DOE OSTI2023

Achieving High Strength and Creep Resistance in Inconel 740H Superalloy through Wire-Arc Additive Manufacturing and Thermodynamic-Guided Heat Treatment

Inconel 740H superalloy is commonly used in advanced ultra-supercritical power plants since it possesses excellent strength and creep resistance. This study investigates the microstructure and mechanical properties of Inconel 740H superalloy fabricated using wire-arc additive manufacturing. The as-printed microstructure consisted of columnar γ grains with the Laves phase and (Nb, Ti)C carbides as secondary phases. The anisotropy in grain structure increased from the bottom to the top regions, while the hardness was highest in the middle portion of the build. To guide the post-heat treatment design, thermodynamic and kinetic simulations were employed to predict the temperature and time. Complete recrystallization with the Laves phase dissolution occurred throughout the build after homogenization at 1200 °C for 2 h. The peak hardness was achieved after aging at 760 °C for 12 h with the M 23 C 6 carbides decorating the grain boundaries and γ’ precipitates in the grain interior. The yield strength (655 MPa) and ductility (29.5%) in the post-heat treated condition exceeded the design targets (620 MPa, 20%). Stress rupture tests at 750 °C showed that the high-temperature performance was at par with the wrought counterparts. The fracture mode after rupture was identified to be intergranular with the presence of grain boundary cavities along with grain boundary sliding.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Determination of Location-Specific Solidification Cracking Susceptibility for a Mixed Dissimilar Alloy Processed by Wire-Arc Additive Manufacturing

Solidification cracking is a major obstacle when joining dissimilar alloys using additive manufacturing. In this work, location-specific solidification cracking susceptibility has been investigated using an integrated computational materials engineering (ICME) approach for a graded alloy formed by mixing P91 steel and Inconel 740H superalloy. An alloy mixture of 26 wt.% P91 and 74 wt.% Inconel 740H, with high configurational and total entropy, was fabricated using wire arc additive manufacturing. Microstructure characterization revealed intergranular solidification cracks in the FCC matrix, which increased in length along with the enrichment of Nb (~27 to 56 wt.%) and Cu (~87 wt.%) in the middle and top regions. DICTRA simulations to model location-specific solidification cracking susceptibility showed that the top region with the highest cooling rate (270 K/s) has the highest solidification cracking susceptibility in comparison with the middle and bottom regions. This is in good agreement with the experimentally observed varying crack length. From Scheil simulations, it was deduced that enrichment of Nb and Cu affected the solidification range as high as ~77%, in comparison with the matrix composition. The overall solidification cracking susceptibility and freezing range was highest for the 26 wt.% P91 alloy amongst the mixed compositions between P91 steel and 740H superalloy, proving that solidification characteristics play a major role in alloy design for additive manufacturing.

20 FOSSIL-FUELED POWER PLANTS↗
DOE OSTI2021

Interfacial characteristics of P91 steel - Inconel 740H bimetallic structure fabricated using wire-arc additive manufacturing

Although bimetallic structures can offer unique solutions to engineering problems with varying functionality, joining two dissimilar alloys using additive manufacturing involves challenges such as cracking and segregation. In this work, bimetallic structures of Inconel 740H superalloy and P91 steel are processed using wire-arc additive manufacturing (WAAM) for the first time. P91 steel is directly deposited over 740H with a cooling time of 20 minutes in between the two depositions. During microstructure characterization, a large gradient zone with coarse grains spanning for ~2200 μm is observed. Moreover, the microhardness of the gradient zone is the least in comparison with the P91 and 740H deposits. No deleterious phase formation is found; however, intergranular cracks are observed along the gradient zone. In order to deduce the reason for cracking, non-equilibrium solidification simulations are performed for the mixed compositions of P91 and 740H in the gradient zone. Here, the reasons for crack formation in the gradient zone are the sudden change in the volumetric coefficient of thermal expansion due to the formation of MC carbides as well as the development of local strains from the thermal residual stresses. Therefore, altering the deposition sequence and introducing gradient layers with mixed composition between the P91 and 740H deposits will be beneficial in achieving defect-free builds. Through the integration of experiments and simulation, this work gains valuable insights into the processability of dissimilar alloy manufacturing using the WAAM technique.

20 FOSSIL-FUELED POWER PLANTS↗
DOE OSTI2020

Residual Stress Modeling with Phase Transformation for Wire Arc Additive Manufacturing of B91 Steel

Wire arc additive manufacturing (WAAM) is an energy-efficient manufacturing technique used for near-net-shape production of functional industrial components. However, heat accumulation during deposition and the associated mechanical and metallurgical changes result in complex residual stress profiles across the cross section of the fabricated components. These residual stresses are detrimental to the service life of the components. In this study, sequentially coupled thermomechanical analysis of WAAM B91 steel is conducted to quantify the residual stress variation across the component. The thermomechanical analysis includes a transient heat transfer model and a static stress model that incorporates the transformation-induced plasticity due to martensitic phase transformation. Here, the experimentally calibrated heat transfer model mirrors the temperature variation of the system during the deposition. The results from the stress model are validated via x-ray diffraction measurements, and the numerical results are in good agreement with the experimental data.

20 FOSSIL-FUELED POWER PLANTS↗
DOE OSTI2020

A Discrete Dendrite Dynamics Model for Epitaxial Columnar Grain Growth in Metal Additive Manufacturing with Application to Inconel

Epitaxial columnar grain growth is a prevalent microstructural feature in the additive manufacturing (AM) of metal components such as Inconel, with cubic unit cell crystal lattice structure (face centered cubic (FCC) or body centered cubic (BCC)). These columnar grains evolve from the partly molten grains in the substrate or the solidified metal. This work proposes an efficient model to simulate the competitive growth of epitaxial columnar dendritic grains. The proposed model tracks the dynamic changes in the dendrites emanating from discrete points along the solid/liquid interface of a quasi-steady melt pool (MP). These dynamic changes include convergence and divergence of growing dendrites. The model is extended to predict the microstructure of large 3D parts and experimentally validated by comparing the simulation results for laser powder bed fusion (L-PBF) and wire-arc additive manufacturing (WAAM) processes. The microstructure and pole figures are predicted for Inconel 718 samples produced by L-PBF and Inconel 740H samples produced by WAAM processes. Finally, the model predictions compare well with the observed microstructure and pole figures results for both the L-PBF and WAAM processes.

20 FOSSIL-FUELED POWER PLANTS↗