High-current, high-voltage AlN Schottky barrier diodes

AlN Schottky barrier diodes with low ideality factor (<1.2), low differential ON-resistance (<0.6 mΩ cm 2 ), high current density (>5 kA cm −2 ), and high breakdown voltage (680 V) are reported. The device structure consisted of a two-layer, quasi-vertical design with a lightly doped AlN drift layer and a highly doped Al 0.75 Ga 0.25 N ohmic contact layer grown on AlN substrates. A combination of simulation, current–voltage measurements, and impedance spectroscopy analysis revealed that the AlN/AlGaN interface introduces a parasitic electron barrier due to the conduction band offset between the two materials. This barrier was found to limit the forward current in fabricated diodes. Further, we show that introducing a compositionally-graded layer between the AlN and the AlGaN reduces the interfacial barrier and increases the forward current density of fabricated diodes by a factor of 10 4 .

Quiñones, C. E. (ORCID:0000000192703747)↗

DOE OSTI2020

Control of passivation and compensation in Mg-doped GaN by defect quasi Fermi level control

A defect quasi Fermi level (dQFL) control process based on above bandgap illumination was applied to control H and V N -complexes, which are the main contributors to the passivation and self-compensation, respectively, in Mg:GaN grown via metalorganic chemical vapor deposition. Secondary ion mass spectrometry measurements confirmed that the total Mg incorporation was unaffected by the process. However, the total H concentration was reduced to similar levels obtained by post-growth thermal activation prior to any annealing treatment. Similarly, the 2.8 eV emission in the photoluminescence spectra, attributed to compensating V N and its complexes, was reduced for the dQFL-process samples. After thermal activation and Ni/Au contact deposition, Hall effect measurements revealed lower resistivities (increased mobilities and free hole concentrations) for dQFL-grown samples with Mg doping concentrations above and below 2 × 10 19 cm -3 . All these results demonstrate that the dQFL process can effectively reduce the H-passivation and self-compensation of the Mg:GaN films.

36 MATERIALS SCIENCE↗