Engineering topics
Koehler, Michael
Publications and source records attributed to Koehler, Michael.
Dual Emission Bands of a 2D Perovskite Single Crystal with Charge Transfer State Characteristics
Several hybrid halide 2D-perovskite species emit light with an emergent and controversial broadband emission Stokes-shifted down from the narrow band emission. This work uncovers the sub- and above-bandgap emission and absorption characteristics of PEA 2 PbI 4 prepared with gap states introduced during single crystal growth. Here, gap states led to coexistent intrinsic and heterostructured electronic frameworks that are selectively accessible with ultraviolet (UV) and infrared (IR) light, respectively, resulting in the phenomenon of photoluminescence (PL) switching from narrowband green to broadband red. Electron-energy dependent cathodoluminescence shows a relative increase in the broadband red PL intensity as the electron penetration depth increases from 30 nm to 2 μm, confirming the heterostructured framework is formed in the bulk of the crystal. Excitation–emission power slope of 2.5 and up-conversion pump transient absorption (TA) spectra suggest that the IR up-conversion excitation with red photoluminescence, peaked at 655 nm, is a multiphoton process occurring in the heterostructured framework through a nonlinear optical response. The energetic pathways toward the dual emission bands are revealed by pump–probe transient absorption spectroscopy, showing energetically broad gap states with high sensitivity to an IR pump are upconverted and subsequently quickly relax from high to low energy levels within 4 ps. Furthermore, the up-conversion red PL demonstrates a linear polarization with magnetic field effects, thus affirming that the band-like heterostructured framework is crystallographically aligned with characteristics of spatially extended charge-transfer states.
Grain size dependence of thermally induced oxidation in zirconium carbide
Here complementary analytical approaches were employed to probe the effect of grain size on thermally induced oxidation of zirconium carbide (ZrC) utilizing thermogravimetric analysis, differential scanning calorimetry, and Raman spectroscopy, as well as synchrotron-based and laboratory-based X-ray diffraction (XRD) experiments. The oxidation mechanism and phase behavior of nanocrystalline ZrC (grain size ~ 20 nm) were compared with that of the more documented microcrystalline ZrC (grain size ~ 1 µm). Synchrotron XRD at the Advanced Photon Source with a hydrothermal diamond anvil cell (HDAC) used as a sample chamber revealed that the onset of oxidation is at ~ 380 °C for microcrystalline ZrC which is in agreement with previous work. In contrast, the critical oxidation temperature was ~ 330 °C for nanocrystalline ZrC. Additional high-temperature synchrotron XRD experiments at the National Synchrotron Light Source II using a lamp furnace in combination with Raman analysis showed that tetragonal ZrO 2 forms as an initial oxidation product and transforms at higher temperatures to the monoclinic phase. Thermogravimetric analysis (TGA) coupled with differential scanning calorimetry (DSC) confirmed the X-ray results of a lower critical oxidation temperature for the nanocrystalline sample. The phase transformations in the oxide phase with associated critical temperatures were also evident in the thermodynamic data as exothermic heat events.
In-situ formation of Al3Ni nano particles in synthesis of Al 7075 alloy by friction stir processing with Ni powder addition
Not Available
Radiation-induced modifications in copper oxide growth
Explore the source record for details and available documents.