Phase evolution and mechanical performance of an ettringite-based binder during hydrothermal aging

Little is known about the performance of ettringite-based binders in hydrothermal conditions. This investigation aims to gain insights into the phase evolution and corresponding mechanical performance of an ettringite-based binder considering crystallization pressure caused by late-reaction products. Additionally, the role of fiber reinforcement on the strength retention of the binder was investigated. When aged at an elevated temperature under water-saturated conditions, hard-burned MgO hydrated to form brucite. The precipitation and growth of the brucite crystals led to a crystallization pressure of approximately 200 MPa calculated using thermodynamic modelling. Damage was observed after 4 months of aging with cracks in the microstructure and eventually a failure at the macro scale. Ettringite remained stable at 60 °C due to the water-saturated conditions. Polypropylene fiber delayed crack propagation and thus reduced the damage caused by crystallization pressure. The fiber improved the flexural performance of composite attaining deflection-hardening behavior regardless of aging conditions.

36 MATERIALS SCIENCE↗

DOE OSTI2021

On the retardation mechanisms of citric acid in ettringite-based binders

This study aims to obtain insights into the retardation mechanism of citric acid in an ettringite-based binder from ladle slag and gypsum. The hydration kinetics and phase assemblage of the binder were experimentally investigated and thermodynamically modelled. Additionally, the effects of citric acid on synthetic ettringite were studied to obtain further understanding of the interaction between this organic ligand and the crystal. Experimental results reveal that citric acid works as an inhibitor of ettringite's formation leading to the precipitation of monosulfate and gypsum; the ettringite surface blockage by citrate ligand effectively prevents precipitation of this crystal. This leads to an overestimation in the precipitation of ettringite in the thermodynamic model due to this kinetic barrier imposed by the ligand. Thermodynamic modelling suggests ettringite, monosulfate, aluminum hydroxide, and strätlingite as main hydrates in this binder, whereas an intermixed C–(A–)S–H gel was observed experimentally instead of strätlingite.

36 MATERIALS SCIENCE↗