NASA NTRS1987

Pseudomorphic InGaAs/AlGaAs modulation-doped FET's with reduced low-frequency noise and thermally stable performance

A high-performance MODFET structure grown by MBE with the incorporation of a single quantum well In(0.15)Ga(0.85)As layer for the transport of two-dimensional electron gas has been critically examined for its thermal stability at 80 K and low-frequency noise form 0.01 to 10 to the 8th Hz. Experimental results indicate that the behavior of this device in both these respects is much superior when compared with the same behavior of conventional MODFETs. A maximum low-field carrier mobility of 29,000 sq cm/s at 80 K and an average carrier saturation velocity of 2 x 10 to the 7th cm/s at 300 K in a 1-micron gate device clearly indicate that the quality of the pseudomorphic quantum well (InGaAs) layer is either comparable or better than that of the usual GaAs buffer layer. The deep level spectra, obtained through photo-FET measurements, and the low-frequency noise spectra at different temperatures obtained for the new pseudomorphic and conventional MODFET's have clearly indicated that contributions from various deep levels present in the new structure are significantly reduced.

Liu, Shih-Ming↗

NASA NTRS1986

Dc and microwave characteristics of a high current double interface GaAs/InGaAs/AlGaAs pseudomorphic modulation-doped field-effect transistor

Extremely large current double interface GaAs/In(0.15)Ga(0.85)As/Al(0.15)Ga(0.85)As pseudomorphic modulation-doped field-effect transistors (MODFET's) grown by molecular beam epitaxy were achieved. The 1-micron gate devices studied have peak current levels (430 mA/mm at 300 K and 483mA/mm at 77 K) roughly one and a half to two times that found in single interface pseudomorphic MODFET's. These devices also retain high transconductances over a broad range of gate voltage, peaking at 312 mS/mm at 300 K and 362 mS/mm at 77 K. Excellent microwave performance is also obtained with a maximum frequency of oscillation (f-max) of 37 GHz and a current gain cut-off frequency of as high as 23 GHz at 300 K. An output power level of 14 dBm (1 dB gain compression) was obtained at 6 GHz for a 290-micron gate width. This double interface single quantum well MODFET may be of great importance in millimeter wave power amplifiers.

Henderson, T.↗

NASA NTRS1985

High transconductance InGaAs/AlGaAs pseudomorphic modulation-doped field-effect transistors

Pseudomorphic In0.15Ga0.85As/A10.15Ga0.85As modulation-doped field effect transistors (MODFET's) exhibiting extremely good dc characteristics have been successfully fabricated. dc transconductance in these strained-layer structures of 270 mS/mm was measured for 1-micron gate, normally-on devices at 300 K. Maximum drain current levels are 290 mA/mm, with excellent pinch-off and saturation characteristics. The transconductance increased to 360 mS/mm at 77 K while no persistent photoconductivity or drain collapse was observed. Preliminary microwave results indicate a 300-K current gain cutoff frequency of about 20 GHz. These results are equivalent to the best GaAs/AlGaAs MODFET results and are due in part to the improved transport properties and carrier confinement in the InGaAs quantum well.

Ketterson, A.↗

NASA NTRS1985

Cryogenic operation of pseudomorphic AlGaAs/InGaAs single-quantum-well MODFETs

The 77 K operation of AlGaAs/InGaAs MODFETs has been investigated. The structures, grown by MBE, make use of a 200 A undoped In(0.15)Ga(0.85)As quantum well for electron confinement and an Si-doped Al(0.15)Ga(0.85)As top barrier. The MODFETs with 1 micron gate lengths exhibit extrinsic transconductances of 360 mS/mm and maximum currents of 310 mA/mm at 77 K. The use of a low Al mole fraction AlGaAs/InGaAs heterojunction makes it possible to avoid the persistent trapping effects encountered in AlGaAs/GaAs MODFETs without sacrificing device performance.

Masselink, W. T.↗