Engineering topics

Kim, Daekun

Publications and source records attributed to Kim, Daekun.

10 records

DOE OSTI2024

Zeolite-promoted platinum catalyst for efficient reduction of nitrogen oxides with hydrogen

Internal combustion engine fueled by carbon-free hydrogen (H 2 -ICE) offers a promising alternative for sustainable transportation. Herein, we report a facile and universal strategy through the physical mixing of Pt catalyst with zeolites to significantly improve the catalytic performance in the selective catalytic reduction of nitrogen oxides (NO x ) with H 2 (H 2 -SCR), a process aiming at NO x removal from H 2 -ICE. Via the physical mixing of Pt/TiO 2 with Y zeolite (Pt/TiO 2 + Y), a remarkable enhancement of NO x reduction activity and N 2 selectivity was simultaneously achieved. The incorporation of Y zeolite effectively captured the in-situ generated water, fostering a water-rich environment surrounding the Pt active sites. This environment weakened the NO adsorption while concurrently promoting the H 2 activation, leading to the strikingly elevated H 2 -SCR activity and N 2 selectivity on Pt/TiO 2 + Y catalyst. This study provides a unique, easy and sustainable physical mixing approach to achieve proficient heterogeneous catalysis for environmental applications.

36 MATERIALS SCIENCE↗

DOE OSTI2024

Enhancing the Carbon Monoxide Oxidation Performance through Surface Defect Enrichment of Ceria-Based Supports for Platinum Catalyst

Effective synthesis and application of single-atom catalysts on supports lacking enough defects remain a significant challenge in environmental catalysis. Herein, we present a universal defect-enrichment strategy to increase the surface defects of CeO 2 -based supports through H 2 reduction pretreatment. The Pt catalysts supported by defective CeO 2 -based supports, including CeO 2 , CeZrO x , and CeO 2 /Al 2 O 3 (CA), exhibit much higher Pt dispersion and CO oxidation activity upon reduction activation compared to their counterpart catalysts without defect enrichment. Specifically, Pt is present as embedded single atoms on the CA support with enriched surface defects (CA-HD) based on which the highly active catalyst showing embedded Pt clusters (Pt C ) with the bottom layer of Pt atoms substituting the Ce cations in the CeO 2 surface lattice can be obtained through reduction activation. Embedded PtC can better facilitate CO adsorption and promote O 2 activation at Pt C –CeO 2 interfaces, thereby contributing to the superior low-temperature CO oxidation activity of the Pt/CA-HD catalyst after activation.

36 MATERIALS SCIENCE↗

DOE OSTI2024

Highly efficient La/Ni co-doped strontium titanate catalyst for co-production of propylene and hydrogen from propane in protonic ceramic electrochemical cells

A highly efficient La/Ni co-doped strontium titanate (LSNT) perovskite catalyst is developed and integrated in a protonic ceramic electrochemical cell for co-production of propylene and high-purity hydrogen from commercial propane feedstock. Propane conversion and hydrogen production rate can be effectively enhanced under an applied current due to the electrochemical promotion effect and/or shifted reaction equilibrium induced by rapid separation of hydrogen product. Water vapor in the feed gas could significantly improve the catalyst stability by suppressing the coke formation. The propane conversion could reach up to 53% at 600 °C under a current density of 90 mA cm −2 . The LSNT catalyst also shows excellent tolerance for the sulfur contaminant in commercial propane gas. Finally, the excellent performance of the LSNT catalyst is attributed to the highly active and selective Ni species at the interface with the perovskite substrate, which are formed in situ via reduction-induced exsolution under reaction conditions.

interfacial active sites↗

DOE OSTI2024

Ru/MgO catalyst with dual Ru structure sites for efficient CO production from CO 2 hydrogenation

The development and comprehension of supported metal catalysts for CO 2 hydrogenation is of paramount importance in mitigating the net CO 2 emissions. Supported Ru catalysts have been widely recognized in facilitating CO 2 methanation, on which recent findings suggest that the CO 2 hydrogenation process can be manipulated to favor the reverse water–gas shift (RWGS) pathway by precisely adjusting the size of Ru particles. However, the size-dependent impact of Ru remains a topic of lively debate. In this work, Ru/MgO catalysts with Ru in the form of single atoms (Ru 1 ) and few-atom cluster (Ru FAC ) structures were prepared for CO 2 hydrogenation. The 1.0Ru/MgO catalyst (with 1 wt.% of Ru), featuring a mixture of Ru 1 and Ru FAC with a size of 0.6–1.0 nm, showed the highest CO yield (38% at 500 °C) with balanced CO 2 conversion and CO selectivity. Transient CO 2 hydrogenation and temperature-programmed surface reaction (TPSR) studies suggested that the adsorbed CO 2 species participated in CO 2 hydrogenation. On Ru 1 sites, CO 2 hydrogenation followed the RWGS pathway, resulting in the production of CO. In contrast, on Ru FAC sites, the enhanced H 2 dissociation ability, along with the presence of adsorbed bidentate and monodentate carbonate species at the Ru-MgO interfaces, facilitated the formation of CH 4 through the CO 2 methanation pathway. In conclusion, this study highlights the critical roles of Ru structure and local environment in defining the CO 2 hydrogenation pathways and provides new design principles for highly active Ru-based catalysts.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2023

Fine-Tuning of Pt Dispersion on Al 2 O 3 and Understanding the Nature of Active Pt Sites for Efficient CO and NH 3 Oxidation Reactions

Fine-tuning the dispersion of active metal species on widely used supports is a research hotspot in the catalysis community, which is vital for achieving a balance between the atomic utilization efficiency and the intrinsic activity of active sites. In this work, using bayerite Al(OH) 3 as support directly or after precalcination at 200 or 550 °C, Pt/Al 2 O 3 catalysts with distinct Pt dispersions from single atoms to clusters (ca. 2 nm) were prepared and evaluated for CO and NH 3 removal. Richer surface hydroxyl groups on AlO x (OH) y support were proved to better facilitate the dispersion of Pt. However, Pt/Al 2 O 3 with relatively lower Pt dispersion could exhibit better activity in CO/NH 3 oxidation reactions. Further reaction mechanism study revealed that the Pt sites on Pt/Al 2 O 3 with lower Pt dispersion could be activated to Pt 0 species much easier under the CO oxidation condition, on which a higher CO adsorption capacity and more efficient O 2 activation were achieved simultaneously. Compared to Pt single atoms, PtO x clusters could also better activate NH 3 into –NH 2 and –HNO species. The higher CO adsorption capacity and the more efficient NH 3 /O 2 activation ability on Pt/Al 2 O 3 with relatively lower Pt dispersion well explained its higher CO/NH 3 oxidation activity. This study emphasizes the importance of avoiding a singular pursuit of single-atom catalyst synthesis and instead focusing on achieving the most effective Pt species on Al 2 O 3 support for targeted reactions. Finally, this approach avoids unnecessary limitations and enables a more practical and efficient strategy for Pt catalyst fabrication in emission control applications.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2023

Hydroxyls on CeO 2 Support Promoting CuO/CeO 2 Catalyst for Efficient CO Oxidation and NO Reduction by CO

Transition metal catalysts, such as copper oxide, are more attractive alternatives to noble metal catalysts for emission control due to their higher abundance, lower cost, and excellent catalytic activity. Here, in this study, we report the preparation and application of a novel CuO/CeO 2 catalyst using a hydroxyl-rich Ce(OH) x support for CO oxidation and NO reduction by CO. Compared to the catalyst prepared from a regular CeO 2 support, the new CuO/CeO 2 catalyst prepared from the OH-rich Ce(OH) x (CuO/CeO 2 –OH) showed significantly higher catalytic activity under different testing conditions. The effect of OH species in the CeO 2 support on the catalytic performance and physicochemical properties of the CuO/CeO 2 catalyst was characterized in detail. It is demonstrated that the abundant OH species enhanced the CuO x dispersion on CeO 2 , increased the CuO x –CeO 2 interfaces and surface defects, promoted the oxygen activation and mobility, and boosted the NO adsorption and dissociation on CuO/CeO 2 –OH, thus contributing to its superior catalytic activity for both CO oxidation and NO reduction by CO. These results suggest that the OH-rich Ce(OH) x is a superior support for the preparation of highly efficient metal catalysts for different applications.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2023

Impact of Oxygen Storage Components in Prototype Pd-Based Three-Way Catalysts under Exhaust Conditions Relevant to Propane Engines

With increasing concerns about global warming, the push for sustainable and eco-friendly fuels is accelerating. Propane, recognized as liquefied petroleum gas or LPG, has garnered research interest as an alternative fuel due to its notable advantages, including a high-octane rating, reduced greenhouse gas emissions, and potential cost-effectiveness. However, to realize its full potential as an alternative fuel it is essential to develop catalysts that efficiently handle emissions at low temperatures. In our research, we investigated three distinct palladium (Pd)-based three-way catalyst (TWC) formulations (PdRh, Pd-only, and Pd-OSC) to investigate the influence of typical TWC components rhodium (Rh) and oxygen storage components (OSC) in exhaust scenarios relevant to propane-fueled engines. Among these, the formulation containing oxygen storage components (Pd-OSC) showed the highest reactivity for both NO and C 3 H 8 while minimizing performance degradation from hydrothermal aging (HTA). Notably, the temperature of 50% conversion (T50) for propane in the Pd-OSC fresh and HTA sample was lower by 30 °C and 13 °C, respectively, compared to the Pd-only sample, highlighting the role of oxygen storage materials in enhancing catalyst performance, even without dithering. Additionally, N 2 physisorption showed that the PdOSC sample has a higher surface area and increased pore volume. This underscores the idea that OSC materials not only augment the catalyst’s porosity but also optimize reactant accessibility to active sites, thus elevating catalytic efficiency. In addition to evaluating performance, we further explored the performance and characteristics of the catalysts using catalytic probe reactions, such as water–gas shift and steam reforming reactions.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2023

Silica modulated palladium catalyst with superior activity for the selective catalytic reduction of nitrogen oxides with hydrogen

A significant promotion effect of colloidal SiO 2 on Pd/TiO 2 catalyst for improving the activity and N 2 selectivity in the selective catalytic reduction of NO with H 2 (H 2 -SCR) was reported, both before and after hydrothermal aging. The SiO 2 addition not only benefited the formation of more oxygen vacancies but also increased Pd dispersion and created rich Pd-SiO 2 interfaces on Pd-SiO 2 /TiO 2 catalyst. The H 2 -SCR of NO on both Pd/TiO 2 and Pd-SiO 2 /TiO 2 followed a Langmuir-Hinshelwood mechanism, in which the adsorbed bridging bidentate nitrates on TiO 2 could react with dissociated H 2 species on Pd sites at Pd-TiO 2 interface. Particularly, on the promoted Pd-SiO 2 /TiO 2 , the Pd-TiO 2 interface could facilitate NO adsorption and activation, and the created Pd-SiO 2 interface could benefit H 2 adsorption and dissociation, thus contributing to its significantly improved H 2 -SCR activity. Additionally, the active Pd species (which should be Pd0 under reaction condition with higher surface concentration) within Pd-SiO 2 /TiO 2 could be well stabilized during long-term hydrothermal aging process through the formation of rich Pd-SiO 2 interfaces.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Impact of Boron-Containing Lubricant Additive on Three-Way Catalyst Reactivity and Physicochemical Properties

Boron-containing compounds are one of the lubricant additive options due to their suitable properties for additives and have been used as commercial lubricant additives. In the present study, the impact of a boron-containing lubricant oil additive, AR9100 (BR), on Pd/Rh-based three-way catalyst (TWC) performance is investigated, and the results are compared with the baseline no-additive (NA) case and the industry standard zinc dialkyl-dithiophosphate (ZDDP) results. Accelerated engine aging is performed using a genset to expose the catalysts to lubricant additives at high temperatures. All aged TWC samples are investigated for reactivity in a bench-flow reactor and characterized using a variety of analytical techniques. Compared with the no-additive case, the temperatures of 90% conversion (T 90 ) of NO, CO, C 3 H 6 , and C 3 H 8 for the ZDDP-aged TWC sample increased by 34, 30, 37, and 48 °C. However, the T 90 of all gas species for the BR-aged TWC sample are similar to the NA-aged TWC sample. Additionally, a significant decrease in water–gas shift reactivity and oxygen storage capacity is observed in the ZDDP-aged sample, but not in the BR-aged sample. Inductively coupled plasma-optical emission spectrometry (ICP-OES) analysis and electron probe microanalysis (EPMA) maps of accelerated engine aging samples show the presence of phosphorus and boron in ZDDP- and BR-aged TWC samples, respectively. However, no boron-related peaks are observed in the X-ray diffraction (XRD) pattern of the BR-aged TWC sample, which may exist in the form of an amorphous phase.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2021

Impact of Primary and Secondary ZDDP and Ionic Liquid as Lubricant Oil Additives on the Performance and Physicochemical Properties of Pd-Based Three-Way Catalysts

In the present study, two industry primary and secondary zinc dialkyldithiophosphate standards, ZDDP1 and ZDDP2, respectively, are evaluated for their impact on the performance of Pd-based three-way catalyst and bench-marked against two mixed lubricant additives formed from either ZDDP1 or ZDDP2 with a second-generation oil-miscible phosphoric-containing ionic liquid (IL). The three-way catalysts (TWCs) are exposed to the lubricant additives in an engine bench under four different scenarios: a base case with no additive (NA), ZDDP1, IL+ZDDP1, ZDDP2, and IL+ZDDP2. The engine-aged TWC samples are characterized through a variety of analytical techniques, including evaluation of catalyst reactivity in a bench-flow reactor. With respect to the water–gas shift reaction and the oxygen storage capacity, the ZDDP2- and IL+ZDDP2-aged TWC samples are more degraded than the ZDDP1- and IL+ZDDP1-aged TWC samples. X-ray diffraction (XRD) patterns indicate that phosphorus in the form of CePO4 was found to be present in the washcoat of all TWC samples, with the highest amount found in the ZDDP2-aged TWC sample. The results obtained from XRD are further confirmed by those from inductively coupled plasma-optical emission spectroscopy (ICP-OES), which show that more phosphorus is detected in the washcoat of ZDDP2- and IL+ZDDP2-aged TWC samples than in the ZDDP1- and IL+ZDDP1-aged TWC samples.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗