Synthesis, crystal structure, and magnetic properties of CoMoFeAl and related compounds
We have carried out joint theoretical and experimental investigations of three Heusler compounds CoMoFeAl, CoMo 0.5 Fe 1.5 Al, and Co 1.5 Mo 0.5 FeAl. Our first-principle calculations show that all three compounds show either ferro- or ferrimagnetic order with CoMoFeAl and CoMo 0.5 Fe 1.5 Al exhibiting high spin polarization of almost 80%. The investigated samples were prepared using arc melting and high vacuum annealing. All the samples show cubic crystal structure with disorder. The parent compound CoMoFeAl shows a small saturation magnetization of 12 emu/g, and a Curie temperature of 440 K. The other two compounds, namely, Co 1.5 Mo 0.5 FeAl and CoMo 0.5 Fe 1.5 Al, show much higher saturation magnetizations of 62 emu/g and 59 emu/g, and substantially higher Curie temperatures of 950 K and 780 K, respectively.
Structural, electronic, and magnetic properties of CoFeVGe-based compounds: Experiment and theory
We have carried out a combined theoretical and experimental investigation of both stoichiometric and nonstoichiometric CoFeVGe alloys. In particular, we have investigated CoFeVGe, Co 1.25 Fe 0.75 VGe, Co 0.75 Fe 1.25 VGe, and CoFe 0.75 VGe bulk alloys. Our first principles calculations suggest that all four alloys show ferromagnetic order, where CoFeVGe, Co 1.25 Fe 0.75 VGe, and Co 0.75 Fe 1.25 VGe are highly spin polarized with spin polarization values of over 80%. However, the spin polarization value of CoFe 0.75 VGe is only about 60%. We have synthesized all four samples using arc melting and high-vacuum annealing at 600 °C for 48 hours. The room temperature x-ray diffraction of these samples exhibits a cubic crystal structure with disorder. All the samples show single magnetic transitions at their Curie temperatures, where the Curie temperature and high field (3T) magnetization are 288 K and 42 emu/g; 305 K and 1.5 emu/g; 238 K and 39 emu/g; and 306 K and 35 emu/g for CoFeVGe, Co 1.25 Fe 0.75 VGe, Co 0.75 Fe 1.25 VGe, and CoFe 0.75 VGe, respectively.
Modifying magnetic properties of MnBi with carbon: an experimental and theoretical study
MnBi and MnBi-based materials have been investigated as prospective rare-earth-free permanent magnets with moderate energy product. One of the main issues with MnBi synthesis is the presence of residual Bi in the sample which reduces the net magnetization. Here, we have found that MnBi synthesized in the presence of carbon substantially reduces the amount of residual Bi, improving its saturation magnetization. We have synthesized Mn 55 Bi 45 and Mn 55 Bi 45 C x samples using arc melting and high-vacuum annealing. The room temperature x-ray diffraction patterns indicate that both Mn 55 Bi 45 and Mn 55 Bi 45 C x crystallize in the hexagonal NiAs-type structure. The Rietveld analysis of the x-ray patterns shows that the amount of residual Bi reduces from 16 wt.% for Mn 55 Bi 45 to 5 wt.% for Mn 55 Bi 45 C x . The high-field (3 T) magnetizations measured at room temperature are 61 emu g –1 and 66 emu g –1 for Mn 55 Bi 45 and Mn 55 Bi 45 C x , respectively. To understand the role of C in enhancing the magnetization of MnBi, we carried out the first-principles calculations of both stoichiometric and nonstoichiometric MnBi alloys, which suggests that the increase of magnetization in Mn 55 Bi 45 C x may be due to the coating of MnBi grains with C.
Electronic, magnetic, and structural properties of CrMnSb 0.5 Si 0.5
Half-metallic Heusler compounds are among the most actively studied materials for applications in spin-based devices. Largely, this is due to their higher Curie temperature compared with the other half-metallic compounds, and relative ease of fabrication. Here we theoretically study one such Heusler alloy CrMnSb 0.5 Si 0.5 . In particular, we demonstrate a potential stability of this compound by estimating its formation energy, its half-metallic electronic structure (stable under a considered range of biaxial strain), and ferrimagnetic alignment. The calculated Curie temperature of this material is 787 K, much higher than room temperature. At the same time, we have shown that in thin-film geometry the spin-polarization of this material is strongly reduced due to the emergence of surface states in the minority-spin energy gap. In addition, one of the considered termination surfaces is thermodynamically unstable, while the other is stable. Here, the presented results may be useful for researchers working on practical applications in the field of spintronics.
Electronic band structure and magnetism of CoFeV 0.5 Mn 0.5 Si
Half-metallic Heusler alloys have attracted significant attention due to their potential application in spin-transport-based devices. We have synthesized one such alloy, CoFeV 0.5 Mn 0.5 Si, using arc melting and high-vacuum annealing at 600 °C for 24 hours. First principles calculation indicates that CoFeV 0.5 Mn 0.5 Si shows a nearly half-metallic band structure with a degree of spin polarization of about 93%. In addition, this value can be enhanced by the application of tensile strain. The room temperature x-ray diffraction patterns are indexed with the cubic crystal structure without secondary phases. The annealed sample shows ferromagnetic order with the Curie temperature well above room temperature ( T c = 657 K) and a saturation magnetization of about 92 emu/g. Our results indicate that CoFeV 0.5 Mn 0.5 Si has a potential for room temperature spin-transport-based devices.
Electronic, structural and magnetic properties of Mn (1+x) Pt (1-x) Sb
Electronic and magnetic properties of half-metallic Heusler alloys can be modified by tuning their chemical compositions. We have carried out a combined theoretical and experimental investigation of Mn (1+x) Pt (1-x) Sb (0 ≤ x ≤ 0.5) alloys. Our first-principles calculations indicate that the stoichiometric MnPtSb exhibits nearly half-metallic band structure, but a robust half-metallicity can be achieved in Mn-rich compositions Mn (1+x) Pt (1-x) Sb (0 ≤ x ≤ 0.5) with x = 0.25 and higher in their cubic structures. In addition, while MnPtSb exhibits ferromagnetic alignment, Mn (1+x) Pt (1-x) Sb are ferrimagnetic for all non-zero values of x. We have also synthesized cubic MnPtSb and Mn 1.25 Pt 0.75 Sb alloys using arc melting and annealing. The magnetic properties of these alloys are consistent with our theoretical predictions. Furthermore, these results indicate that the Mn-rich Mn (1+x) Pt (1-x) Sb alloys have potential for spin-transport-based devices.
Perpendicular magnetic anisotropy in half-metallic thin-film Co 2 CrAl
Magnetocrystalline anisotropy (MCA) is one of the key parameters investigated in spin-based electronics (spintronics), e.g. for memory applications. Here, we employ first-principles calculations to study MCA in thin film full Heusler alloy Co 2 CrAl. This material was studied in the past, and has been reported to exhibit half-metallic electronic structure in bulk geometry. In our recent work, we showed that it retains a 100% spin-polarization in thin-film geometry, at CrAl atomic surface termination. Here, we show that the same termination results in a perpendicular magnetic anisotropy, while Co surface termination not only destroys the half-metallicity, but also results in in-plane magnetization orientation. In addition, for films thicker than around 20 nm the contribution from magnetic shape anisotropy may become decisive, resulting in in-plane magnetization orientation. To the best of our knowledge, this is one of the first reports of half-metallic thin-film surfaces with perpendicular magnetic anisotropy. Furthermore, this result may be of interest for potential nano-device applications, and may stimulate a further experimental study of this and similar materials.
Chemical substitution induced half-metallicity in CrMnSb (1– x ) P x
Half-metallic Heusler alloys have been intensively studied in recent years due to their potential applications in spin-based devices, e.g., in magnetic tunnel junctions. Yet, their properties may be very sensitive to the choice of the substrates, i.e., to the epitaxial strain and interface properties. Here, we report the results of our computational work on the half-Heusler compound CrMnSb (1–x) P x . In particular, we demonstrate that the parent compound CrMnSb is close to a half-metallic material at the optimized lattice parameter, with the onset of the half-metallic bandgap a few meV above the Fermi energy. Moreover, although it undergoes a half-metallic transition under a uniform compression of ~1.5%, such a transition is absent under epitaxial strain. At the same time, we show that a half-metallic transition could be induced by a chemical substitution of Sb with P, which results in a volume reduction of the unit cell. In particular, 50% substitution of Sb with P leads to a robust half-metallicity in CrMnSb (1–x) P x , with 100% spin polarization being retained at a large range of epitaxial strain. Furthermore, our results indicate that CrMnSb0.5P0.5 could be grown on different types of substrates, e.g., GaAs, without its electronic properties being detrimentally affected by biaxial strain. In addition, CrMnSb 0.5 P 0.5 exhibits a fully compensated ferrimagnetic alignment, which could be potentially useful in applications where stray magnetic fields are undesirable.
Structural, magnetic, and magnetocaloric properties of (Nd 0.7 Ce 0.3 )YFe 17
Structural, magnetic, and magnetocaloric properties of iron-deficient (Nd 1-x Ce x )YFe 17 alloys in the rhombohedral Th 2 Zn 17 –type crystal structure prepared by arc-melting and vacuum annealing have been investigated. Among the investigated alloys, (Nd 0.7 Ce 0.3 )YFe 17 shows the highest values of magnetic entropy change and relative cooling power, namely 5.45 J kg -1 K -1 and 504 J kg -1 for a magnetic field change of 5 T. The Curie temperature and saturation magnetization of the (Nd 0.7 Ce 0.3 )YFe 17 alloy are 301 K and 162 emu/g, respectively. The absence of thermal and magnetic hysteresis with relatively high cooling capacity near room temperature suggests that Fe-deficient (Nd 0.7 Ce 0.3 )YFe 17 carries significant potential for room-temperature magnetic refrigeration.