Revealing in-plane movement of platinum in polymer electrolyte fuel cells after heavy-duty vehicle lifetime
Fuel cell heavy-duty vehicles (HDVs) require increased durability of oxygen-reduction-reaction electrocatalysts, making knowledge of realistic degradation mechanisms critical. Here identical-location micro-X-ray fluorescence spectroscopy was performed on membrane electrode assemblies. The results exposed heavy in-plane movement of electrocatalyst after HDV lifetime, suggesting that electrochemical Ostwald ripening may not be a local effect. Development of local loading hotspots and preferential movement of electrocatalyst away from cathode catalyst layer cracks was observed. The heterogeneous degradation exhibited by a modified cathode gas diffusion layer membrane electrode assembly after HDV lifetime was successfully quantified by the identical-location approach. Further synchrotron micro-X-ray diffraction and micro-X-ray fluorescence experiments were performed to obtain the currently unknown correlation between electrocatalyst nanoparticle size increase and loading change. A direct correlation was discovered which developed only after HDV lifetime. Finally, the work provides a route to engineer immediate system-level mitigation strategies and to develop structured cathode catalyst layers with durable electrocatalysts.
37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
Effect of Commercial Gas Diffusion Layers on Catalyst Durability of Polymer Electrolyte Fuel Cells in Varied Cathode Gas Environment
Gas diffusion layers (GDLs) play a crucial role in heat transfer and water management of cathode catalyst layers in polymer electrolyte fuel cells (PEFCs). Thermal and water gradients can accelerate electrocatalyst degradation and therefore the selection of GDLs can have a major influence on PEFC durability. Currently, the role of GDLs in electrocatalyst degradation is poorly studied. Here, we perform electrocatalyst accelerated stress test studies on membrane electrode assemblies (MEAs) prepared using three most commonly used GDLs. The effect of GDLs on electrocatalyst degradation is evaluated in both nitrogen (non-reactive) and air (reactive) gas environments at 100% relative humidity. In situ electrochemical characterization and extensive physical characterization is performed to understand the subtle differences in electrocatalyst degradation and correlated to the use of different GDLs. Overall, no difference is observed in the electrocatalyst degradation due to GDLs based on polarization curves at the end of life. But interestingly, MEA with a cracked microporous layer (MPL) in the GDL exhibited a higher electrocatalyst loading loss, which resulted in a lower and more heterogeneous increase in the average electrocatalyst nanoparticle size.
25 ENERGY STORAGE↗
Correlating the Morphological Changes to Electrochemical Performance During Carbon Corrosion in Polymer Electrolyte Fuel Cells
A mechanistic understanding of carbon corrosion in polymer electrolyte fuel cells (PEFCs) is required to design durable catalyst layers. Uncontrolled startup and shutdown of PEFCs cause electrochemical oxidation of carbon, which leads to several degradation phenomena, such as loss in electrochemical surface area (ECSA), pore structure collapse or increase in mass transport resistance. In this study, the chronology of morphological changes in the cathode catalyst layer due to carbon corrosion was identified and correlated with electrochemical performance degradation. PEFCs were subjected to the Department of Energy carbon corrosion accelerated stress test (AST) protocol. The study revealed two phases: in the initial phase (~500 AST cycles), amorphous carbon in contact with Pt nanoparticles oxidized fast. Rapid carbon loss and catalyst layer thinning occurred, but pore structure did not change significantly. Pt nanoparticles detached from the support and ECSA decreased drastically. In the second phase (~1500 AST cycles), carbon corrosion slowed down, but severe pore structure collapse was observed. Porosity and pore connectivity within the cathode catalyst layer decreased considerably. Electrochemical diagnostics corroborated this finding by showing significantly higher O2 mass transport resistance. Lastly, no significant change was observed in the concentration of oxides on the carbon surface after AST. But overall water management in the cathode catalyst layer deteriorated as the pore structure collapsed. This study provides an in-depth understanding of morphological changes during PEFC carbon corrosion AST protocol and motivates novel material design strategies to enable durable PEFCs.
catalyst layers↗
Carbon Corrosion in Polymer Electrolyte Fuel Cells: A Complex Interplay between Morphological Changes and Electrochemical Performance
Due to the high gravimetric energy density of hydrogen, the focus of implementation of polymer electrolyte fuel cells (PEFCs) has shifted from light duty passenger vehicles to heavy duty vehicles such as buses, trucks, locomotives and marine vessels. A mechanistic understanding of degradation is therefore necessary to improve durability and efficiency. During start-up and shut-down (SUSD) of PEFC systems, the catalyst (Pt nanoparticles embedded on carbon support) undergoes local potentials ~ 1 - 1.5 V caused by a combination of fuel (H 2 ) starvation, mixed fuel region and cell reversal. This leads to a series of degradation phenomenon including reduction in cathode catalyst layer (cCL) thickness and porosity, loss in electrochemical surface area (ECSA), ionomer degradation and loss in electrical contact, therefore resulting in severe performance loss. The convoluted relationship between these individual degradation mechanisms, their chronology and their effects on electrochemical performance are yet unresolved. Here, the complex interplay between morphological changes due to carbon corrosion and its effects on the electrochemical performance were analyzed using a combination of detailed electrochemical characterization, spectroscopy, and electron microscopy techniques.
25 ENERGY STORAGE↗
Probing Heterogeneous Degradation of Catalyst in PEM Fuel Cells under Realistic Automotive Conditions with Multi-Modal Techniques
The heterogeneity of polymer electrolyte fuel cell catalyst degradation is studied under varied relative humidity and types of feed gas. Accelerated stress tests (ASTs) are performed on four membrane electrode assemblies (MEAs) under wet and dry conditions in an air or nitrogen environment for 30 000 square voltage cycles. The largest electrochemically active area loss is observed for MEA under wet conditions in a nitrogen gas environment AST due to constant upper potential limit of 0.95 V and significant water content. The mean Pt particle size is larger for the ASTs under wet conditions compared to dry conditions, and the Pt particle size under land is generally larger than under the channel. Observations from ASTs in both conditions and gas environments indicate that water content promotes Pt particle size growth. ASTs under wet conditions and an air environment show the largest difference in Pt particle size growth for inlet versus outlet and channel versus land, which can be attributed to larger water content at outlet and under land compared to inlet and under channel. From X-ray fluorescence experiments Pt particle size increase is a local phenomenon as Pt loading remains relatively uniform across the MEA.
25 ENERGY STORAGE↗