NASA NTRS1984

Bulk undercooling

Bulk undercooling methods and procedures will first be reviewed. Measurement of various parameters which are necessary to understand the solidification mechanism during and after recalescence will be discussed. During recalescence of levitated, glass-encased large droplets (5 to 8 mm diam) high speed temperature sensing devices coupled with a rapid response oscilloscope are now being used at MIT to measure local thermal behavior in hypoeutectic and eutectic binary Ni-Sn alloys. Dendrite tip velocities were measured by various investigators using thermal sensors or high speed cinematography. The confirmation of the validity of solidification models of bulk-undercooled melts is made difficult by the fineness of the final microstructure, the ultra-rapid evolution of the solidifying system which makes measurements very awkward, and the continuous modification of the microstructure which formed during recalescence because of precipitation, remelting and rapid coarsening.

Kattamis, T. Z.↗

NASA NTRS1981

Reduced gravity favors columnar crystal growth

In zero gravity, alined columnar microstructures form at expense of equiaxed growth. Preferential crystal growth occurs in solidification chamber consisting of semicylindrical copper chill block brazed to stainless steel top plate. Method is best utilized in castings where directional dependence of physical properties is beneficial, as in turbine blades.

Kattamis, T. Z.↗

NASA NTRS1980

The effect of reduced gravity on solidification microstructures of NH4Cl-H2O alloys

The effect of gravity on the columnar-to-equiaxed microstructural transition was studied in small samples of NH4Cl-H2O. The behavior of the samples during laboratory (one gravity) experiments was contrasted with their behavior during a (low gravity) sounding rocket flight. In one gravity, the columnar zone accounted for 25 to 100 pct of the structure, depending on the superheat and orientation of the chill. Grain multiplication occurred by showering and by convection induced dendrite arm remelting. Convection was caused by both thermal gradients and solutal gradients. In low gravity, however, completely columnar structures were obtained; all grain multiplication mechanisms were entirely suppressed. Reduced gravity also modified the thermal conditions and caused the liquid to cool more slowly. This resulted in a steeper temperature gradient in the liquid ahead of the solidification interface. 'Big bang' type nucleation occurred in two of the samples, distributing nuclei throughout the liquid. Despite this, an equiaxed zone did not form, indicating that the most significant effect of low gravity on this experiment was modification of the thermal conditions.

Papazian, J. M.↗

NASA NTRS1977

Flight IV technical report for experiment 74-37 contained polycrystalline solidification in low-G

Experiments were performed to study the effect of a low-gravity environment on the columnar-to-equiaxed transition (CET) during polycrystalline solidification. Solutions of H2O-30 wt% NH4Cl and H2O-37 wt% NH4Cl were solidified in semicylindrical molds with radial heat extraction. Both solutions were quenched from the same soak temperature (90 C); the respective superheat temperatures were, therefore, approximately 57 and 23 C. The lower superheat resulted in a completely columnar structure, and the higher superheat resulted in a 1/3 columnar - 2/3 equiaxed microstructure; these results were independent of the relationship between heat flow direction and gravity. Grain multiplication mechanisms observed were showering, thermal inversion driven convection cells, and compositionally induced density inversion driven convection cells.

Papazian, J. M.↗

NASA NTRS1976

Flight 1 technical report for experiment 74-37 contained polycrystalline solidification in low-G

A .005 M solution of fluorescein in cyclohexanol was directionally solidified in a standard 10 x 10 x 45mm UV silica cuvette, using a bottom thermoelectric chilling device. Progress of the experiment was monitored by time lapse photography. During flight (SPAR I) the camera malfunctioned and only one quarter of the expected data were collected. Comparison of flight and ground specimens indicated that: (1) The dark green layer observed ahead of the solid-liquid interface which is most likely the solute-enriched zone, appears to be wider in the flight specimen; (2) Parasitic nucleation ahead of the solid-liquid interface in the flight sample led to an irregularly shaped interface, smaller grain size, equiaxed grain morphology and a larger average macroscopic growth rate; (3) The formation of equiaxed grains ahead of the solid-liquid interface in the flight specimen may be attributed to ordered islands within the liquid, which survived remelting because of the low degree of superheating (approximately equal to 1.5 C), did not settle because of reduced gravity and acted as nuclei during cooling.

Papaziak, J. M.↗

NASA NTRS1973

Investigation of solidification in zero-gravity environment; M553 sphere forming experiment. Phase C: Evaluation of Skylab specimens

Results on specimen evaluation and discussion of solidification behavior in each case are reported in the following order: (1) specimen SL-1.6, (2) specimen SL-2.8, (3) specimen SL-2.4, (4) specimen SL-1.10 and (5) specimen SL-1.11. Comparison is made with ground-processed specimens of similar composition, whenever pertinent and meaningful. Among the nondestructive evaluation methods the measurement of sphericity was conducted by micrometric and shadowgraphic techniques. The intricate shape of specimens in some cases appeared difficult to define. In measuring the density, liquid penetration inside cavities that outcrop on the surface was avoided by sealing off these cavities. Among the destructive evaluation methods the use of the Quantimet 720 required particular attention, because of the small difference in contrast between second phases and micropores. With regard to microporosity microvoids in the core of some specimens were so fine that X-ray microradiography had to be used.

Kattamis, T. Z.↗

NASA NTRS1973

Investigation of solidification in zero-gravity environment: M553 sphere forming experiment. Nickel-silver alloy evaluation

The processing of nickel-silver alloy specimens in space is discussed. Four specimens were melted only partially, while a fifth was melted completely and assumed after solidification a perfectly spherical shape. Growth of the solid was epitaxial on the unmelted material or on the retaining sting and occurred without undercooling. Solidification was dendritic in all cases with nonequilibrium silver particles forming monotectically between dendrite arms. Substantial loss of silver by evaporation took place. Evaporation of the silver within internal gas cavities on the melt was followed by surface condensation after completion of solidification and cooling, leading to a silver-rich lining in these cavities. The material gave no microstructural evidence of any reduction in liquid convection.

Kattamis, T. Z.↗