Epitaxial registry and transport properties in V4O7 thin films

We report the growth of V4O7 thin films deposited simultaneously on amorphous SiO2 and crystalline c-cut Al2O3 substrates. x-ray diffraction shows that films grown on SiO2 are polycrystalline with no preferred orientation, while films grown on Al2O3 exhibit a well-defined out-of-plane orientation and an in-plane registry consistent with epitaxial growth. Transmission electron microscopy confirms the crystallographic relationship between the V4O7 film and the Al2O3 substrate. Atomic force microscopy indicates substantially lower surface roughness for films grown on Al2O3 (~6 nm) compared to those grown on SiO2 (~22 nm), and Raman spectroscopy confirms stabilization of the same V4O7 phase on both substrates. Electrical transport measurements reveal a metal–insulator transition near 244 K for both substrates, with thermal hysteresis not exceeding ~1 K. Although the transition temperature remains essentially unchanged, films grown on Al2O3 exhibit higher conductivity over the entire temperature range, exceeding that of films grown on SiO2 by approximately two orders of magnitude at 100 K and by a factor of five at 300 K. These results indicate that the conductivity differences are consistent with variations in microstructural connectivity associated with crystallographic order.

36 MATERIALS SCIENCE↗

Crystallographic registry in epitaxial V3O5 thin films

Crystallographic orientation plays a central role in determining transport properties in correlated oxides with low-hysteresis metal–insulator transitions. Here, V3O5 thin films were grown on Al2O3 (0001) and their crystallographic registry was evaluated using x-ray diffraction and cross-sectional transmission electron microscopy. θ–2θ measurements show a single out-of-plane orientation defined by the (202) reflection. Azimuthal φ-scans of the V3O5 (310) reflection exhibit twelve discrete maxima over 360°, indicating a finite set of in-plane orientations imposed by the substrate symmetry. High-resolution TEM and fast Fourier transform analysis confirm crystallographic coherence at the film–substrate interface. The electrical conductivity exhibits a metal–insulator transition at TMIT ≈ 423 K with no measurable thermal hysteresis and a total change of ~1.6 orders of magnitude between 300 and 480 K. These results establish crystallographic registry in epitaxial V3O5 thin films and provide a structurally well-defined system for future studies of orientation-dependent transport.\r\nT

36 MATERIALS SCIENCE↗

Kinetic control of phase evolution and defect-mediated recombination in AACVD-grown copper antimony sulphide thin films

Copper antimony sulphide (CAS) is a multinary chalcogenide semiconductor in which small deviations from stoichiometry can drive phase competition and strong defect-mediated modulation of optoelectronic properties. However, the systematic roles of copper precursor fraction and deposition time in governing phase evolution, off-stoichiometry, and recombination dynamics in aerosol-assisted chemical vapour deposition (AACVD)-grown undoped CAS thin films remain insufficiently understood. In this work, undoped CAS thin films were deposited by AACVD using Cu(dedtc)2 and Sb(dedtc)3 single-source precursors at 550 °C and a carrier gas flow rate of 150 sccm, while the Cu(dedtc)2 mole fraction (x = 0.15 – 0.55) and deposition time (1 – 2 hours) were systematically varied to probe how growth kinetics influence phase composition, microstructure, and defect-mediated optical properties without post-deposition annealing or extrinsic doping. Increasing copper precursor content drives phase evolution toward tetrahedrite-dominant CAS films at intermediate Cu(dedtc)2 mole fractions, with the film deposited at x = 0.35 exhibiting the strongest tetrahedrite character within the parameter space examined. The films are also copper-rich, antimony-poor, and sulphur-deficient, consistent with off-stoichiometric growth and intrinsic defect formation, plausibly including copper interstitials, Cu-on-Sb antisites, and sulphur vacancies. These growth-dependent compositional deviations are accompanied by tunable indirect optical bandgaps of approximately 1.60 – 2.18 eV and weak visible photoluminescence governed by defect-mediated recombination. Time-resolved photoluminescence reveals bi-exponential decay behaviour with lifetimes of approximately 0.1 – 3.6 ns, with emission dominated by slower donor–acceptor pair recombination and a smaller contribution from faster trap-assisted pathways. Collectively, these results establish an explicit kinetic process–structure–defect–property relationship for AACVD-grown CAS thin films and provide a growth–structure–property framework relevant to future optimization of CAS-based optoelectronic and energy materials.