NASA NTRS1990

Hydrogen permeation, diffusion and solubility in IN-100 and Waspaloy

An attempt has been made to determine the permeation rate of hydrogen in IN-100 and Waspaloy by determining the evolution rate of hydrogen from a closed capsule of the test materials. Enclosed vanadium hydride was the source of hydrogen in the capsule. The presentation discusses the treatment of data and assesses the validity of the techniques in permeation measurement. In addition to permeation experiments, the solubility and diffusion of hydrogen in IN-100 and Waspaloy were also determined. For hydrogen diffusion in Waspaloy, Delta H was 38.5 kJ and D(0) was 0.0026 sq cm/sec. For IN-100, Delta H was 68.2 kJ and D(0) was 0.059 sq cm /sec. Both IN-100 and Waspaloy exhibited limited solubility of hydrogen at pressures up to 340 atmospheres hydrogen.

Khan, A. S.↗

NASA NTRS1990

Solubility and diffusion of hydrogen in IN-100 and Waspaloy

The solubility of hydrogen, at a fixed hydrogen pressure, was measured in two different heat treatment conditions in both IN-100 and Waspaloy by equilibrium and analysis. The diffusion coefficients were determined by measuring the rate of hydrogen evolution in a vacuum. Hydrogen evolution appeared to be a diffusion-controlled process in all cases. For hydrogen diffusion in Waspaloy, Delta H was 38.5 kJ and D0 was 2.6 x 10 to the -7th sq/s. For IN-100, Delta H was 68.2 kJ and D0 was 59 x 10 to the -7th sq/s. The values for Waspaloy are close to those for pure nickel. The values for IN-100 are more similar to high nickel alloys that show trapping or surface layer impedance.

Khan, A. S.↗

NASA NTRS1982

Nicral ternary alloy having improved cyclic oxidation resistance

NiCrAl alloys are improved by the addition of zirconium. These alloys are in the Beta or gamma/gamma' + Beta region of the ternary system. Zirconium is added in a very low amount between 0.06 and 0.20 weight percent. There is a narrow optimum zirconium level at the low value of 0.13 weight percent. Maximum resistance to cyclic oxidation is achieved when the zirconium addition is at the optimum value.

Barrett, C. A.↗

NASA NTRS1981

The effect of zirconium on the cyclic oxidation of NiCrAl alloys

This paper examines results with cyclic oxidation tests of Ni(9-20) Cr(15-30) Al-(x)Zr alloys carried out at 1100 C and 1200 C in static air. The concentration of zirconium varies from 0 to 0.63 atomic percent. Significant aluminum penetration is found in metallographic and electron microscopic examination of oxidized surfaces. Small amounts of zirconium lead to minimal penetration, and with increased zirconium content pronounced oxide penetration is observed.

Barrett, C. A.↗