DOE OSTI2024

Electrical property enhancement of non-heat-treatable wrought aluminum alloys using graphene additives

With growing efforts of electrification, aluminum’s role as a light-weight conductor material has become increasingly prominent. There is a critical need to improve the electrical performance of aluminum at room temperature and high operating temperatures. In this study, the effect of graphene nanoparticle additives on the electrical performance of a non-heat treatable alloy were (AA3003) explored. Graphene’s unusual structure and electronic properties were used to improve AA3003 properties. Here, in this work, the effects of graphene on the evolution of electrical properties and microstructural features have been explored on lab scale hot extruded AA3003-graphene composites. Hot pressing schedules and extrusion temperatures were varied to investigate changes in intermetallic dispersion characteristics in the presence of dispersed graphene. We measured a reduction of 10.3 % in the temperature coefficient of resistance in the AA3003 sample with 0.05 wt% graphene extruded at 400 °C, along with a maximum increase of 1.1 % in electrical conductivity at 20 °C. Increasing the hot-pressing times up to 8 hours was also found to consistently increase the electrical conductivity, due to increased precipitation of intermetallic phases. Despite being a non-heat treatable alloy, AA3003 displays interesting precipitation dynamics and grain recrystallization trends that can be modulated with varying levels of heat treatment, graphene concentrations, and hot extrusion process parameters.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Simultaneously improved electrical and mechanical performance of hot-extruded bulk scale aluminum-graphene wires

Aluminum-based alloys are highly sought after as lightweight alternatives in electric grid applications. Improving the electrical conductivity of aluminum alloys has the potential to increase the energy efficiency of power transport. Here we used a hot extrusion process to synthesize AA1100 alloy with low-cost reduced graphene oxide nanoparticles to manufacture ultra-conductive aluminum composites in this study. The effects of graphene content on the electrical and mechanical performance of the composites were evaluated. The macroscale AA1100/graphene wires demonstrated a 2.1% enhancement in electrical conductivity at 20 °C, while the ultimate tensile strength increased by 6.1%. A Zener-Hollomon model was used to confirm the in-process exfoliation of the agglomerated graphene nanoparticle feedstock into high electrical conductivity graphene-like flakes during extrusion. They may have provided high-velocity carrier pathways leading to the enhanced electrical performance of the alloy. Transmission electron microscopy at aluminum-graphene interfaces ensures the preclusion of detrimental carbide formation during composite synthesis while confirming the structure graphene-like flakes. The in-process exfoliation provides an economically viable technique to produce bulk scale graphinated aluminum composites for advanced application and can be applied more generally to other alloy systems.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Macro copper-graphene composites with enhanced electrical conductivity

Composites demonstrating simultaneously enhanced-electrical conductivity, current density and lowered-temperature coefficient of resistance (TCR) compared to copper have been highly sought after for their advantages in efficient energy transport behavior. While such conductors have been demonstrated in 1D (nanowires) and 2D (films) samples, achieving similar behavior in 3D has been challenging owing to the limitations of the synthesis techniques used. In this paper, novel macro-scale 3D copper conductors were demonstrated with simultaneously increased electrical conductivity and decreased temperature coefficient of resistance (TCR) through the addition of graphene. Hot-extrusion was used to manufacture over 1-m-long, 2-mm-diameter copper-graphene composites with varying graphene content and defect density. Results showed that the electrical conductivity and current density in composites with low defect density graphene increased monotonically as a function of graphene content. They also demonstrated a significant decrease of over 17% in TCR with the addition of only 15 ppm graphene along with over 52% improvement in current density. Comparatively composites with high defect density graphene demonstrated lower electrical conductivity and current density. This study provides first-of-its-kind evidence of 3D metal composites whose bulk electrical performance has been enhanced using graphene additive in minute quantities. Further developments in this area are essential to achieve high performance composite conductors that can improve energy transport efficiency and pave way for industrial adoption of such materials in the future.

36 MATERIALS SCIENCE↗