High-Temperature Oxidation Study in a Multi-Oxidant Environment Using 18 O Tracer
The goal of this study was to use 18 O-enriched water to better understand the role of H 2 O in high-temperature oxidation. Seven model and three commercial M-Cr and M-Cr-Al alloys were studied in air with 10% of H 2 O at 800 °C for 5 h. Oxygen from water vapor was more reactive than oxygen from the air and 18 O enriched at the outermost layers of the formed Cr- and Al-rich oxides. Alloys with Al and/or Ti additions showed signs of internal oxidation but 18 O was not enriched inside the alloy in locations with internal oxidation. In conclusion, depending on the alloy Al content, the oxide went from Al oxidation beneath a chromia scale to external alumina scale formation.