DOE OSTI2024

Analysis of the turbostratic structures in PAN-based carbon fibers with wide-angle x-ray diffraction

Carbon fiber (CF) is a versatile material renowned for its excellent mechanical, thermal, and electrical properties. Polyacrylonitrile (PAN)-based CFs dominate the market due to their high tensile strength, rendering them suitable for structural applications in a wide variety of applications ranging from sporting goods to aerospace. Over five decades of commercial development of PAN-based CF has resulted in a range of varieties with different tensile moduli and tensile strengths. The microstructures, nanostructures, and crystal structures of PAN-based CF play pivotal roles in the macroscale properties of this material. In particular, the crystal structure and crystallite orientation in CF is closely related to the mechanical properties. The crystal structure of PAN-based CF generally consists of turbostratic carbon, which is a disordered form of graphite, the characteristics of which can be effectively characterized in a bulk format through wide-angle x-ray diffraction (WAXD). In this work, we employed a three-part approach to the analysis of WAXD patterns collected from four intermediate modulus PAN-based CFs. The approach incorporates a Scherrer analysis, a Debye analysis, and an orientational analysis to provide precise estimates of crystallite sizes, crystallite distributions, and crystallite orientations with the fiber axis. Furthermore, the results presented here suggest that intermediate modulus PAN-based CF mostly consists of small turbostratic crystallites (<4 nm), with larger crystallites having increased orientation with the fiber axis. The results here imply the presence of curvature and/or wrinkling of the turbostratic layers within the CF structure.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Unveiling the microstructural evolution of carbon fibers derived from polyamide-6

Polyacrylonitrile-based carbon fibers have dominated the industry for decades, but the high cost of polyacrylonitrile has prevented the widespread adoption of carbon fiber in high-volume structural applications. As such, a significant amount of research has been dedicated to finding an alternative, low-cost carbon fiber precursor. In this work, carbon fibers were produced from polyamide-6 using metal salt impregnation and a thermo-oxidative stabilization step. To gain further insight into the carbonization process and microstructural transformation, the morphologies, crystallinities, elemental compositions, and thermal stabilities of the fibers were characterized at various stages of processing. The stabilization step resulted in a significant increase in carbon yield, indicating a dramatic increase in thermal stability. This is due to the crosslinking of polyamide-6 chains, which was confirmed by functional group analysis. The crystallinity of the fibers was also significantly altered during processing, as the produced carbon fibers consisted of pseudo-amorphous carbon with two distinct regions of metal salt impregnation. Finally, the findings and microstructural evolution mechanisms provide guidelines for further research into carbon fiber produced from polyamide-6.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Experimental Investigation of a Novel Membrane-Based Condensing Heat Exchanger for High Efficiency Furnaces

Building space heating consumes approximately one-third of all global natural gas end use. Higher-efficiency (i.e., condensing) furnaces constitute only about 30% of the annual furnace shipments in the United States because the condensing heat exchangers must use highly expensive, corrosion-resistant materials to be protected from acidic components in the furnace flue gas stream. Increasing the market share of high-efficiency furnaces will reduce greenhouse gas emissions. This study developed and tested a benchtop prototype of a novel membrane-based heat exchanger (MHX) for high-efficiency furnaces to achieve nonacidic condensation via nanoporous membranes. Test results show that both sensible and latent heat were recovered by the MHX, and the fraction of latent heat recovery ranged from about 25% to 45% over the range of operating conditions evaluated. The amount of water condensed through the MHX increased with the increase of flue gas flow rate and decreased with increasing coolant temperature. The fraction of latent heat recovery decreased with the increase of flue gas flow rate and coolant temperature. The pH value of condensed water from the MHX was only mildly acidic, varying from 5.3 to 5.6 without any additional treatment, about 2.0 to 2.3 pH points higher (i.e., less acidic) than typical values for the condensate from conventional condensing furnaces. Therefore, feasibility of the MHX was experimentally verified, and the MHX could enable wider market penetration of highly energy-efficient condensing furnaces by reducing costs associated with managing the acid condensation compared with conventional condensing furnaces, possibly enabling the use of existing vent systems when replacing noncondensing furnaces (due to higher flue gas exit temperatures), and possibly reducing furnace first costs.

32 ENERGY CONSERVATION, CONSUMPTION, AND UTILIZATI↗

DOE OSTI2021

Alumina-based filters made via binder jet 3D printing of alumina powder, colloidal silica infiltration, and sintering

Alumina-based, porous filter media was made via a binder jet 3D printing process consisting of an alumina powder printing step with subsequent heating, colloidal silica infiltration, drying, and sintering to consolidate particles yet retain a net open porous microstructure. The composites made were alumina-silica or alumina-mullite, where the silica sintering aid was used to densify and join the alumina particles. The resulting composite structures had open porosities in the 25–31 vol% range as measured by Archimedes density. Pressure drops were measured across the filter media at constant flow rates to compare disc shapes and complex, 3D printed filters based on the N95 design requirements. Complex, 3D-printed alumina composites were produced with acceptable pressure drops for N95 implementation.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Predicted Heat Flux Performance of Actively Cooled Tungsten-Armored Graphitic Foam Monoblocks

Tungsten (W)–armored graphitic foam monoblocks were developed for applications requiring high-Z plasma-facing material in long-pulse fusion experiments and ultimately deuterium-tritium fusion reactors. The monoblocks are an integrated material system combining the advantages of a chemical vapor deposited (CVD) W coating with a high-conductivity graphitic foam. The W is a high-melting-point, high-Z material with low tritium retention. The graphitic foam coupled to a swirl tube serves as a high-thermal-conductivity heat sink that cannot melt, although it can sublime at much higher temperatures than copper melts. Together, they comprise a robust plasma-facing component (PFC) weighing roughly 5% of an all-W component or 17% of a traditional W-coated copper heat sink.A single-channel mock-up consisting of four graphitic foam monoblocks equipped with a water-cooled swirl tube was fabricated for eventual testing in the 60-kW, EB-60, rastered electron beam at the Applied Research Laboratory of The Pennsylvania State University. Two monoblocks have a thin 50-μm-thick coating of pure W chemically vapor deposited over NbC and pure Nb interlayers. Two others have a 2-mm-thick pure W coating CVD on graphitic monoblocks using the same interlayers. The mock-up will be cooled with available 10 m/s, 0.7 MPa water with a 22°C inlet temperature and subjected to varying uniform heat loads up to 20 MW/m 2 . It is equipped with type-K thermocouples at various depths, and calibrated infrared thermography and spot pyrometry will be used to characterize the heated surface. Real-time water calorimetry will be used to ascertain the absorbed steady-state power and infer the heat flux during testing. Since testing cannot be done under prototypic divertor flow conditions, it is necessary to predict the thermal response of this novel PFC system and investigate the power sharing between radiation and convection at divertor heat flux levels and its inherent ability to avoid critical heat flux. Results are reported for predictions obtained from computational fluid dynamics models up to 30 MW/m 2 of steady-state uniform heat flux. Leading-edge heat loads of 30 MW/m 2 on a 2-mm-wide side strip were also investigated to ascertain if coating delamination is likely.

70 PLASMA PHYSICS AND FUSION TECHNOLOGY↗

DOE OSTI2020

Transient computational and experimental thermal analysis of graphite foam monoblock

A densified graphite foam is being explored for its applicability as plasma-facing material in fusion devices. Three different graphite foam monoblocks are constructed and tested in the Garching Large Divertor Sample Testing Facility. The monoblock samples consist of graphite foam press-fit to a single tube, graphite foam cubes brazed to a single, and graphite foam cubes press-fit to a single tube. The tube is composed of CuCrZr with a steel twisted tape. The monoblocks are exposed to the heat fluxes of 5, 6, and 8 MW/m 2 for 30 s to determine the maximum surface and body temperatures measured with thermocouple for each monoblock design. The press-fit monoblocks are exposed to 8 MW/m 2 for 15 s for 100 cycles to determine the effect of thermal cycling on the contact between the graphite foam and the tube. STAR-CCM+ is used to predict how much the contact between the foam and tubes varies as a result of thermal cycling. In addition, the 6 MW/m 2 loading is modeled in STAR-CCM+ to compare the transient cooldown curves of the computational results to the recorded temperatures at the surface and two different thermocouple locations. This comparison is used to validate the temperature-dependent thermal conductivity and specific heat capacity used in the models of the graphite foam. The computational modeling of the experiment has been used to hypothesize ways to use and improve upon the graphite foam as a suitable material for fusion applications.

Gehrig, Monica↗