DOE OSTI2024

Finite Element Analysis and Machine Learning Guided Design of Carbon Fiber Organosheet-Based Battery Enclosures for Crashworthiness

Carbon fiber composite can be a potential candidate for replacing metal-based battery enclosures of current electric vehicles (E.V.s) owing to its better strength-to-weight ratio and corrosion resistance. However, the strength of carbon fiber-based structures depends on several parameters that should be carefully chosen. Here, in this work, we implemented high throughput finite element analysis (FEA) based thermoforming simulation to virtually manufacture the battery enclosure using different design and processing parameters. Subsequently, we performed virtual crash simulations to mimic a side pole crash to evaluate the crashworthiness of the battery enclosures. This high throughput crash simulation dataset was utilized to build predictive models to understand the crashworthiness of an unknown set. Our machine learning (ML) models showed excellent performance (R 2 > 0.97) in predicting the crashworthiness metrics, i.e., crush load efficiency, absorbed energy, intrusion, and maximum deceleration during a crash. We believe that this FEA-ML work framework will be helpful in down select process parameters for carbon fiber-based component design and can be transferrable to other manufacturing technologies.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Room Temperature Stamping of High-Strength Aluminum for Lightweight Structural Automotive Components

The use of aluminum (Al) 7xxx series in automobile structural applications is limited by factors such as its low room-temperature formability in T6 temper and the need for off-line artificial aging to regain high strength if it is formed in soft temper. In this study, two tempers were established that enable Al 7075 blanks to be room temperature stamped to create side impact beams that achieve near-T6 strength without post-forming artificial aging. It is shown that natural aging at room temperature, after solution treatment and before stamping, provides an alternative to high temperature pre-aging and hot stamping techniques in 7xxx alloys. Both tempers enabled room temperature stamping of the beams without cracking, indicating good formability. The Al beams were ~38% lighter than the benchmark boron steel beam. Further, the hardness in the low-deformation regions of the stamped Al beams were within 88% of a conventional 7075-T6 sheet. Paint-bake treatment of the beams appeared to cause over aging, lowering the ultimate tensile strength and ductility. Finite element three point bending simulations of the beams showed higher bending force and energy absorption before failure for the Al 7075 showing good promise for 7xxx series Al as a light-weight alternative to steel beams.

36 MATERIALS SCIENCE↗

DOE OSTI2023

A sensitivity analysis of twinning crystal plasticity finite element model using single crystal and poly crystal Zircaloy

The popularity of crystal plasticity finite element method (CPFEM) models is increasing due to their ability to predict the mechanical response of crystalline materials such as metals and metal alloys more accurately than traditional continuum mechanics models. This is since the crystal plasticity models consider the effect of atomic structure, microstructural morphology, and properties of individual grains. These CPFEM models use a large number of material parameters in order to capture the mesoscale physics which comes with the downside of the tedious calibration process. In this paper, a CPFEM code was developed to include the twinning induced grain reorientation and subsequent crystallographic slip for HPC material. The developed code is incorporated in a large-scale, parallelized nonlinear solver WARP3D. Further, a sensitivity analysis with respect to 22 material parameters was then conducted using single crystal and polycrystal representative volume element (RVE) of Zircaloy material. Loading was applied along five different crystallographic orientations for single crystal RVE and along three directions namely, rolling (RD), transverse (TD), and normal (ND) direction for polycrystal RVE. Results obtained from the sensitivity analysis were used for the calibration of material parameters for Zircaloy. Finally, developed code along with calibrated material parameters was used to investigate the effect of the hydride phase formation in Zircaloy which is a typical case observed for nuclear applications. It was found that the volume fraction of the hydride phase has a significant impact on the mechanical properties of Zircaloy.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Investigation of desorption of hydrogen gas from polymer matrix using thermal desorption analysis and finite element modeling

Polymer materials are used widely as sealing materials and liners in hydrogen storage and transportation infrastructure. During operating conditions, polymers are exposed to high pressure hydrogen gas periodically. When in contact, the hydrogen gas diffuses through the polymer material with ease due to its smaller sized molecules compared to the polymer molecules. In the event of rapid decompression of outside hydrogen gas, the hydrogen molecules within the polymer diffuse out. This process is known as the desorption of polymer and can cause blisters or cracking causing permanent damage to the polymer. Here, we used a combined experimental and modeling approach to investigate the desorption of the hydrogen gas in the polymer. Thermal desorption analysis (TDA) experiments were performed on the polymer sample exposed to the high-pressure hydrogen gas to measure the diffusion coefficient and equilibrium hydrogen concentration. Experiments also provided the quantity of hydrogen within the polymer during the desorption process which followed Fick’s law. However, for higher pressurization values, some anomaly was observed in the quantity of hydrogen remaining in the polymer sample. A continuum mechanics based coupled diffusion–deformation-damage model was deployed to simulate the gas desorption process in the material using the finite element method to understand its effect on the material. It was found that the anomaly in TDA results were due to the blister formation on the polymer surface which resulted in longer hydrogen retention. Simulations also showed that blister formation can be affected by multiple parameters such as the addition of filler particles, and pre-existing cavity size.

36 MATERIALS SCIENCE↗

DOE OSTI2023

A diffusion–deformation model with damage for polymer undergoing rapid decompression failure

Green hydrogen is emerging as one of the most promising alternatives to replace fossil fuels. While hydrogen gas has a good energy density by weight, its poor energy density by volume requires it to be stored under high pressure for commercial use. The hydrogen infrastructure developed to handle this high pressure hydrogen contains multiple components made of polymers as sealing agents. Although polymers do not react chemically with hydrogen gas, they undergo a mechanical failure when high pressure hydrogen gas is suddenly depressurized. This phenomenon known as 'rapid decompression failure' occurs due to the diffusion of hydrogen through polymer and getting trapped inside pre-existing cavities or voids. Here, in this paper, a continuum mechanics-based coupled diffusion-deformation-damage model was developed to predict the hydrogen distribution, stress distribution, and damage propagation inside the polymer while it undergoes rapid decompression failure. The polymer was modeled as a hyperelastic material because it represents the nonlinear material response observed in uniaxial tensile tests perfectly. The effects of hydrogen diffusivity, pre-existing cavity size, cavity location, applied hydrogen pressure, and depressurization rate on damage initiation were studied. It was found that the coefficient of diffusion plays an important role in damage initiation and damage was mostly concentrated in the inside areas rather than near the surface. Experiments were conducted with EPDM polymer which agreed well with the predicted trends using the given model. The effect of adding carbon black and silica filler particles and plasticizer to the pure EPDM polymer was also studied. It was found that damage during RDF decreases with the addition of fillers, but increases with the addition of the plasticizer. Finally, the damage evolution in the presence of two cavities was also studied, and was found that the interaction of stress fields around the cavities alters the damage occurring during RDF.

36 MATERIALS SCIENCE↗