We present the synthesis and experimental characterization of the binary intermetallic compound Pr 7 Ru 3 . The polycrystalline sample was prepared by arc melting pure Pr and Ru, followed by homogenization at 500 °C and 600 °C for 48 and 89 h, respectively. Powder x-ray diffraction confirms that Pr 7 Ru 3 crystallizes in an orthorhombic crystal structure (Pnma, space group no. 62) with the lattice parameters: a = 7.3606(7) Å, b = 23.120(1) Å and c = 6.5959(5) Å. Magnetization, resistivity, and heat capacity measurements reveal a ferromagnetic transition in Pr 7 Ru 3 with the Curie temperature T C ~ 24.5 K. The bulk transition is confirmed by a large λ-shape anomaly observed in the specific heat measurement. The magnetic susceptibility above the transition obeys the modified Curie-Weiss law with a positive Curie-Weiss temperature $\ominus$ CW = 30(1) K and an effective magnetic moment of 3.39(1) μ B /Pr. Resistivity data for Pr 7 Ru 3 reveals metallic-like behavior with a clear anomaly at the transition temperature which is smeared by an applied magnetic field. We also synthesized high-quality nonmagnetic analog La 7 Ru 3 for which superconducting transition is observed with T c = 1.95 K, in agreement with the literature.
For this study, the B20-type cobalt germanide CoGe was investigated by measuring the specific heat, resistivity, and 59 Co nuclear magnetic resonance (NMR). We observed a phase transition at T Q = 13.7 K, evidenced by a very narrow peak of the specific heat and sharp changes of the nuclear spin-spin (T 2 –1 ) and spin-lattice ( T 1 – 1 ) relaxation rates. The fact that the entropy release is extremely small and the Knight shift is almost independent of temperature down to low temperatures as anticipated in a paramagnetic metal indicates that the T Q transition is of nonmagnetic origin. In addition, we detected a crossover scale T 0 ~ 30 K below which the resistivity and the NMR linewidth increase, and T 1 –1 is progressively distributed in space, that is, a static and dynamical spatial inhomogeneity develops. While the order parameter for the T Q transition remains an open question, a group-theoretical analysis suggests that the finite electric quadrupole density arising from the low local site symmetry at cobalt sites could drive the crystal symmetry lowering from the P2 1 3 symmetry that is commensurate to the R3 symmetry with an incommensurate wave vector, which fairly well accounts for the T Q transition. The quadrupole-order-driven commensurate-incommensurate phase transition may be another remarkable phenomenon arising from the structural chirality inherent in the noncentrosymmetric B20 family.