DOE OSTI2020

Synthesis and flash sintering of (Hf 1-x Zr x )B 2 solid solution powders

(Hf 1-x Zr x )B 2 solid solution powders were synthesized by two methods. First, solution-based processing of HfCl 4 , ZrCl 4 , sucrose, and H 3 BO 3 was conducted followed by heat treatment in Argon to carry out the carbothermal reduction (CTR) reaction to form the diboride powders. Alternatively, in the so-called borohydride reduction (BHR) method, HfCl 4 , ZrCl 4 and NaBH 4 were mixed in an Argon glove box followed by heat treatment in Argon at 700-1500°C. The synthesized powders were characterized by XRD, SEM, TEM, EDS, and TGA, and the influence of different parameters such as starting composition, heat treatment temperature and time on products characteristics were revealed. Both CTR and BHR solid solution powders were then consolidated within ~5 min in a homemade flash sintering (FS) setup. Here, the composition, microstructure, hardness, and thermal-oxidation properties of flash sintered ceramics were characterized, and the implication of this study and directions for future research were discussed.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Synthesis and Flash Sintering of (Hf1-xZrx)B2 Solid Solution Fine Powders

Fine powders of (Hf1-xZrx)B2 solid solution were synthesized by two methods. In the first one, solution-based processing of HfCl4, ZrCl4, sucrose and H3BO3 was carried out followed by heat treatment (e.g., at 1500 °C for 1 h) in Argon to achieve the carbothermal reduction (CTR) reaction to form the boride solid solution. In the second one, called boron hydride reduction (BHR) method, HfCl4, ZrCl4 and NaBH4 were directly mixed in a glove box followed by heat treatment in Argon at elevated temperatures from 700 to 1500 °C. In addition, the powders synthesized via both methods were flash sintered without sample preheating in a homemade setup. The synthesized powders as well as the flash sintered bulk ceramics were characterized using different techniques including XRD, SEM, EDS, TEM, TGA-DSC, and Vickers hardness test to reveal the inter-relationships between starting materials composition, processing conditions, and the resulting materials microstructure and physical/chemical properties.

Belisario, Jose↗