NASA NTRS1993

Indentation-flexure and low-velocity impact damage in graphite epoxy laminates

Static indentation-flexure and low-velocity impact tests were performed on quasi-isotropic and cross-ply graphite/epoxy composite laminates. The load-deflection relations in static tests and impact force history in impact tests were recorded. The damage was assessed by using ultrasonic C-scanning and photo-micrographic techniques. Some features of the static behavior were explained by simple analytical models. A good correlation existed between the load-deflection curves for static and impact loading. It was found that results from a few static indentation-flexure tests can be used to predict the impact force history and delamination radius in composite laminates due to low-velocity impact.

Kwon, Young S.↗

NASA NTRS1992

Indentation-flexure and low-velocity impact damage in graphite/epoxy laminates

Static indentation and low velocity impact tests were performed on quasi-isotropic and cross ply graphite/epoxy composite laminates. The load deflection relations in static tests and impact force history in the impact tests were recorded. The damage was assessed by using ultrasonic C-scanning and photomicrographic techniques. The static behavior of the laminates and damage progression during loading, unloading, and reloading were explained by a simple plate delamination model. A good correlation existed between the static and impact responses. It was found that results from a few static indentation-flexture tests can be used to predict the response and damage in composite laminates due to a class of low velocity impact events.

Kwon, Young S.↗