Damage of thermal control coating properties by energetic mercury ion bombardment.
The thermophysical properties (absorptance and emittance) of five commonly used spacecraft thermal control coatings have been measured in situ after exposure to 1.5 and 3 KeV mercury ions. Sample temperature was varied from 20 to 150 C. The results showed negligible change in emittance but significant degradation of the solar absorptance at fluences of 10 to the 17th power ions/sq cm. Plots of absorptance as a function of ion fluence are presented, along with pre- and post-exposure ex situ spectral absorptance measurements. The widely used Z93 white paint exhibited quantitative degradation from mercury ions similar to that reported by other experimenters for hydrogen and helium ions.
Kelley, L. R.↗