Engineering topics
Komini Babu, Siddharth (ORCID:0000000157248486)
Publications and source records attributed to Komini Babu, Siddharth (ORCID:0000000157248486).
Asymmetric gas diffusion layers for improved water management in PGM-free electrodes
Not Available
Effect of Engineered Cracks in Catalyst Layers on PEMFC Catalyst Layer Durability
Proton exchange membrane fuel cells (PEMFCs) are expected to play a pivotal role in decarbonizing the transportation sector, and particularly heavy-duty vehicles (HDVs). However, improvements in durability are needed for PEMFCs to compete with state-of-the-art power sources for HDVs. Here, we examine how catalyst layer (CL) cracks that are engineered affect the CL durability by using patterned silicon templates to control the CL crack density at the micrometer scale. Electrochemical analyses show that the initial PEMFC performance is relatively unaffected by crack density, but the performance after durability testing was strongly affected. Specifically, CLs with high crack density showed higher performance relative to CLs without cracks after application of a carbon corrosion accelerated stress test. Electrochemical analyses coupled with X-ray computed tomography and scanning transmission electron microscopy with energy dispersive X-ray spectroscopy showed that the cracks provide shorter oxygen diffusion pathways to reaction sites, leading to decreased oxygen transport resistance. Additionally, we observed that the catalyst durability is unaffected by cracks. Our results provide a mechanistic explanation of the role of cracks in CL durability.
Effect of Catalyst and Catalyst Layer Composition on Catalyst Support Durability
Polymer electrolyte membrane fuel cells (PEMFCs) are efficient, zero-emission engines for the automotive sector. However, cost and durability are major barriers for the commercialization of PEMFCs. Degradation of the carbon support in the cathode catalyst layer due to high potential excursions caused by unmitigated events like H 2 starvation, or start-up/shutdown are still a major durability issue in PEMFCs. Catalyst support durability was studied by accelerated stress tests (ASTs) that included repeated potential cycling from 1.0 to 1.5 V. The effect of catalyst layer composition on carbon corrosion was studied using membrane electrode assemblies with different catalysts (Pt, PtCo), catalyst composition (catalyst wt.%, supports), ionomer composition (loading, and equivalent weights). The corrosion of the carbon support is similar between Pt and PtCo catalysts. However, the performance degradation rate is higher for the alloy catalysts due to differences in catalyst particle size and the transition metal’s leaching accelerating the performance degradation. The carbon loss is lower for catalysts with lower initial carbon loading (or higher catalyst wt.%), which is better for durability. However, the cumulative loss of carbon is identical for electrodes with the same catalyst support irrespective of catalyst and ionomer composition in the catalyst layer.
Editors’ Choice—Diffusion Media for Cation Contaminant Transport Suppression into Fuel Cell Electrodes
Polymer electrolyte membrane fuel cells provide an alternative option to fossil fuel-based energy conversion devices. However, the corrosion of fuel cell components, specifically the bipolar plates, introduces contaminants (e.g., Fe, Ni) into the membrane electrode assembly (MEA). These contaminants accelerate the ionomer degradation by acting as a Fenton’s reagent, decreasing the fuel cell’s durability. This study presents the mechanism and the diffusion media properties affecting the transport of cation contaminants into the MEA. Cation contaminant transport was studied after altering the gas diffusion layers (GDLs) wettability, emulating the GDL properties after prolonged operation, by ex situ hydrogen peroxide treatment or in situ electrochemical potential cycling. A GDL with crack-free microporous layer (MPL) showed a lower cation transport rate to the catalyst layer than MPL with cracks after both ex situ and in situ treatment. A novel GDL was developed from modification of the conventional GDL via the addition of a hydrophobic layer to the GDL substrate, which suppressed the contaminant cation transport significantly. This novel GDL also showed improved fuel cell performance.