Durable High-Power Membrane Electrode Assemblies with Low Pt Loading
Recent progress in developing and implementing Pt-alloy cathode catalysts and thin (10-15 micron) low resistance membranes has enabled high performance state of art (SOA) membrane electrode assembly (MEA) with low Pt loading. However, these high performing MEAs do not meet durability requirements, especially at peak power, because of complex degradation mechanisms that are sensitive to the materials, MEA design, and fuel cell operating strategy. Specifically, power degradation of the cathode occurs via Pt and Co dissolution as well as deterioration of O 2 transport properties. Additionally, thin membranes are subject to failure due to manufacturing defects in the adjacent gas diffusion media and electrodes and the formation of membrane-attacking radical species caused by high gas crossover. In this project led by General Motors LLC (GM), the objective was to enhance the durability of SOA MEA through optimization of operating conditions, instead of new materials development. Along with our project partners, we have mapped the impact of operating conditions on the durability of SOA MEA. Output of the project include a low Pt loading SOA MEA that exceeds Department of Energy (DOE) 2020 target of >1 W/cm 2 at rated power and pathway to achieve >5000 h of durability. Durability studies in the project provide a detailed understanding of failure modes and operating condition sensitivity on cathode and membrane failure, critical for defining operating conditions and hybridization strategies that can guide system controls to maximize low-Pt MEA life. The project also generated and validated degradation models that will provide future research direction, critical for guiding future cycles of automotive MEA development.