Grain subdivision and structural modifications by high-energy heavy ions in UO 2 with different initial grain size
Irradiation with 84 MeV Xe ions at peak fluence above 7 × 10 17 ions/cm 2 has been carried out on two UO 2 samples with different initial grain sizes at 300 °C and 500 °C. Characterization of both grain structure and bubble morphology has been performed using transmission electron microscopy, image analysis and precession electron diffraction. The bubble size in the large-grained sample was smaller than that in the standard-grain sample, confirming fission gas precipitation resistance in the former. The ion irradiation in the high electronic energy deposition range has caused formation of a large density of dislocations which resulted in grain polygonization for the sample with standard grain size, which was observed in multiple lamellas extracted next to each other at peak dose. The sample with large grains showed inconsistent behavior. In one case, dislocation pile-up occurred, but no sub-grain formation was observed. An adjacent location showed sub-grain formation, even if to less extent compared to the standard grain-size sample. Furthermore, these findings suggest a limited polygonization resistance in large-grained UO 2 compared to standard-grain UO 2 . Recrystallization of both sample surfaces was present, leaving unclear if this is a surface effect or a consequence of the highest energy deposition rate in this area.