NASA NTRS1985

Fatigue Damage in Notched Composite Laminates Under Tension-Tension Cyclic Loads

The results are given of an investigation to determine the damage states which develop in graphite epoxy laminates with center holes due to tension-tension cyclic loads, to determine the influence of stacking sequence on the initiation and interaction of damage modes and the process of damage development, and to establish the relationships between the damage states and the strength, stiffness, and life of the laminates. Two quasi-isotropic laminates were selected to give different distributions of interlaminar stresses around the hole. The laminates were tested under cyclic loads (R=0.1, 10 Hz) at maximum stresses ranging between 60 and 95 percent of the notched tensile strength.

Stinchcomb, W. W.↗

NASA NTRS1985

Fatigue response of notched graphite/epoxy laminates

Tests were performed to determine the damage states in quasi-isotropic graphite/epoxy laminates with center holes caused by cyclic tensile loading. The influence of the stacking sequence on the initiation and interaction of damage modes and the relationship between damage, strength, stiffness, and life of the laminates were also studied. X-ray radiography, moire interferometry, and stiffness change were used to monitor damage. Fatigue damage in both laminates began with matrix cracks around the holes leading to delaminations. In laminates cycled at the same percent of notched tensile strength the stacking sequence influenced the density of the matrix cracks and the modes and distribution of the damage. Ply cracking was also caused by the stacking sequence. The damage states in the two laminates produced stiffness changes of 15 to 20 percent, different rates of change in residual strength, and a factor of two to four difference in fatigue life. It was determined that continued cyclic loading produced matrix cracks which led to fatigue of the laminates.

Kress, G. R.↗