Enabling 4C Fast Charging of Lithium–Ion Batteries by Coating Graphite with a Solid–State Electrolyte

Enabling fast-charging (≥4C) of lithium-ion batteries is an important challenge to accelerate the adoption of electric vehicles. However, the desire to maximize energy density has driven the use of increasingly thick electrodes, which hinders rate capability. Herein, atomic layer deposition is used to coat a single-ion conducting solid electrolyte (Li 3 BO 3 -Li 2 CO 3 ) onto postcalendered graphite electrodes, forming an artificial solid-electrolyte interphase (SEI). When compared to uncoated control electrodes, the solid electrolyte coating: 1) eliminates natural SEI formation during preconditioning; 2) decreases interphase impedance by >75% compared to the natural SEI; and 3) extends cycle life under 4C charging conditions, enabling retention of 80% capacity after 500 cycles (compared to 12 cycles in the uncoated control) in pouch cells with >3 mAh cm –2 loading. Furthermore, this work demonstrates that 4C charging without Li plating can be achieved through purely interfacial modification without sacrificing energy density and sheds new light on the role of the SEI in Li plating and fast-charge performance.

25 ENERGY STORAGE↗
DOE OSTI2021

Operando video microscopy of Li plating and re-intercalation on graphite anodes during fast charging

Despite the demand for fast-charging lithium (Li)-ion batteries, high-energy-density batteries with thick graphite anodes are limited by Li plating when charging at >4C rates. In this work, plan-view operando video microscopy is applied on >3 mA h cm –2 calendared graphite electrodes to study the dynamic evolution of local state-of-charge (SoC) and Li plating during fast charging. This technique allows for visualization of the spatial heterogeneity in SoC across the electrode, nucleation and growth of Li filaments, Li re-intercalation into graphite, “dead Li” formation, and SoC equilibration. The operando microscopy analysis is complemented by ex situ imaging of through-plane gradients in SoC to gain a three-dimensional visualization of spatial heterogeneity. We demonstrate that (1) Li plating preferentially nucleates on the graphite particles that lithiate fastest during fast charging; (2) the onset of Li plating correlates with the local minimum of the graphite electrode potential; (3) galvanic corrosion currents are responsible for Li re-intercalation, dead Li formation, and SoC re-equilibration after fast charging; and (4) electrochemical signatures during OCV rest or discharge are associated with Li re-intercalation into graphite. Furthermore, this work provides insight into the Li–graphite interactions at the composite electrode level and can be used to inform strategies to diagnose and mitigate Li plating during fast charging.

25 ENERGY STORAGE↗
DOE OSTI2021

Method of improved performance in metal electrodes for batteries

Disclosed are methods for pre-conditioning or pre-treating the surface of a metal (e.g., lithium) electrode such that the cycle life and efficiency of the electrode within an electrochemical cell are improved through the prevention of dendrite growth. The pretreatment process includes the use of an alternating current to modify the surface properties of the metal electrode, such that a more uniform flux of metal ions is transferred across the electrode-electrolyte Interface in subsequent electrodeposition and electrodissolution processes. As a result, an electrode treated with such a process exhibits improved performance and durability, including markedly lower overpotentials and largely improved metal (e.g., lithium) retention in strip plate tests as compared with untreated electrodes.

Dasgupta, Neil P.↗
DOE OSTI2020

Electro-chemo-mechanical evolution of sulfide solid electrolyte/Li metal interfaces: operando analysis and ALD interlayer effects

Sulfide solid electrolytes (SE) show promise for high-performance solid-state batteries because of their high ionic conductivity and ease of processing. However, sulfide electrolytes have suffered from chemical and electrochemical instability against Li metal anodes. In this paper, we use a suite of in situ/operando microscopy and spectroscopy techniques to demonstrate that Al 2 O 3 interlayers deposited using atomic layer deposition (ALD) delay degradation at the Li/LGPS interface by modifying the solid electrolyte interphase (SEI) chemistry and morphology. Optical and scanning electron microscopy are used to rationalize the electrochemical response of the system, which is attributed to a delayed onset of mechanical degradation at the interface when ALD interlayers are used. Operando X-ray photoelectron spectroscopy demonstrates that the dynamic evolution of SEI chemistry is impacted by the presence of the ALD interlayer. In situ Auger spectroscopy and operando optical microscopy provide visual evidence of spatial heterogeneity of Li plating, which is attributed to the chemo-mechanical degradation of the ALD interphase. The implications of these observations provide valuable insights toward the development of robust interlayers for solid-state batteries.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗