DOE OSTI2024

Strength-ductility synergy through microstructural and compositional heterogeneity in directed energy deposition additive manufacturing of face-centered cubic materials

Directed energy deposition (DED) is an additive manufacturing (AM) process based on welding technology and offers the advantages of large build volume, high deposition rate, and ability to fabricate multi-material parts. Epitaxial continuous columnar grain growth is a characteristic microstructural feature of DED processed alloys. In this study, a bamboo-like microstructure (periodic alternation of equiaxed and columnar structure) was produced by adopting an intermittent deposition strategy in 316L stainless steel and Inconel 625. The formation of a bamboo-like alternating microstructure was confirmed through electron backscattered diffraction (EBSD) analysis. Hardness mapping showed that the columnar to equiaxed transition (CET) occurred at the region right below the fusion line. A finite element (FE) model was used to investigate the relationship between the temperature gradient (G) and the solidification rate (R). The FE model showed a low G/R ratio at the region right below the interface promoting the CET. The grain size and material-dependent deformation behaviors are analyzed using digital image correlation (DIC). The lower deformation on the fine-grain regions observed in DIC analysis is attributed to a higher strain hardening rate, which is confirmed through dislocation density analysis on a tensile-interrupted specimen. The periodically alternating grain size coupled with the microstructural changes caused by intermittent deposition strategy result in a better strength-ductility synergy in both single-material and bimetallic specimens.

36 MATERIALS SCIENCE↗

DOE OSTI2024

Investigating stainless steel/aluminum bimetallic structures fabricated by cold metal transfer (CMT)-based wire-arc directed energy deposition

Here, this study investigated the process of fabricating a bimetallic structure of 316L stainless steel (SS) and 4043 aluminum (Al) using wire-arc directed energy deposition (DED) based on the cold metal transfer (CMT) process. The impact of heat input on the fabricated structure’s geometry, porosity, and microstructures at the interface, with a specific emphasis on the intermetallic compound (IMC) formation, and the subsequent impact on the joint strength of the structure, were studied. The IMC layer at the interface was predominantly comprised of FeAl 2 Si. For the various heat input conditions studied, the IMC layer's thickness varied from 5 µm to 18 µm. The tensile strength reached up to approximately 130 MPa, which is among the highest reported in the literature for steel/Al bimetallic structures. The specimens fabricated with high heat input conditions had a thicker IMC layer at the steel/Al interface, resulting in a more brittle interface and degradation of the mechanical properties.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Phase stability and mechanical properties of wire + arc additively manufactured H13 tool steel at elevated temperatures

Wire + arc additive manufacturing (WAAM) is considered an innovative technology that can change the manufacturing landscape in the near future. WAAM offers the benefits of inexpensive initial system setup and a high deposition rate for fabricating medium- and large-sized parts such as die-casting tools. Here, AISI H13 tool steel, a popular die-casting tool metal, is manufactured by cold metal transfer (CMT)-based WAAM and is then comprehensively analyzed for its microstructural and mechanical properties. Location-dependent phase combinations are observed, which could be explained by nonequilibrium thermal cycles that resulted from the layer-by-layer stacking mechanism used in WAAM. In addition, remelting and reheating of the layers reduces welding anomalies (e.g., pores and voids). The metallurgical characteristics of the H13 strongly correlate with the mechanical properties. The combinations of phases at different locations of the additively manufactured part exhibit a periodic microhardness profile. Martensite, Retained Austenite, Ferrite, and Carbide phases are found in combination at different locations of the part based on the part’s temperature distribution during additive deposition. Moreover, the tensile properties at elevated temperatures (23 °C, 300 °C, and 600 °C) are comparable to those from other WAAM and additive manufacturing (AM) processes. The X-ray diffraction results verify that the microstructural stability of the fabricated parts at high temperatures would allow them to be used in high temperatures.

36 MATERIALS SCIENCE↗