-state interactions to develop bond strength. The joining of tungsten and steel, especially for fusion reactors, presents a unique challenge due to the significant disparity in melting temperatures and the propensity to form brittle intermetallics. Here, diffusion characteristics of tungsten–steel interfaces are examined and the influence of bonding parameters on mechanical properties are investigated. Additionally, CALPHAD modeling is employed to explore joining parameters, thermal stability, and diffusion kinetics. The insights from this research can be extended to join numerous dissimilar materials for specific applications such as aerospace, automobile industry, power plants, etc., enabling advanced and robust design with high efficiency.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Degradation of electrical resistivity of tungsten following shielded neutron irradiation

A major challenge for heat transfer in nuclear materials is to ensure thermal mobility after high amounts of neutron irradiation. Tungsten is widely selected as a heat transfer material in fusion reactors. In metals, thermal conductivity is dominated by electrons’ ability to transfer energy. Neutron irradiation generates point defects, clusters, and solid transmutation (e.g.rhenium and osmium in tungsten), which inhibit electron motion. The purpose of this work is to quantify the irradiation-induced change in electron mobility and deconvolute transmutation and microstructural effects on observed changes to electron mobility. Single and polycrystalline tungsten were fast neutron irradiated in the High Flux Isotope Reactor at Oak Ridge National Laboratory to doses between 0.2 and 0.7 displacements per atom (dpa) and temperatures from 500 °C to 1000 °C. Grain growth was observed in all samples. Microstructure and transmutation were quantified. The geometric orientation of samples with elongated grains has been shown to affect electrical resistivity. A mathematical model was developed and used to deconvolute solid-solution transmutation, grain, and temperature-dependent lattice effects on resistivity. At ~0.4 dpa at ~590 °C, the combined resistivity degradation due to voids, vacancies, interstitials, and dislocations is estimated to be greater than the contribution from solid solution Re transmutation, which is greater than the contribution from grain boundaries. At doses of ~0.7 dpa at ~750 °C, solid solution Re contributions are greater than all other effects combined. As a result, this work establishes a basis to predict the effects of irradiation temperature and transmutation on thermal properties of tungsten and highlights the importance of irradiation temperature.

36 MATERIALS SCIENCE↗
DOE OSTI2023

A novel design of transitional layer structure between reduced activation ferritic martensitic steels and tungsten for plasma facing materials

Plasma-facing components (PFCs) are among the most critical gaps for fusion energy to establish technical and economic feasibility. Tungsten as a first wall/blanket material in PFCs requires to be integrating with reduced activation ferritic martensitic (RAFM) steels as a structural component. Currently, major drawbacks are the requirement of brazing, the formation of a brittle interface, and a large difference between the coefficients of thermal expansion of tungsten and steel. Here, a novel transitional multilayer structure was designed and investigated to join tungsten and RAFM steels using three interlayers. The composition of each interlayer was selected based on computational thermodynamics and diffusion kinetics to ensure a body-centered cubic (bcc) single-phase structure and prevent the formation of a brittle intermetallic phase region in the temperature range of 600–1150 °C. Although the transitional layer structure was designed for additive manufacturing, spark plasma sintering (SPS) as proof of concept was used to bond the individual layers. Interfaces were investigated using scanning and transmission electron microscopy methods but no layered intermetallic phase was observed. Nanoindentation maps across the interface suggest major hardness differences at the interface between tungsten and the vanadium interlayer, as well as the interface between RAFM steel and the FeCrAl interlayer.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Influence of fatigue precracking and specimen size on Master Curve fracture toughness measurements of EUROFER97 and F82H steels

EUROFER97 and F82H steels are two leading reduced-activation ferritic-martensitic (RAFM) steels for fusion first wall and blanket applications. Exposure to the harsh environment of fusion reactors can result in severe degradation of fracture toughness. Thus, the post-irradiation evaluation of fracture toughness is critical for understanding the material behavior. Due to the space constraints of irradiation facilities and challenges in controlling a uniform irradiation condition for large size specimens, the development of small specimen test techniques (SSTT) is indispensable to evaluate the performance of irradiated materials. In this study, we evaluated specimen size effects on the Master Curve fracture toughness of EUROFER97 and F82H steels. A wide variety of specimens, including 0.5 T compact tension (C(T)) specimens, 0.16 T mini-compact tension (miniC(T)) specimens, and 1.65 mm miniature bend bar specimens, were tested. The testing methodology was based on the Master Curve method in the ASTM E1921 standard. No specimen size effect was observed in 0.5 T C(T) and 0.16 T miniC(T) specimens on the Master Curve reference temperature T0, while 1.65 mm miniature bend bar specimens yielded a higher T 0Q . A strong effect of fatigue precracking on T 0 for 0.5 T C(T) and 0.16 T miniC(T) specimens was observed, such that testing on specimens with skewed fatigue precrack fronts resulted in lower T 0 than for specimens with ASTM standard qualified straight fatigue precrack fronts. The results highlight the importance of experimental quality control in developing SSTT for Master Curve fracture toughness testing. Lastly, we also evaluated and provided recommendations on the minimum number of specimens needed for each specimen type for yielding reliable T 0Q values.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Codes and standards for ceramic composite core materials for High Temperature Reactor applications

Fiber-reinforced ceramic matrix composites are attractive for high-temperature nuclear applications due to excellent thermal and mechanical properties as well as reasonable-to-outstanding radiation resistance. Over the past 20 years, the use of ceramic matrix composite applications expanded to many commercial non-nuclear industries as fabrication and application of the technologies mature. The ASME Boiler Pressure Vessel Code, under Section III Division 5, provides the design and construction rules for High Temperature Reactor components. It published the first rules for ceramic matrix composites to be used for reactor core components. The rules lay out the quality requirements together with the design and materials criteria for the use and application of silicon carbide- and carbon-based matrix material technologies. As with the established graphite rules, the ceramic composite material rules are structured in Subsection HH (from Section III), that addresses the criteria for class SN nonmetallic core components. The code rules rely heavily on the development and publication of standards for composite specification, classification, and testing of mechanical, thermal, and other properties. These test methods are developed in ASTM Committee C28 on Advanced Ceramics, with a current focus on ceramic composite tubes. This article describes the detail of the composites code, the design methodology and similarities to the graphite code, the guidance for the development of specifications for ceramic composites (for nuclear applications) including recent standard developments, and it mentions the next steps to support licensing aspects by validating the code with benchmarking data.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗
DOE OSTI2023

Understanding the effect of specimen size on the properties of fine-grain isotropic nuclear graphite for irradiation studies: Physical, electrical, thermal properties

Programs at Oak Ridge National Laboratory are investigating the effects of neutron irradiation in the High Flux Isotope Reactor (HFIR) on properties of fine-grain nuclear graphites. Specimens were irradiated in the HFIR flux trap, which required using specimens that are smaller than the sizes recommended by ASTM standards. Here, this work has investigated whether subsized specimens can be used to reliably determine the measured physical (density, elastic moduli, and electrical resistivity) and thermal properties (coefficient of thermal conductivity and thermal conductivity). The results show the specimen sizes in this investigation had a minimal influence on any of the measured properties. Even for the properties where size influenced the measured value (density and thermal conductivity), an explanation is provided, and the consequences can be accounted for in post-irradiation results. This work demonstrated that using subsized specimens for physical and thermal property measurements is suitable when necessary for fine-grain isotropic graphite.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Understanding the effect of specimen size on the properties of fine-grain isotropic nuclear graphite for irradiation studies: Mechanical properties

Programs at Oak Ridge National Laboratory are investigating the effects of neutron irradiation in the High Flux Isotope Reactor (HFIR) on properties of fine-grain isotropic nuclear graphites. Specimens were irradiated in the HFIR flux trap, which requires using specimens that are smaller than the sizes recommended by ASTM standards. Here, this work has investigated whether subsized specimens can be used to reliably predict strength behavior. The results show that (1) tensile strength was loosely coupled to specimen volume, (2) the compression specimens had a slightly higher strength for larger volumes, (3) the uniaxial flexural strength was nearly independent of specimen effective area for one orientation whereas the other orientation showed a slight strength–size scaling Weibull behavior, and (4) equibiaxial flexural strength followed traditional strength–size scaling Weibull behavior. These results suggest that fine-grain graphite is more similar to ceramics than to medium- and large-grained graphite with respect to both the strength-limiting flaws (Griffith theory) and the effect of machining on the strength behavior. This work shows that using specimens that are smaller than ASTM recommendations are suitable for investigating the strength changes caused by neutron irradiation because the primary interest is the relative change in the strength distribution parameters rather than their absolute values.

36 MATERIALS SCIENCE↗