7 records

DOE OSTI2022

2,3-Diphenylthieno[3,4-b]pyrazines as Hole-Transporting Materials for Stable, High-Performance Perovskite Solar Cells

High-performance and durable perovskite solar cells (PSCs) have advanced rapidly, enabled in part by the development of superior interfacial hole-transporting layers (HTLs). Here, in this study, a new series of 2,3-diphenylthieno[3,4-b]pyrazine (DPTP)-based small molecules containing bis- and tetrakis-triphenyl amino donors (1–3) was synthesized from simple, low-cost, and readily available starting materials. The matched energy levels, ideal surface topographies, high hole mobilities of 8.57 × 10 –4 cm 2 V –1 S –1 , and stable chemical structures of DPTP-4D (3) make it an effective hole-transporting material, delivering a PCE of 20.18% with high environmental, thermal, and light-soaking stability when compared to the reference HTL materials, doped Spiro-OMeTAD and PTAA in PSC n-i-p planar devices. Overall, these DPTP-based molecules are promising HTM candidates for the fabrication of stable PSCs.

14 SOLAR ENERGY↗

DOE OSTI2022

Film formation mechanisms in mixed-dimensional 2D/3D halide perovskite films revealed by in situ grazing-incidence wide-angle X-ray scattering

We report mixed dimensionality 2D/3D hybrid halide perovskites retain the stability of 2D perovskites (formula (A')2(A)n-1PbnI3n+1) and long diffusion lengths of the 3D materials (formula AMX3), thereby affording solar cells with extended stability as well as state of the art efficiencies approaching that of the 3D materials. These films are made by spin coating precursor solutions with arbitrarily large average layer thickness n ($\langle$n$\rangle$ > 7) to give films with both 2D and 3D phases present. While the 2D and 3D perovskite film formation mechanisms have been studied previously, little is understood about composite 2D/3D film formation. We used in situ grazing-incidence wide-angle scattering (GIWAXS) with synchrotron radiation to fully characterize films fabricated from precursor solutions with stoichiometries of (BA) 2 (MA) n-1 Pb n I 3n+1 ($\langle$n$\rangle$ = 3, 4, 5, 7, “12,” “50,” and ∞ (MAPbI 3 )). Four different mechanisms are seen depending on the stoichiometry in the precursor solution. When $\langle$n$\rangle$ = 3, oriented perovskite grows directly. For $\langle$n$\rangle$ = 4-5, the needle-shaped solvate (MA) 2 Pb 3 I 8 ·2DMF forms concomitantly with the oriented perovskite which leads to 2D/3D composite films. For $\langle$n$\rangle$ ≥ 7, this solvate dominates and unoriented perovskite grows in secondarily. For 3D perovskite, the solvate is the only phase formed. Kinetic analysis shows faster and earlier growth of the solvate with increasing $\langle$n$\rangle$. Using this knowledge, we show that the undesirable solvate mechanism can be reduced by addition of excess ammonium iodide in the precursor solution to give highly oriented films.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2021

Organic-inorganic hybrid perovskite compounds

Photoactive materials comprising organic-inorganic hybrid halide perovskite compounds are provided. Photovoltaic cells and light-emitting devices incorporating the photoactive materials into their light-absorbing and light-emitting layers, respectively, are also provided. The halide perovskites have an amAMX3 perovskite crystal structure, wherein am is an alkyl diamine cation, an aromatic diamine cation, an aromatic azole cation, a cyclic alkyl diamine cation or a hydrazinediium cation; A is a monovalent alkylammonium cation or an alkali metal cation; X is a halide ion or a combination of halide ions; and M is an octahedrally coordinated bivalent metal atom.

Ke, Weijun↗

DOE OSTI2021

Tunable Broad Light Emission from 3D “Hollow” Bromide Perovskites through Defect Engineering

We report hybrid halide perovskites consisting of corner-sharing metal halide octahedra and small cuboctahedral cages filled with counter cations have proven to be prominent candidates for many high-performance optoelectronic devices. The stability limits of their three-dimensional perovskite framework are defined by the size range of the cations present in the cages of the structure. In some cases, the stability of the perovskite-type structure can be extended even when the counterions violate the size and shape requirements, as is the case in the so-called "hollow" perovskites. In this work, we engineered a new family of 3D highly defective yet crystalline "hollow" bromide perovskites with general formula (FA) 1-x (en) x (Pb) 1-0.7x (Br) 3-0.4x (FA = formamidinium (FA + ), en = ethylenediammonium (en 2+ ), x = 0-0.44). Pair distribution function analysis shed light on the local structural coherence, revealing a wide distribution of Pb-Pb distances in the crystal structure as a consequence of the Pb/Br-deficient nature and en inclusion in the lattice. By manipulating the number of Pb/Br vacancies, we finely tune the optical properties of the pristine FAPbBr 3 by blue shifting the band gap from 2.20 to 2.60 eV for the x = 0.42 en sample. A most unexpected outcome was that at x > 0.33 en incorporation, the material exhibits strong broad light emission (1% photoluminescence quantum yield (PLQY)) that is maintained after exposure to air for more than a year. This is the first example of strong broad light emission from a 3D hybrid halide perovskite, demonstrating that meticulous defect engineering is an excellent tool for customizing the optical properties of these semiconductors.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2020

CsPbBr3 perovskite detectors with 1.4% energy resolution for high-energy γ-rays

Halide perovskite semiconductors are poised to revitalize the field of ionizing radiation detection as they have done to solar photovoltaics. We show that all-inorganic perovskite CsPbBr 3 devices resolve 137 Cs 662-keV γ-rays with 1.4% energy resolution, as well as other X- and γ-rays with energies ranging from tens of keV to over 1 MeV in ambipolar sensing and unipolar hole-only sensing modes with crystal volumes of 6.65 mm 3 and 297 mm 3 , respectively. Furthermore, we report the scale-up of CsPbBr 3 ingots to up to 1.5 inches in diameter with an excellent hole mobility–lifetime product of 8 × 10 -3 cm 2 V -1 and a long hole lifetime of up to 296 μs. CsPbBr 3 detectors demonstrate a wide temperature region from ~2 °C to ~70 °C for stable operation. Detectors protected with suitable encapsulants show a uniform response for over 18 months. Consequently, we identify perovskite CsPbBr 3 semiconductor as an exceptional candidate for new-generation high-energy γ-ray detection.

47 OTHER INSTRUMENTATION↗

DOE OSTI2020

Water-Stable 1D Hybrid Tin(II) Iodide Emits Broad Light with 36% Photoluminescence Quantum Efficiency

The optical and light emission properties of tin and lead halide perovskites are remarkable because of the robust room-temperature (RT) performance, broad wavelength tunability, high efficiency, and good quenching resistance to defects. These highly desirable attributes promise to transform current light-emitting devices, phosphors, and lasers. One disadvantage in most of these materials is the sensitivity to moisture. Here, we report a new air-stable one-dimensional (1D) hybrid lead-free halide material (DAO)Sn 2 I 6 (DAO, 1,8-octyldiammonium) that is resistant to water for more than 15 h. The material exhibits a sharp optical absorption edge at 2.70 eV and a strong broad orange light emission centered at 634 nm, with a full width at half-maximum (fwhm) of 142 nm (0.44 eV). The emission has a long photoluminescence (PL) lifetime of 582 ns, while the intensity is constant over a very broad temperature range (145–415 K) with a photoluminescence quantum yield (PLQY) of at least 20.3% at RT. Above 415 K the material undergoes a structural phase transition from monoclinic (C2/c) to orthorhombic (Ibam) accompanied by a red shift in the band gap and a quench in the photoluminescence emission. Density functional theory calculations support the trend in the optical properties and the 1D electronic nature of the structure, where the calculated carrier effective masses along the inorganic chain are significantly lower than those perpendicular to the chain. As a result, thin films of the compound readily fabricated from solutions exhibit the same optical properties, but with improved PLQY of 36%, for a 60 nm thick film, among the highest reported for lead-free low-dimensional 2D and 1D perovskites and metal halides.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2020

Three-Dimensional Lead Iodide Perovskitoid Hybrids with High X-ray Photoresponse

Large organic A cations cannot stabilize the 3D perovskite AMX 3 structure because they cannot be accommodated in the cubo-octhedral cage (do not follow the Goldschmidt tolerance factor rule), and they generally template low-dimensional structures. In this paper, we report that the large dication aminomethylpyridinium (AMPY) can template novel 3D structures which resemble conventional perovskites. They have the formula (xAMPY)M 2 I 6 (x = 3 or 4, M = Sn 2+ or Pb 2+ ) which is double of the AMX3 formula. However, because of the steric requirement of the Goldschmidt tolerance factor rule, it is impossible for (xAMPY)M 2 I 6 to form proper perovskite structures. Instead, a combination of corner-sharing and edge-sharing connectivity is adopted in these compounds leading to the new 3D structures. DFT calculations reveal that the compounds are indirect band gap semiconductors with direct band gaps presenting at slightly higher energies and dispersive electronic bands. The indirect band gaps of the Sn and Pb compounds are ~1.7 and 2.0 eV, respectively, which is slightly higher than the corresponding AMI 3 3D perovskites. The Raman spectra for the compounds are diffuse, with a broad rising central peak at very low frequencies around 0 cm –1 , a feature that is characteristic of dynamical lattices, high anharmonicity, and dissipative vibrations very similar to the 3D AMX 3 perovskites. Devices of (3AMPY)Pb 2 I 6 crystals exhibit clear photoresponse under ambient light without applied bias, reflecting a high carrier mobility (μ) and long carrier lifetime (τ). The devices also exhibit sizable X-ray generated photocurrent with a high μτ product of ~1.2×10 -4 cm 2 /V and a X-ray sensitivity of 207 μC∙Gy -1 ∙cm -2 .

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗