Into the Void: Single Nanopore in Colloidally Synthesized Bi 2 Te 3 Nanoplates with Ultralow Lattice Thermal Conductivity
Not Available
Engineering topics
Publications and source records attributed to Kauzlarich, Susan M..
Not Available
Not Available
Thermoelectrics are an important class of materials with great potential in alternative energy applications. In this study, two-dimensional (2D) nanoplates of the layered chalcogenides, Sb 2 Te 3 and Bi 2 Te 3 , are synthesized and composites of the two are investigated for their thermoelectric properties. The two materials, Sb 2 Te 3 and Bi 2 Te 3 , were synthesized as hexagonal, 2D nanoplates via a colloidal polyol route. The as-synthesized Sb 2 Te 3 and Bi 2 Te 3 vary drastically from one another in their lateral and vertical dimensions as revealed by scanning electron microscopy and atomic force microscopy. The single crystalline nanoplate nature is deduced by high-resolution transmission electron microscopy and selected area electron diffraction. Nanoplates have well-defined hexagonal facets as seen in the scanning and transmission electron microscopy images. The nanoplates were consolidated as an anisotropic nanostructured pellet via spark plasma sintering. Preferred orientation observed in the powder X-ray diffraction pattern and scanning electron microscopy images of the fractured pellets confirm the anisotropic structure of the nanoplates. Thermoelectric properties in the parallel and perpendicular directions were measured, revealing strong anisotropy with a significant reduction to thermal conductivity in the perpendicular direction due to increased phonon scattering at nanoplate interfaces. All compositions, except that of the 25% Bi 2 Te 3 nanoplate composite, behave as degenerate semiconductors with increasing electrical resistivity as the temperature increases. The Seebeck coefficient is also increased dramatically in the nanocomposites, the highest reaching 210 μV/K for 15% Bi 2 Te 3 . The increase in Seebeck is attributed to energy carrier filtering at the nanoplate interfaces. Overall, these enhanced thermoelectric properties lead to a drastic increase in the thermoelectric performance in the perpendicular direction, with zT ~ 1.26, for the 15% Bi 2 Te 3 nanoplate composite at 450 K.
Crystallization of amorphous materials by thermal annealing has been investigated for numerous applications in the fields of nanotechnology, such as thin-film transistors and thermoelectric devices. The phase transition and shape evolution of amorphous germanium (Ge) and Ag@Ge core–shell nanoparticles with average diameters of 10 and 12 nm, respectively, were investigated by high-energy electron beam irradiation and in situ heating within a transmission electron microscope. The transition of a single Ge amorphous nanoparticle to the crystalline diamond cubic structure at the atomic scale was clearly demonstrated. Depending on the heating temperature, a hollow Ge structure can be maintained or transformed into a solid Ge nanocrystal through a diffusive process during the amorphous to crystalline phase transition. Selected area diffraction patterns were obtained to confirm the crystallization process. In addition, the thermal stability of Ag@Ge core–shell nanoparticles with an average core of 7.4 and a 2.1 nm Ge shell was studied by applying the same beam conditions and temperatures. The results show that at a moderate temperature (e.g., 385 °C), the amorphous Ge shell can completely crystallize while maintaining the well-defined core–shell structure, while at a high temperature (e.g., 545 °C), the high thermal energy enables a freely diffusive process of both Ag and Ge atoms on the carbon support film and leads to transformation into a phase segregated Ag–Ge Janus nanoparticle with a clear interface between the Ag and Ge domains. In conclusion, this study provides a protocol as well as insight into the thermal stability and strain relief mechanism of complex nanostructures at the single nanoparticle level with atomic resolution.
Explore the source record for details and available documents.
The new Eu 5 Al 3 Sb 6 phase has been successfully synthesized as a pure phase through Sn flux methods yielding large, high-quality crystals. This structure type features disordered Al clusters that appear in the form of dual tetrahedra. It crystallizes in the monoclinic C2/m space group exhibiting a rock-salt-like Eu–Sb framework with [Al 4 ] tetrahedra replacing some of the cationic Eu atoms (space group: C2/m, a = 8.151(1) Å, b = 14.181(2) Å, c = 8.145(1) Å, β = 109.577(2)°). The structure models the [Al 4 ] as dual tetrahedra with the Al atom sites 37.5% occupied along with Eu present on the central site at 8% occupancy and the remainder of the site being vacant. The presence of the [Al 4 ] cluster is further supported by HRTEM. Electronic structure calculations show that this material is a semimetal with observed band crossings close to the Fermi level. Strong Al–Sb antibonding interactions were found from COHP calculations close to the Fermi level and provide the rationale for the deficiency of the Al cluster. Mössbauer spectroscopy on Eu-151 and Sb-121 provides oxidation states of 2+ and 3– along with the local environment. Magnetic susceptibility measurements can be described well with a Curie–Weiss law where an effective moment of 7.80 μB/mol Eu is obtained, consistent with Eu 2+ , and show canted antiferromagnetic behavior below 10 K. Temperature dependent resistivity shows a Kondo-like low-temperature upturn caused by enhanced scattering of the itinerant electrons with the 4f orbitals of Eu.