DOE OSTI2024

Elucidation of Ce/Zr ratio effects on the physical properties and catalytic performance of CuO x /Ce y Zr 1− y O 2 catalysts

Although cerium oxide (CeO 2 ) is widely used as a catalyst support, its limited defect sites and surface oxygen vacancy/mobility should be improved. The incorporation of zirconium (Zr) in the cerium (Ce) lattice is shown to increase the number of oxygen vacancies and improve catalytic activity. Using a fixed surface density (SD) of copper (∼2.3 Cu atoms per nm 2 ) as a surface species, the role of the support (Ce y Zr 1−y O 2 (y = 1.0, 0.9, 0.6, 0.5, and 0.0)) and defect site effects in the CO oxidation reaction was investigated. Spectroscopic (e.g., Raman, XRD, XPS) and microscopic (e.g., SEM-EDX, HR-TEM) characterization techniques were applied to evaluate the defect sites, crystallite size, lattice parameters, chemical composition, oxidation states of elements and microstructure of the catalysts. Here, the CO oxidation reaction with varied CO : O 2 ratios (1 : 5, 1 : 1, and 1 : 0.5 (stoichiometric)) was used as a model reaction to describe the relationship between the structure and the catalytic performance of each catalyst. Based on the characterization results of Ce y Zr 1−y O 2 materials, the addition of Zr causes physical and chemical changes to the overall material. The inclusion of Zr into the structure of CeO 2 decreased the overall lattice parameter of the catalyst and increased the number of defect sites. The prepared catalysts were able to reach complete CO conversion (∼100%) at low temperature conditions (<200 °C), each showing varied reaction activity. The difference in CO oxidation activity was then analyzed and related to the structure, wherein Cu loading, surface oxygen vacancies, reduction–oxidation ability, CuO x –support interaction and oxygen mobility in the catalyst were the crucial descriptors.

36 MATERIALS SCIENCE↗

DOE OSTI2024

Unlocking High Capacity and Reversible Alkaline Iron Redox Using Silicate-Sodium Hydroxide Hybrid Electrolytes

Alkaline iron (Fe) batteries are attractive due to the high abundance, low cost, and multiple valent states of Fe but show limited columbic efficiency and storage capacity when forming electrochemically inert Fe 3 O 4 on discharging and parasitic H 2 on charging. Herein, sodium silicate is found to promote Fe(OH) 2 /FeOOH against Fe(OH) 2 /Fe 3 O 4 conversions. Electrochemical experiments, operando X-ray characterization, and atomistic simulations reveal that improved Fe(OH) 2 /FeOOH conversion originates from (i) strong interaction between sodium silicate and iron oxide and (ii) silicate-induced strengthening of hydrogen-bond networks in electrolytes that inhibits water transport. Furthermore, the silicate additive suppresses hydrogen evolution by impairing energetics of water dissociation and hydroxyl de-sorption on iron surfaces. In conclusion, this new silicate-assisted redox chemistry mitigates H 2 and Fe 3 O 4 formation, improving storage capacity (199 mAh g -1 in half-cells) and coulombic efficiency (94 % after 400 full-cell cycles), paving a path to realizing green battery systems built from earth-abundant materials.

36 MATERIALS SCIENCE↗

DOE OSTI2024

Revealing the Nature of Binary-Phase on Structural Stability of Sodium Layered Oxide Cathodes

The emergence of layered sodium transition metal oxides featuring a multiphase structure presents a promising approach for cathode materials in sodium-ion batteries, showcasing notably improved energy storage capacity. However, the advancement of cathodes with multiphase structures faces obstacles due to the limited understanding of the integrated structural effects. Herein, the integrated structural effects by an in-depth structure-chemistry analysis in the developed layered cathode system Na x Cu 0.1 Co 0.1 Ni 0.25 Mn 0.4 Ti 0.15 O 2 with purposely designed P2/O3 phase integration, are comprehended. The results affirm that integrated phase ratio plays a pivotal role in electrochemical/structural stability, particularly at high voltage and with the incorporation of anionic redox. In contrast to previous reports advocating solely for the enhanced electrochemical performance in biphasic structures, it is demonstrated that an inappropriate composite structure is more destructive than a single-phase design. The in situ X-ray diffraction results, coupled with density functional theory computations further confirm that the biphasic structure with P2:O3 = 4:6 shows suppressed irreversible phase transition at high desodiated states and thus exhibits optimized electrochemical performance. Finally, these fundamental discoveries provide clues to the design of high-performance layered oxide cathodes for next-generation SIBs.

36 MATERIALS SCIENCE↗

DOE OSTI2024

A Comparative Study of Degradation Behaviors of LiFePO 4 , LiMn 2 O 4 , and LiNi 0.8 Mn 0.1 Co 0.1 O 2 in Different Aqueous Electrolytes

Aqueous Li-ion batteries (ALIBs) are an important class of battery chemistries owing to the intrinsic non-flammability of aqueous electrolytes. However, water is detrimental to most cathode materials and could result in rapid cell failure. Identifying the degradation mechanisms and evaluating the pros and cons of different cathode materials are crucial to guide the materials selection and maximize their electrochemical performance in ALIBs. Here, in this study, we investigate the stability of LiFePO 4 (LFP), LiMn 2 O 4 (LMO) and LiNi 0.8 Mn 0.1 Co 0.1 O 2 (NMC) cathodes, without protective coating, in three different aqueous electrolytes, i.e., salt-in-water, water-in-salt, and molecular crowding electrolytes. The latter two are the widely reported "water-deficient electrolytes." LFP cycled in the molecular crowding electrolyte exhibits the best cycle life in both symmetric and full cells owing to the stable crystal structure. Mn dissolution and surface reduction accelerate the capacity decay of LMO in water-rich electrolyte. On the other hand, the bulk structural collapse leads to the degradation of NMC cathodes. LMO demonstrates better full-cell performance than NMC in water-deficient aqueous electrolytes. LFP is shown to be more promising than LMO and NMC for long-cycle-life ALIB full cells, especially in the molecular crowding electrolyte. However, none of the aqueous electrolytes studied here provide enough battery performance that can compete with conventional non-aqueous electrolytes. This work reveals the degradation mechanisms of olivine, spinel, and layered cathodes in different aqueous electrolytes and yields insights into improving electrode materials and electrolytes for ALIBs.

36 MATERIALS SCIENCE↗

DOE OSTI2023

The NO reduction by CO over NiO x /CeO 2 catalysts with a fixed Ni surface density: pretreatment effects on the catalyst structure and catalytic activity

NiO x /CeO 2 catalysts have shown promising results in various catalytic reactions, including the NO reduction by CO. Here, in this study, we investigated the effect of oxidation and reduction treatments on the NO reduction by CO over pretreated NiO x /CeO 2 catalysts. A series of oxidized and reduced supported NiO x catalysts were synthesized in two steps: (1) the pretreatment of CeO 2 supports at different temperatures (400, 500, and 700 °C) under oxidizing and reducing conditions and (2) the synthesis of NiO x /CeO 2 catalysts by an incipient wetness impregnation method (IWI) with a fixed surface density of 5.3 Ni per nm 2 under specific conditions (oxidation/reduction) applied during the CeO 2 treatment. The prepared catalysts were characterized via BET, ICP/OES, Raman, XPS, and XRD to understand their physicochemical properties. The results showed that as the pretreatment temperature increased, the physicochemical properties of NiO x /CeO 2 catalysts were changed: a decreased specific surface area (SSA), decreased oxygen vacancy/defect sites, and an increased crystallite size. The oxidized NiO x /CeO 2 catalyst at a lower pretreatment temperature displayed a better catalytic activity, indicating that the physicochemical properties of the catalysts were key factors in enhancing the catalytic activity. To understand the intermediate species and reaction mechanism during the NO reduction by CO, an in situ DRIFTS study was performed and a possible reaction mechanism was also discussed.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Multielectrode electrochemical cell for in situ structural characterization of amorphous thin-film catalysts using high-energy X-ray scattering

A multielectrode-based electrochemical cell allows the structural characterization of an amorphous thin-film water oxidation catalyst under various electrochemical potentials using high-energy X-ray scattering and atomic pair distribution function (PDF) techniques. A multielectrode with five electrodes provides a sufficiently low background signal to enable high-energy X-ray scattering (HEXS) measurements and amplifies the extremely low HEXS signals from samples for high-resolution PDF analysis of in situ data from thin-film catalysts. Glassy carbon (GC) creates a relatively low intensity HEXS pattern and is used as a working electrode. Instead of a three-dimensional (3D) porous electrode architecture, the flat geometry of the electrode enables various deposition techniques to be used for the preparation of a highly conductive metal oxide layer. PDF analysis demonstrates high spatial resolution for a 230 nm thick amorphous iridium oxide film deposited on two roughened 60 µm thick GC electrodes. The PDF analysis resolves the domain size and distinguishes changes in fine structure which are directly correlated with the structure and function of the catalysts. In conclusion, the results bring the opportunity to analyze the structure of nanometre-scale amorphous thin-film catalysts in an electrolyte-compatible and compact 3D-printed electrochemical cell in a three-electrode configuration.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Chloride Insertion Enhances the Electrochemical Oxidation of Iron Hydroxide Double-Layer Hydroxide into Oxyhydroxide in Alkaline Iron Batteries

Rechargeable alkaline iron batteries that constitute environmentally benign electrolytes and earth-abundant industrial materials are desirable green solutions for large-scale energy storage. As one of the most abundant metal elements in the earth’s crust, iron (Fe) can satisfy nearly all criteria for low-cost and safe battery electrodes. However, challenges in achieving reversible Fe redox impede their extensive implementation in modern energy supply systems. Here, this study revealed that Cl-anion insertion into Fe(OH) 2 layered double hydroxide (LDH) formed a green rust intermediate phase with the formula [Fe 2 2+ Fe 1 3+ (HO – ) 6 ] + [Cl] – , which assisted a high Fe(OH) 2 /FeOOH conversion reaction (64.7%) and improved cycling stability. This new iron redox chemistry was validated by operando X-ray diffraction, electrochemical testing, X-ray absorption spectroscopy (XAS), X-ray photoelectron spectroscopy (XPS) analysis, scanning transmission electron microscopy–energy-dispersive X-ray spectroscopy (STEM-EDS) mapping, and molecular dynamics (MD) simulations. Our study provides new insight into designing LDH materials for high-capacity alkaline iron batteries.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Boosting the interfacial superionic conduction of halide solid electrolytes for all-solid-state batteries

Designing highly conductive and (electro)chemical stable inorganic solid electrolytes using cost-effective materials is crucial for developing all-solid-state batteries. Here, we report halide nanocomposite solid electrolytes (HNSEs) ZrO 2 (-ACl)-A 2 ZrCl 6 (A = Li or Na) that demonstrate improved ionic conductivities at 30 °C, from 0.40 to 1.3 mS cm -1 and from 0.011 to 0.11 mS cm -1 for Li + and Na + , respectively, compared to A 2 ZrCl 6 , and improved compatibility with sulfide solid electrolytes. The mechanochemical method employing Li 2 O for the HNSEs synthesis enables the formation of nanostructured networks that promote interfacial superionic conduction. Via density functional theory calculations combined with synchrotron X-ray and 6 Li nuclear magnetic resonance measurements and analyses, we demonstrate that interfacial oxygen-substituted compounds are responsible for the boosted interfacial conduction mechanism. Compared to state-of-the-art Li 2 ZrCl 6 , the fluorinated ZrO 2 -2Li 2 ZrCl 5 F HNSE shows improved high-voltage stability and interfacial compatibility with Li 6 PS 5 Cl and layered lithium transition metal oxide-based positive electrodes without detrimentally affecting Li + conductivity. We also report the assembly and testing of a Li-In||LiNi 0.88 Co 0.11 Mn 0.01 O 2 all-solid-state lab-scale cell operating at 30 °C and 70 MPa and capable of delivering a specific discharge of 115 mAh g -1 after almost 2000 cycles at 400 mA g -1 .

36 MATERIALS SCIENCE↗

DOE OSTI2023

Structural mapping and tuning of mixed halide ions in amorphous sulfides for fast Li-ion conduction and high deformability

Amorphous sulfides are among the most promising candidates for solid electrolytes (SEs) owing to their excellent deformability and acceptable Li-ion conductivity (σion) at room temperature. However, the complex atomic structure of these amorphous materials without long-range ordering results in a lack of structural understanding and difficulties in tuning material properties. Here, in this study, we performed structural mapping of glassy sulfide SEs composed of various anion clusters using a combinatorial atomic level analysis of synchrotron X-ray-based pair distribution function (PDF) and reverse Monte-Carlo (RMC) methods, demonstrating the potential to tune σ ion in glass SEs. First, we prepared a new glassy sulfide with a mixed anion framework of two halogens (Br and I) as atomic anions, with PS 4 3- molecular anions in a Li 2 S–P 2 S 5 -based glass SE. At a specific Br content, [(Li 2 S) 0.658 (LiI 0.9 LiBr 0.1 ) 0.342 ] 0.825 [P 2 S 5 ] 0.175 recorded a σ ion of 2.27 mS cm -1 , the highest value for any glass sulfides reported to date; however, its elastic modulus was still suppressed to 14.48 GPa. PDF and RMC calculations successfully provided structural mapping of anion clusters, including two halogens. Molecular dynamics simulations of each composition confirmed that flexible coordination caused by the rattling of small polarizable Br ions in the mixed halogens of glassy SEs contributed to the superior σ ion . Our results may provide new insights into the design of superior glassy SEs that play key roles in all-solid-state batteries requiring fast Li-ion conduction and high deformability.

36 MATERIALS SCIENCE↗