System-level ASPEN models were developed for the CO2 partial reduction subsystem and a bioregenerative life support subsystem (BRLSS). The individual component and subsystem models were integrated into three different system-level atmospheric revitalization subsystem (ARS) models: baseline physico-chemical, BRLSS, and partial reduction of Martian CO2. The Aspen models were based on FORTRAN interfaces necessary for integration with another program, G189A, to perform quasi-transient modeling. Detailed reactor models were prepared for the two CO2 reduction reactors (Bosch and Advanced Carbon Formation), and the low-temperature trace contaminant oxidation reactor.

Kolodney, M.↗

NASA NTRS1972

Activated sintering of ThO2 and ThO2-Y2O3 with NiO.

Scanning electron microscopy and isothermal shrinkage measurements were used to study the effects of additives on the sintering of Thoria-Yttria compacts and loose powders. Small amounts of the oxides of Ni, Zn, Co, and Cu were found to reduce the sintering temperature (which is normally above 2000 C). In particular, NiO, at a concentration of 0.8 wt %, was found to yield high-density bodies at temperatures below 1500 C. Densification occurs very rapidly, and is followed by a much slower sintering process typical of volume diffusion.

Halbfinger, G. P.↗

NASA NTRS1971

Mechanism of the oxidation of titanium disilicide.

Study of the oxidation of TiSi2 at temperatures of 300 to 1300 C. Wafers prepared using the techniques of powder metallurgy had densities of 95 to 98% of the theoretical value. On oxidation at temperatures up to 600 C, the polished wafers formed a protective, titania-silica glass. The rate data indicate a complex surface and diffusion-limited mechanism. Above 600 deg C, the oxide consisted of an amorphous SiO2 film with crystalline islands of TiO2 (rutile). From 1000 to 1300 C, parabolic kinetics with an activation energy of 21.3 kcal/mole were observed. These data are consistent with a model in which the rate-determining step is the diffusion of oxygen through the silica film with the simultaneous diffusion of titanium from the substrate to the islands of rutile growing on top of the amorphous silica.

Schwettmann, F. N.↗