Deciphering oxygen-induced surface segregation of Pt3V alloy using ambient pressure XPS
Explore the source record for details and available documents.
36 MATERIALS SCIENCE↗
Engineering topics
Kim, Dongwoo
Publications and source records attributed to Kim, Dongwoo.
Shapeshifting Nanocatalyst for CO2 Conversion
The conversion of CO2 into high-value chemicals through a photoreduction reaction in water is a promising route to reduce the dependence on fossil fuels. Enhancing selectivity toward hydrocarbons or alcohols can be achieved by Ag-Cu alloys. However, the stabilized surface state created by Ag-Cu interactions is still poorly understood. In this work, multi-modal in situ X-ray experiments reveals underlying mechanisms and the evolution of Ag-Cu nanoparticles under CO2 reduction reaction (CO2RR) conditions. Both morphological and chemical changes of Ag and Cu species induced by diffusion mechanics are tracked during nanocatalyst operation. The initial spheroid Ag-Cu nanoparticles are composed of a Cu-rich shell and Ag-rich core. The reduction treatment promotes Ag migration toward the surface. During photocatalytic CO2 reduction reaction, Cu atoms migrate back to the surface, forming Ag-Cu-O species. The study observes the surface oxidation of Cu(0) to Cu+ and the presence of Ag at the sub-surface region. Furthermore, nanoparticles change their shape, decreasing their specific surface area, driven by Cu diffusion during the CO2 photoreduction reaction. The results provide invaluable insights into the dynamic restructuring of the catalyst under reaction conditions and into the active species responsible for CO2 conversion.
CO2 reduction reaction↗
Study of CO 2 Adsorption Properties on the SrTiO 3 (001) Surface with Ambient Pressure XPS
The adsorption properties of CO 2 on the SrTiO 3 (001) surface were investigated using ambient pressure X-ray photoelectron spectroscopy under elevated pressure and temperature conditions. On the Nb-doped TiO 2 -enriched (1 × 1) SrTiO 3 surface, CO 2 adsorption, i.e., the formation of CO 3 surface species, occurs first at the oxygen lattice site under 10 –6 mbar CO 2 at room temperature. The interaction of CO 2 molecules with oxygen vacancies begins when the CO 2 pressure increases to 0.25 mbar. The adsorbed CO 3 species on the Nb-doped SrTiO 3 surface increases continuously as the pressure increases but starts to leave the surface as the surface temperature increases, which occurs at approximately 373 K on the defect-free surface. On the undoped TiO 2 -enriched (1 × 1) SrTiO 3 surface, CO 2 adsorption also occurs first at the lattice oxygen sites. Both the doped and undoped SrTiO 3 surfaces exhibit an enhancement of the CO 3 species with the presence of oxygen vacancies, thus indicating the important role of oxygen vacancies in CO 2 dissociation. When OH species are removed from the undoped SrTiO 3 surface, the CO 3 species begin to form under 10 –6 mbar at 573 K, thus indicating the critical role of OH in preventing CO 2 adsorption. The observed CO 2 adsorption properties of the various SrTiO 3 surfaces provide valuable information for designing SrTiO 3 -based CO 2 catalysts.
36 MATERIALS SCIENCE↗
MgO Nanostructures on Cu(111): Understanding Size- and Morphology-Dependent CO 2 Binding and Hydrogenation
To design and optimize cost-effective technologies for the capture, utilization, and storage of carbon dioxide (CO 2 ), we need a fundamental knowledge and control of chemical interactions associated with the capture and conversion of the molecule into high-value chemicals, minerals, and all kinds of materials. Bulk magnesium oxide (MgO) is frequently used for the trapping and storage of CO 2 by generation of magnesium carbonates. In this study, the growth and reactivity of MgO nanostructures on a Cu 2 O/Cu(111) substrate were investigated using scanning tunneling microscopy (STM) and synchrotron-based ambient-pressure X-ray photoelectron spectroscopy (AP-XPS). For extremely small concentrations of Mg (~ 0.01 monolayer (ML)), a well-ordered film of copper oxide with small clusters (0.2-0.5 nm in width, 0.4-0.6 Å in height) of embedded MgO was seen. At a coverage of 0.1 ML, MgO nanoparticles with a width of 0.4 to 1 nm and a height of ~ 1.5 Å were randomly distributed on the copper oxide. Further, random distribution was also observed when the MgO coverage was raised to 0.25 ML, with the width of the MgO particles increasing to 2-2.5 nm and the height reaching 2 Å. These oxide nanostructures displayed a high reactivity towards CO 2 and H 2 that is not seen for bulk MgO. Dissociation of H 2 was observed at room temperature with reaction of the H adatoms with CuO x and C-containing groups. On the small MgO nanostructures (< 1 nm in width), instead of plain carbonate formation, there was dissociation of CO 2 into CO and C species, opening reaction channels for the conversion of this harmful molecule into oxygenates and light alkanes.
03 NATURAL GAS↗