The Shape Factor for Pits and Its Impact on Pit Stability

This study employs the finite element method (FEM) to predict the impact of pit shape on pit stability via shape factors of various pit geometries relevant to localized corrosion. Lower values of the shape factor indicate an increased ease in maintaining pit stability. Analyzed geometries include undercut pits, bispherical pit-within-pit structures, and covered pits with perforated (lacy) covers. The effect of the water layer thickness, transport properties of the electrolyte inside and outside the pit, and cathode location on the pit shape factor were also explored. Results show that occluded pits exhibit lower shape factors than open ones, with disk-shaped pits decreasing further as c/r ratio and occlusion angle increase. The findings also suggest minimal influence from a secondary pit if the primary remains active. An equation is presented that quantifies the impact of lacy covers, revealing significant shape factor value reduction. Additionally, high salt concentrations inside pits have a limited stabilizing effect compared to geometry, while thin water layers and adjacent cathodic/sinks reduce pit stability.

Shehi, A. (ORCID:0009000271548041)↗

DOE OSTI2023

Influence of Realistic, Cyclic Atmospheric Cycles on the Pitting Corrosion of Austenitic Stainless Steels

Pitting corrosion was evaluated on stainless steels 304H, 304, and 316L the surfaces of which had ASTM seawater printed on them as a function of surface roughness after exposure to an exemplar realistic atmospheric diurnal cycle for up to one year. Methods to evaluate pitting damage included optical imaging, scanning electron microscopy imaging, profilometry analysis, and polarization scans. The developed cyclic exposure environment did not significantly influence pitting morphology nor depth in comparison to prior static exposure environments. Cross-hatching was observed in a majority of pits for all material compositions with the roughest surface finish (#4 finish) and in all surface finishes for the 304H composition. Evidence is provided that cross-hatched pit morphologies are caused by slip bands produced during the grinding process for the #4 finish or by material processing. Additionally, micro-cracking was observed in pits formed on samples with the #4 surface finish and was greatly reduced or absent for pits formed on samples with smooth surface finishes. This suggests that both a low RH leading to an MgCl 2 -dominated environment and a rough surface containing significant residual stress are necessary for micro-cracking. Finally, the use of various characterization techniques and cross sectioning was employed to both qualitatively and quantitatively assess pitting damage across all SS compositions and surface finishes.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Cathodic Kinetics on Platinum and Stainless Steel in NaOH Environments

During typical atmospheric conditions, cathodic reduction reactions produce hydroxyl ions increasing the pH in the cathodic region. Therefore, cathodic reduction reactions are investigated on platinum and stainless steel 304 L (SS304L) in NaOH solutions ranging in pH from 13.6 to 16.5. It was found that in solution pHs less than 16.5 the cathodic reduction reaction on Pt and SS304L was ORR with an electron transfer number less than two due to superoxide formation as an intermediate. Increasing pH decreased the number of electrons transferred. At a pH of 16.5, the cathodic reduction reaction on SS304L is no longer ORR and the cathodic current on the surface of the alloy is due to oxide reduction occurring on the surface as indicated by the creation of multi-component Pourbaix diagrams. The results of this study have important implications for predicting corrosion in atmospheric environments.

25 ENERGY STORAGE↗

DOE OSTI2021

Editors’ Choice—Natural Convection Boundary Layer Thickness at Elevated Chloride Concentrations and Temperatures and the Effects on a Galvanic Couple

The natural convection boundary layer ( δ n c ) and its influence on cathodic current in a galvanic couple under varying electrolytes as a function of concentration (1 − 5.3 M NaCl) and temperature (25 °C−45 °C) were understood. Polarization scans were obtained under quiescent conditions and at defined boundary layer thicknesses using a rotating disk electrode on platinum and stainless steel 304L (SS304L); these were combined to determine δ n c . With increasing chloride concentration and temperature, δ n c decreased. Increased mass transport (Sherwood number) results in a decrease in δ n c , providing a means to predict this important boundary. Using Finite Element Modeling, the cathodic current was calculated for an aluminum alloy/SS304L galvanic couple as a function of water layer ( WL ) thickness and cathode length. Electrolyte domains were delineated, describing (i) dominance of ohmic resistance over mass transport under thin WL , (ii) the transition from thin film to bulk conditions at δ n c , and (iii) dominance of mass transport under thick WL . With increasing chloride concentration, cathodic current decreased due to decreases in mass transport. With increasing temperature, increased cathodic current was related to increases in mass transport and solution conductivity. This study has implications for sample sizing and corrosion prediction under changing environments.

25 ENERGY STORAGE↗