7 records

DOE OSTI2023

Schottky contacts on ultra-high-pressure-annealed GaN with high rectification ratio and near-unity ideality factor

Here we investigate the electrical characteristics of Ni Schottky contacts on n-type GaN films that have undergone ultra-high-pressure annealing (UHPA), a key processing step for activating implanted Mg. Contacts deposited on these films exhibit low rectification and high leakage current compared to contacts on as-grown films. By employing an optimized surface treatment to restore the GaN surface following UHPA, we obtain Schottky contacts with a high rectification ratio of ~10 9 , a near-unity ideality factor of 1.03, and a barrier height of ~0.9 eV. These characteristics enable the development of GaN junction barrier Schottky diodes employing Mg implantation and UHPA.

42 ENGINEERING↗

DOE OSTI2022

Vertical GaN junction barrier Schottky diodes with near-ideal performance using Mg implantation activated by ultra-high-pressure annealing

Here we report a kV class, low ON-resistance, vertical GaN junction barrier Schottky (JBS) diode with selective-area p-regions formed via Mg implantation followed by high-temperature, ultra-high pressure (UHP) post-implantation activation anneal. The JBS has an ideality factor of 1.03, a turn-on voltage of 0.75 V, and a specific differential ON-resistance of 0.6 mΩ·cm 2 . The breakdown voltage of the JBS diode is 915 V, corresponding to a maximum electric field of 3.3 MV cm –1 . These results underline that high-performance GaN JBS can be realized using Mg implantation and high-temperature UHP post-activation anneal.

42 ENGINEERING↗

DOE OSTI2022

Schottky contacts to N-polar GaN with SiN interlayer for elevated temperature operation

In this Letter, we unveil the high-temperature limits of N-polar GaN Schottky contacts enhanced by a low-pressure chemical vapor deposited (LPCVD) SiN interlayer. Compared to conventional Schottky diodes, the insertion of a 5 nm SiN lossy dielectric interlayer in-between Ni and N-polar GaN increases the turn-on voltage (V ON ) from 0.4 to 0.9 V and the barrier height ($\phi_B$) from 0.4 to 0.8 eV. This modification also reduces the leakage current at zero bias significantly: at room temperature, the leakage current in the conventional Schottky diode is >103 larger than that observed in the device with the SiN interlayer, while at 200 °C, this ratio increases to 105. Thus, the rectification ratio (ION/IOFF) at ±1.5 V reduces to less than one at 250 °C for the conventional Schottky diode, whereas for SiN-coated diodes, rectification continues until 500 °C. The I–V characteristics of the diode with an SiN interlayer can be recovered after exposure to 400 °C or lower. Contact degradation occurs at 500 °C, although devices are not destroyed yet. Here, we report N-polar GaN Schottky contact operation up to 500 °C using an LPCVD SiN interlayer.

71 CLASSICAL AND QUANTUM MECHANICS, GENERAL PHYSIC↗

DOE OSTI2022

Record >10 MV/cm mesa breakdown fields in Al 0.85 Ga 0.15 N/Al 0.6 Ga 0.4 N high electron mobility transistors on native AlN substrates

The ultra-wide bandgap of Al-rich AlGaN is expected to support a significantly larger breakdown field compared to GaN, but the reported performance thus far has been limited by the use of foreign substrates. In this Letter, the material and electrical properties of Al 0.85 Ga 0.15 N/Al 0.6 Ga 0.4 N high electron mobility transistors (HEMT) grown on a 2-in. single crystal AlN substrate are investigated, and it is demonstrated that native AlN substrates unlock the potential for Al-rich AlGaN to sustain large fields in such devices. We further study how Ohmic contacts made directly to a Si-doped channel layer reduce the knee voltage and increase the output current density. High-quality AlGaN growth is confirmed via scanning transmission electron microscopy, which also reveals the absence of metal penetration at the Ohmic contact interface and is in contrast to established GaN HEMT technology. Two-terminal mesa breakdown characteristics with 1.3 μm separation possess a record-high breakdown field strength of ~11.5 MV/cm for an undoped Al 0.6 Ga 0.4 N-channel layer. The breakdown voltages for three-terminal devices measured with gate-drain distances of 4 and 9 μm are 850 and 1500 V, respectively.

71 CLASSICAL AND QUANTUM MECHANICS, GENERAL PHYSIC↗

DOE OSTI2021

On the characteristics of N-polar GaN Schottky barrier contacts with LPCVD SiN interlayers

In this work, we study the behavior of N-polar GaN Schottky diodes with low-pressure chemical vapor deposited (LPCVD) SiN interlayers and unveil the important role of an amphoteric miniband formed in this interlayer due to a previously identified and dominating Si dangling bond defect. Through analysis of temperature-dependent current–voltage (I–V–T), capacitance–voltage (C–V), and x-ray photoelectron spectroscopy measurements, we observe that when nickel is deposited on LPCVD SiN pretreated with hydrofluoric acid, the SiN/GaN interface is responsible for determining the overall system's barrier height. By contrast, contact formation on oxidized LPCVD SiN leads to a metal/SiN-dominant barrier. We, consequently, propose band diagrams that account for an amphoteric miniband in LPCVD SiN, leading to a new understanding of LPCVD SiN as a lossy dielectric with surface barrier-dependent behavior.

42 ENGINEERING↗

DOE OSTI2020

Chemical treatment effects on Schottky contacts to metalorganic chemical vapor deposited n-type N-polar GaN

In this article, we investigate the effect of different chemical treatments, such as solvents, bases, and acids, on the surface properties and electrical behavior of Schottky diodes fabricated on metalorganic chemical vapor deposition-grown, n-type, N-polar GaN. The I–V and C–V barrier heights of the as-grown Schottky diodes are found to be 0.40 eV and 0.60 eV, respectively, with an ideality factor n = 1.07. It is found that the solvent treatments neither change the surface nor the electrical performance of the Schottky diodes, as expected. However, the treatments by the alkaline photolithography developer and acid—the latter of which is often used to clean the surface of Ga-polar GaN films prior to metal contact deposition—degrade the performance of N-polar GaN. These base and acid treatments severely roughen the surface by creating triangular/hexagonal crystallographic facets. The I–V and C–V barrier heights of these base- and acid-treated diodes are increased to 0.63 eV and 1.00 eV, respectively, with ideality factor values n < 1.2. X-ray photoelectron spectroscopy studies indicate that base- and acid-treated surfaces have lower oxygen content as compared to the as-grown sample surface. It is understood that the increment in the barrier height for base- and acid-treated diodes could be due to the change in polarity, from N-polar to semi-polar/non-polar, on these crystallographic features. All these results demonstrate that, unlike for Ga-polar GaN, the N-polar GaN surface is highly reactive to bases and acids.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2020

High gain, large area, and solar blind avalanche photodiodes based on Al-rich AlGaN grown on AlN substrates

We demonstrate large area (25 000 μm2) Al-rich AlGaN-based avalanche photodiodes (APDs) grown on single crystal AlN substrates operating with differential (the difference in photocurrent and dark current) signal gain of 100 000 at 90 pW (<1 μW cm−2) illumination with very low dark currents <0.1 pA at room temperature under ambient light. The high gain in large area AlGaN APDs is attributed to a high breakdown voltage at 340 V, corresponding to very high breakdown fields ∼9 MV cm−1 as a consequence of low threading and screw dislocation densities < 103 cm−2. The maximum charge collection efficiency of 30% was determined at 255 nm, corresponding to the bandgap of Al0.65Ga0.35N, with a response of 0.06 A/W. No response was detected for λ > 280 nm, establishing solar blindness of the device.

Reddy, Pramod (ORCID:0000000285561178)↗