DOE OSTI2024

Composite coatings from polycarbosilane derived SiC and Al/SiC cermet active fillers as protective barriers against steel corrosion

Stainless steel is used throughout the world as a structural material. However, it undergoes corrosion damage when exposed to extremely corrosive media, such as the marine environment. An alternative to solve this problem lies in the development of coatings that can withstand extreme conditions but also be easily deposited with inherently corrosion-resistant materials such as silicon carbide (SiC). The present study shows a simple method to produce Al/SiC cermet powders by attrition milling. The resulting cermet powders with a metallic matrix and hemispherical morphology, were employed as fillers in polycarbosilane (PCS) solutions that were sprayed on A304 stainless steel substrates. Al/SiC composite coatings were produced after heating the sprayed suspensions at 700 °C for 1 h in Ar atmosphere. The resulting composite coatings exhibited low surface energies (< 35 mN/m), water contact angles of 53°, and adhesion strength of up to 30 MPa. Finally, corrosion tests were performed in a cyclic corrosion test chamber, showing that these coatings effectively reduced the corrosion rate of stainless steel by 87%, reaching corrosion rate values of 0.007 g/cm 2 year.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Superhydrophobic to superhydrophilic wettability transition of functionalized SiO 2 nanoparticles

The superhydrophobic and superhydrophilic surfaces and their transitions are of great interest for the production of self-cleaning, anti-biofouling, or corrosion-resistant materials. This research reports the wettability transition from superhydrophobic to superhydrophilic SiO 2 nanoparticles functionalized with 1H, 1H, 2H, 2H-perfluorooctyltriethoxysilane (POTS) and induced by temperature. The functionalization of these nanoparticles was confirmed by Fourier transform infrared spectroscopy, X-ray photoelectron spectroscopy (XPS), and transmission electron microscopy. The functionalization of SiO 2 nanoparticles with POTS resulted in superhydrophobic surfaces with water contact angles up to 157°. A sudden transition to superhydrophilic behavior with water contact angles (WCA) below 5° was observed when the sample was heat-treated at 500 °C, despite the presence of fluorine on the surface of these nanoparticles, as confirmed by XPS and transmission electron microscopy. XPS suggested that the transition was caused by the change in orientation of the fluoroalkyl molecules and its partial decomposition due to the loss of the –CF 3 group, resulting in shorter chains with a tail-end group with C–O bonds, which promoted the superhydrophilicity.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Influence of SiC microstructure on its corrosion behavior in molten FLiNaK salt

The influence of the microstructure on the corrosion rate of three monolithic SiC samples in FLiNaK salt at 900 °C for 250 h was studied. The SiC samples, labeled as SiC-1, SiC-2, and SiC-3, had corrosion rates of 0.137, 0.020, and 0.043 mg/cm 2 h, respectively. Compared with grain size and the presence of special grain boundaries (i.e., Σ3), the content of high-angle grain boundaries (HAGBs) appeared to have the strongest influence on the corrosion rate of SiC in FLiNaK salt, since the corrosion rate increased six times as the concentration of high-angle grain boundaries increased from 19 to 32% for SiC-2 and SiC-1, respectively. The results here stress the importance of controlling the content of HAGBs during the production process of SiC.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Comparative study of three yttrium organometallic compounds for the stabilization of the cubic phase in YSZ deposited by PE-CVD

In this work, the efficiencies of three organometallic yttrium precursors used to produce YSZ coatings by plasma-enhanced chemical vapor deposition were studied. Yttrium (III) acetylacetonate, Y (acac) 3 , yttrium (III) hexafluoroacetylacetonate, Y (acacF 6 ) 3 , and yttrium (III) tris(2,2,6,6-tetramethyl-3,5-heptanedionate), Y (tmhd) 3 , were used to stabilize the cubic phase in zirconia deposited at temperatures from 500 to 800 °C. Our results showed that at temperatures between 500 and 600 °C, Y (tmhd) 3 appeared to be the most efficient dopant as it introduced the highest concentration of yttria (1–2.7 mol%) with only 6.4–5.6 at.% carbon. However, at 700 and 800 °C, Y (acac) 3 introduced twice as much yttria (8–15 mol%) as Y (tmhd) 3 with almost the same amount of carbon (5.4–3 at.%). Conversely, Y (acacF6)3 was the least efficient as it maintained a low concentration of yttria of around 0.7–1.8 mol% with 3.6–8.2 at.% carbon for all the deposition temperatures. Among these precursors, only Y (acac) 3 surpassed 8 mol% yttria and achieved a fully stabilized cubic phase at 800 °C, with the remaining samples stabilizing only the tetragonal phase. The tetragonal phase was stabilized due to the formation of crystallites of around 10 nm. The observed difference in the efficiency of the three precursors was correlated to important differences in their decomposition behavior as observed by mass spectrometry and thermogravimetry/differential scanning calorimetry.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Controlled Reduction of Graphene Oxide Using Sulfuric Acid

Sulfuric acid under different concentrations and with the addition of SO 3 (fuming sulfuric acid) was studied as a reducing agent for the production of reduced graphene oxide (RGO). Three concentrations of sulfuric acid (1.5, 5, and 12 M), as well as 12 M with 30% SO 3 , were used. The reduction of graphene oxide increased with H 2 SO 4 concentration as observed by Fourier-transformed infrared spectroscopy and X-ray photoelectron spectroscopy. It was observed that GO lost primarily epoxide functional groups from 40.4 to 9.7% and obtaining 69.8% carbon when using 12 M H 2 SO 4 , without leaving sulfur doping. Additionally, the appearance of hexagonal domain structures observed in transmission electron microscopy and analyzed by selected area electron diffraction patterns confirmed the improvement in graphitization. Although the addition of SO 3 in H 2 SO 4 improved the GO reduction with 74% carbon, as measured by XPS, the use of SO 3 introduced sulfur doping of 1.3%. RGO produced with sulfuric acid was compared with a sample obtained via ultraviolet (UV) irradiation, a very common reduction route, by observing that the RGO produced with sulfuric acid had a higher C/O ratio than the material reduced by UV irradiation. This work showed that sulfuric acid can be used as a single-step reducing agent for RGO without sulfur contamination.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2020

Polymer-derived SiC/C/Al environmental barrier coatings on carbon steel

Carbon steel is a widely used structural material; however, it lacks corrosion resistance in water environments. An alternative approach to overcome this challenge is to implement the deposition of inherently corrosion-resistant ceramic coatings. SiC/C/Al coatings were developed at 700°C, using polycarbosilane in combination with Al and C, which were included as active and passive fillers, respectively. Here, we show that it is necessary to use Al particle sizes below 10 µm for them to function as an active filler below 900°C. Owing to their laminar microstructure, these coatings showed a cohesive delamination with an adhesion strength of 10 MPa. Results demonstrated that these coatings were able to reduce the corrosion of carbon steel in saline water by 99.7%, with corrosion rates of 38.33 mpy for carbon steel, and 0.099 and 0.155 mpy for SiC/C and SiC/C/Al (10 µm) coatings, respectively.

36 MATERIALS SCIENCE↗