Publications and source records attributed to Kokta, Milan R..
A room temperature solid-state laser is provided. A laser crystal is disposed in a laser cavity. The laser crystal has a LuAG host material doped with a concentration of about 0.35% Ho ions, about 5.57% Tm ions and at least about 1.01% Cr ions. A broadband energizing source such as a flashlamp is disposed transversely to the laser crystal to energize the Ho ions, Tm ions and Cr ions.
Ho:Tm:LuAG has been grown, examined spectroscopically, and lased at 2.1 microns. Ho:Tm:LuAG was selected for this experimental investigation when quantum-mechanical modeling predicted that it would be a good laser material for Ho laser operation on one of the 5I7 to 5I8 transitions. Lasing was achieved at 2.100 microns, one of the three wavelengths predicted to be most probable for laser action.
Variable temperature laser experiments were performed with two compositions of Tm:Cr:YAG (5.0:1.0 and 1.5:2.0 percent substitutions), with special attention given to the spectroscopic details of energy transfer and quasi-3 level lasing. Differences in laser threshold and flashlamp degradation were found in lasing the two compositions, and it is suggested that the difference is due to the 1.5:2.0 rod having much less efficient energy transfer than the 5.0:1.0 Tm:Cr crystals. To first order, the thermal occupation factor is found to dominate laser threshold determination at temperatures betwen 120 and 240 K.