Fabrication and testing of silver-hydrogen cells
The development and life testing of single electrode and multi electrode stacks to optimize the individual components and characterize the performance of a silver hydrogen battery system are described. A NASA-developed inorganic separator material was used as the main separator within the cells. Single electrode test cells were cycled at 75% of nominal capacity out through approximately 1,000 cycles in a number of cases where deterioration in performance was observed. This deterioration appears to be a decay in usable capacity of the silver electrode; but the exact mechanism is still unidentified. Twenty ampere-hour boilerplate test cells consisting of a stack of ten silver electrodes and twenty hydrogen electrodes were cycled also at 75% depth of discharge. The oldest stack achieved 522 stable cycles to the end of the program. Weight analysis of light-weight cells showed that 50 ampere-hour cells with improved components could be capable of as much as 40 watt hours per pound.