NASA NTRS1985

Development of an impact- and solvent-resistant thermoplastic composite matrix, phase 3

The polyimide from BTDA 1,6-hexanediamine and m-phenylenediamine was selected from a prior study for the present study. Methods to prepare prepreg which would provide low void composites at low molding pressures from the thermoplastic polyimide were studied. Cresol solutions of the polyimide were applied to a balanced weave carbon fabric and the cresol removed prior to composite molding. Low void composites were prepared from smoothed prepregs at high pressures (34.5 MPa) and temperatures as low as 260 C. Lower molding pressures lead to higher void composites. Need for a lower melt viscosity in the neat resin is suggested as a requirement to achieve low void composites at low pressures. Some mechanical properties are included.

Delano, C. B.↗

NASA NTRS1984

Aliphatic-Aromatic Heterocyclics as Potential Thermoplastics for Composite Matrices

The successful development of impact- and solvent-resistant thermoplastic systems for glass graphite composites is particularly attractive because of the demonstrated streamlined manufacturability of such composites. Hypothetically, thermoplastics only require simple heating and cooling cycles for component manufacture, whereas thermosets require precise, and possibly extended heating schedules which must be consistent with the cure chemistry. The sensitivity of the majority of existing thermoplastics to aircraft fluids and other solvents preempts their serious consideration in aircraft components. This is the basic reason that Acurex proposed insolubility in common solvents as the starting point. The target properties are summarized as follows: (1) prepreg properties (use of conventional prepregging equipment, 6+ months shelf stability, processability, and thermoformability); and (2) composite properties (-54 C to 93 C capability, good mechanical properties, good environmental properties, and impact resistance).

Delano, C. B.↗

NASA NTRS1984

Development of an impact- and solvent-resistant thermoplastic composite matrix

Synthesis, moldability and chloroform, acetone and tricresyl phosphate resistance of 16 polymer compositions are described. These aliphatic heterocyclic polymers include polyimides, polybenzimidazoles, and N-arylenepolybenzimidazoles. A solution condensation (cresol) method to prepare imidized aliphaic polyimides is described. Two polyimides and one polybenzimidazole demonstrate no crazing or cracking during 500 hr exposure to the cited solvents under stress. Modification of one aliphatic polyimide with several aromatic amines suggests that m-phenylenediamine is singular in its behavior to improve the chloroform resistance of that class of polyimides.

Delano, C. B.↗