Kota, Arun | Search NASA

NASA NTRS2004

Residual Gas Effects on Detached Solidification in Microgravity

Our long term goal has been to make detached solidification reproducible, which requires a full understanding of the mechanisms underlying it. Our Moving Meniscus Model of steady-state detachment predicts that it depends strongly on the surface tension of the melt and the advancing contact angle with the ampoule wall. Thus, the objective of the current project was to determine the influence of residual gases on the surface tension and contact angle of molten semiconductors on typical ampoule materials. Our focus was on the influence of oxygen on indium antimonide on clean silica ("quartz"). The research was performed by three chemical engineering graduate students, the third of whom will complete his research in the summer of 2005. Originally, we had planned to use a sealed silica cell containing a zirconia electrochemical element to control the oxygen partial pressure. However, zirconia requires an operating temperature above the 530 C melting point of InSb and is difficult to form a gas-tight seal with silica. Thus, we decided instead to flow an oxygen-containing gas through the cell. A special apparatus was designed, built and perfected. A piece of InSb was placed on a horizontal silica plate in a quartz cell. High purity argon, helium or hydrogen-containing gas is passed continuously through the cell while the oxygen concentration in the effluent gas is measured. The shape of the resulting drop was used to determine contact angle and surface tension of Ga-doped and high purity InSb. Oxygen appeared to decrease the contact angle, and definitely did not increase it. The following section gives the background for the research. Section 2 summarizes the results obtained on Ga-doped InSb with relatively high oxygen concentrations. Section 3 describes recent improvements made to the apparatus and methods of analysis. Section 4 gives recent results for high-purity InSb at low oxygen concentrations. Final results will be obtained only this summer (2005). Each section has its own references.

Wilcox, William R.↗

NASA NTRS2003

Residual Gas Effects on Detached Solidification in Microgravity

Many microgravity directional solidification experiments yielded ingots with portions that grew without contacting the ampoule wall, leading to greatly improved crystallographic perfection. Our long-term goal is to make such detached solidification reproducible, which requires a full understanding of the mechanisms underlying it. Our Moving Meniscus Model of steady-state detachment predicts that it depends strongly on the surface tension of the melt and the advancing contact angle with the ampoule wall. Detached solidification is more likely when the contact angle for the melt on the ampoule wall is high, i.e. non-wetting. It has been claimed that impurities increase the contact angle. The objective of the current project is to determine the influence of residual gases on the surface tension and contact angle of molten semiconductors on typical ampoule materials. We are focusing on determining the influence of oxygen on the contact angle of molten InSb on clean silica ('quartz'), including the advancing and retreating contact angles in addition to the usual equilibrium contact angle. We have created a gas flow system that allows us to control the oxygen partial pressure over a sessile drop of InSb on a horizontal quartz surface. The cell is slowly tilted while videotaping to reveal the contact angles on the two sides of the drop just prior to it rolling down the surface. Thus far, we have learned the following: (1) Molten InSb readily forms an oxide layer in the presence of the trace amounts of oxygen found in high purity argon; (2) This oxide contains a substantial amount of Ga, which presumably is a trace contaminant that is not detectable in the starting material; (3) The addition of 10% hydrogen to the argon gas is sufficient to reduce the oxide and produce a clean drop; (4) An infrared filter must precede the video camera in order to produce a sharp image of the drop for later image analysis; (5) Tilting the surface on which the drop rests causes the two sides of the drop to display different contact angles, reflecting contact line sticking; (6) Vibration strongly accelerates the approach of the drop to its final shape on a horizontal surface by helping to overcome sticking of the contact line; (7) Oscillation of the drop surface due to vibration appears to increase as the surface is inclined from horizontal. Presumably, the angle at which the drop rolls down the surface is also reduced by vibration. This observation is particularly significant, as the meniscus must move along the ampoule wall during detached solidification.

Regel, Liya L.↗