2 kV Al 0.64 Ga 0.36 N-channel high electron mobility transistors with passivation and field plates

Abstract High voltage (∼2 kV) Al 0.64 Ga 0.36 N-channel high electron mobility transistors were fabricated with an on-resistance of ∼75 Ω. mm (∼21 mΩ. cm 2 ). Two field plates of variable dimensions were utilized to optimize the breakdown voltage. The breakdown voltage reached >3 kV (tool limit) before passivation however it reduced to ∼2 kV after Si 3 N 4 surface passivation and field plate deposition. The breakdown voltage and on-resistance demonstrated a strong linear correlation in a scattered plot of ∼50 measured transistors. The fabricated transistors were electrically characterized and benchmarked against the state-of-the-art high-voltage (> 1 kV) Al-rich (>40%) AlGaN-channel transistors in breakdown voltage and on-resistance, indicating significant progress.

Alam, Md Tahmidul (ORCID:000900086556839X)↗
DOE OSTI2024

Nonequivalent Atomic Vibrations at Interfaces in a Polar Superlattice

In heterostructures made from polar materials, e.g., AlN–GaN–AlN, the nonequivalence of the two interfaces is long recognized as a critical aspect of their electronic properties; in that, they host different 2D carrier gases. Interfaces play an important role in the vibrational properties of materials, where interface states enhance thermal conductivity and can generate unique infrared-optical activity. The nonequivalence of the corresponding interface atomic vibrations, however, is not investigated so far due to a lack of experimental techniques with both high spatial and high spectral resolution. Herein, the nonequivalence of AlN–(Al 0.65 Ga 0.35 )N and (Al 0.65 Ga 0.35 )N–AlN interface vibrations is experimentally demonstrated using monochromated electron energy-loss spectroscopy in the scanning transmission electron microscope (STEM-EELS) and density-functional-theory (DFT) calculations are employed to gain insights in the physical origins of observations. It is demonstrated that STEM-EELS possesses sensitivity to the displacement vector of the vibrational modes as well as the frequency, which is as critical to understanding vibrations as polarization in optical spectroscopies. The combination enables direct mapping of the nonequivalent interface phonons between materials with different phonon polarizations. Furthermore, the results demonstrate the capacity to carefully assess the vibrational properties of complex heterostructures where interface states dominate the functional properties.

36 MATERIALS SCIENCE↗
DOE OSTI2023

High figure of merit extreme bandgap Al 0.87 Ga 0.13 N-Al 0.64 Ga 0.36 N heterostructures over bulk AlN substrates

We report on high-quality n -Al 0.87 Ga 0.13 N-A 0.64 Ga 0.36 N heterostructures over single crystal AlN. For these pseudomorphic heterostructures, high-resolution X-ray and X-ray Topographic analysis was used to establish a threading dislocation density of 7 × 10 3 cm -2 . Using reverse composition graded n + -Al x Ga 1- x N contact layers, we obtained linear ohmic contacts with 4.3 Ω mm specific resistance. A critical breakdown field >11 MV cm -1 was also measured. In combination with the channel resistance of 2400 Ω sq -1 , these translate to a Baliga’s Figure of Merit of 2.27 GW cm -2 . This, to the best of our knowledge is the highest reported value for extreme bandgap AlGaN heterostructures.

42 ENGINEERING↗