NASA NTRS1990

MIS capacitor studies on silicon carbide single crystals

Cubic SIC metal-insulator-semiconductor (MIS) capacitors with thermally grown or chemical-vapor-deposited (CVD) insulators were characterized by capacitance-voltage (C-V), conductance-voltage (G-V), and current-voltage (I-V) measurements. The purpose of these measurements was to determine the four charge densities commonly present in an MIS capacitor (oxide fixed charge, N(f); interface trap level density, D(it); oxide trapped charge, N(ot); and mobile ionic charge, N(m)) and to determine the stability of the device properties with electric-field stress and temperature. The section headings in the report include the following: Capacitance-voltage and conductance-voltage measurements; Current-voltage measurements; Deep-level transient spectroscopy; and Conclusions (Electrical characteristics of SiC MIS capacitors).

Kopanski, J. J.↗

NASA NTRS1987

Behavior of ion-implanted junction diodes in 3C SiC

p-n junction diodes have been formed by ion implantation of B or Al in 3C SiC and annealing at 1365 C. The current-voltage characteristics of the Al-implanted structures show little rectification. The B-implanted diodes show rectification, with ideality factors of 2.2 and higher, breakdown voltages between 5 and 10 V, and a series resistance of the order of 20 kohm. The current-voltage characteristics were measured between room temperature and 270 C. The extracted ideality factors increase with temperature.

Avila, R. E.↗

NASA NTRS1986

Behavior of inversion layers in 3C silicon carbide

A study on the field-induced surface-charge region in 3C silicon carbide (SiC) using 1 MHz capacitance-voltage (C-V) measurements at room temperature is here reported. A double column mercury probe was used on oxidized SiC substrates to form metal-oxide-semiconductor (MOS) structures. These structures were characterized in terms of the substrate doping profile, effective fixed oxide charge, and interface trap density. A distinctive feature of the MOS C-V curves from accumulation to inversion is that after going into deep depletion the capacitance rises to its equilibrium inversion level during the voltage sweep. Capacitance transient measurements indicate that the minority-carrier generation occurs at the SiO2/SiC interface.

Avila, R. E.↗

NASA NTRS1984

Thermal oxidation of 3C silicon carbide single-crystal layers on silicon

Thermal oxidation of thick single-crystal 3C SiC layers on silicon substrates was studied. The oxidations were conducted in a wet O2 atmosphere at temperatures from 1000 to 1250 C for times from 0.1 to 50 h. Ellipsometry was used to determine the thickness and index of refraction of the oxide films. Auger analysis showed them to be homogeneous with near stoichiometric composition. The oxide growth followed a linear parabolic relationship with time. Activation energy of the parabolic rate constant was found to be 50 kcal/mole, while the linear rate constant was 74 kcal/mole. The latter value corresponds approximately to the energy required to break a Si-C bond. Electrical measurements show an effective density of 4-6 x 10 to the 11th per sq cm for fixed oxide charges at the oxide-carbide interface, and the dielectric strength of the oxide film is aproximately 6 x 10 to the 6th V/cm.

Fung, C. D.↗