Demonstration of Niobium Tin in 218 MHz Low-beta Quarter Wave Accelerator Cavity

A 218 MHz quarter wave niobium cavity has been fabricated for the purpose of demonstrating Nb3Sn technology on a low-beta accelerator cavity. Niobiumtin has been established as a promising next generation SRF material, but development has focused primarily in high-beta elliptical cell cavities. This material has a significantly higher TC than niobium, allowing for design of higher frequency quarter wave cavities (that are subsequently smaller) as well as for significantly lowered cooling requirements (possibly leading to cryocooler based designs). The fabrication, initial cold testing, and Nb3Sn coating are discussed as well as test plans and details of future applications.

43 PARTICLE ACCELERATORS↗
DOE OSTI2023

Demonstration of Niobium Tin in 218 MHz Low-beta Quarter Wave Accelerator C

A 218 MHz quarter wave niobium cavity has been fabricated for the purpose of demonstrating Nb3Sn technology on a low-beta accelerator cavity. Niobium-tin has been established as a promising next generation SRF material, but development has focused primarily in high- beta elliptical cell cavities. This material has a significantly higher TC than niobium, allowing for design of higher frequency quarter wave cavities (that are subsequently smaller) as well as for significantly lowered cooling requirements (possibly leading to cryocooler based designs). The fabrication, initial cold testing, and Nb3Sn coating are discussed as well as test plans and details of future applications.

72 PHYSICS OF ELEMENTARY PARTICLES AND FIELDS↗
DOE OSTI2023

Demonstration of Niobium Tin in 218 MHz Low-beta Quarter Wave Accelerator C

A 218 MHz quarter wave niobium cavity has been fabricated for the purpose of demonstrating Nb3Sn technology on a low-beta accelerator cavity. Niobium-tin has been established as a promising next generation SRF material, but development has focused primarily in high- beta elliptical cell cavities. This material has a significantly higher TC than niobium, allowing for design of higher frequency quarter wave cavities (that are subsequently smaller) as well as for significantly lowered cooling requirements (possibly leading to cryocooler based designs). The fabrication, initial cold testing, and Nb3Sn coating are discussed as well as test plans and details of future applications.

72 PHYSICS OF ELEMENTARY PARTICLES AND FIELDS↗
DOE OSTI2023

Electropolishing parameters study for surface smoothening of low-$\beta$650 MHz five-cell niobium superconducting radio frequency cavity

Electropolishing (EP) is applied to niobium (Nb) superconducting radio frequency (SRF) cavities, which are used in particle accelerators for their surface treatment. The EP process for 1.3 GHz cavities has been extensively studied earlier. In this work, a parametric study on EP of low-β (0.61) 650 MHz Nb SRF cavities (LB650), which will be used in pre-production cryomodule for proton improvement plan-II (PIP-II) linear accelerator, was conducted to determine adequate EP conditions for attaining a smooth surface of the cavities. EP performed with the standard parameters and an initial cathode (cathode-I) having a cathode surface area of ~5% of the cavity surface area yielded a rough equator surface of the cavity. The grain step height on the equator weld position was measured to be ~ 32 μm. The rough surface was attributed to preferential grain etching confirmed by a polarization curve showing a linear relationship between the EP current and voltage and the absence of the current plateau region. The cathode was modified to make its surface area twice that of cathode-I. The modified cathode (cathode-M) provided a current plateau region in the corresponding I-V curves measured at different cavity temperatures. The onset voltage for the plateau was found to be higher at higher cavity temperatures. Here this study revealed that even with cathode-M, the standard 18 V was low for EP of such large-sized cavities when the cavity temperature was 18 °C. EP performed at a higher voltage of 22–24.5 V with cathode-M yielded a smooth surface with a grain step height of only 0.6 μm. The applied EP conditions also improved removal uniformity along the cavity length. In contrast to the cavity treated with cathode-I, the cavities treated with cathode-M achieved a significantly higher accelerating gradient (E acc ) in vertical tests conducted in a cryostat at 2 K. The modified EP was found efficient to produce the cavities that achieved E acc of 22.4 MV/m, required by PIP II project in the baseline RF tests, to qualify for further surface processing used to enhance their quality factors.

72 PHYSICS OF ELEMENTARY PARTICLES AND FIELDS↗
DOE OSTI2022

Study on Electropolishing Conditions for 650 MHz Niobium SRF Cavity

The PIP II linear accelerator includes different types of niobium SRF cavities including 650 MHz elliptical low (0.61) and high (0.92) beta cavities. The elliptical cavity surface is processed with the electropolishing method. The elliptical cavities especially the low-$\beta$ 650 MHz cavities showed a rough equator surface after the EP was per-formed with the standard EP conditions. This work was focused to study the effect of different EP parameters, including cathode surface area, temperature and voltage, and optimize them to improve the cavity surface.

72 PHYSICS OF ELEMENTARY PARTICLES AND FIELDS↗