Dynamic substrate reactions during room temperature heavy ion irradiation of CoCrCuFeNi high entropy alloy thin films

Abstract High entropy alloys (HEAs) are promising materials for various applications including nuclear reactor environments. Thus, understanding their behavior under irradiation and exposure to different environments is important. Here, two sets of near-equiatomic CoCrCuFeNi thin films grown on either SiO 2 /Si or Si substrates were irradiated at room temperature with 11.5 MeV Au ions, providing similar behavior to exposure to inert versus corrosion environments. The film grown on SiO 2 had relatively minimal change up to peak damage levels above 500 dpa, while the film grown on Si began intermixing at the substrate–film interface at peak doses of 0.1 dpa before transforming into a multi-silicide film at higher doses, all at room temperature with minimal thermal diffusion. The primary mechanism is radiation-enhanced diffusion via the inverse Kirkendall and solute drag effects. The results highlight how composition and environmental exposure affect the stability of HEAs under radiation and give insights into controlling these behaviors.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Identifying chemically similar multiphase nanoprecipitates in compositionally complex non-equilibrium oxides via machine learning

Abstract Characterizing oxide nuclear fuels is difficult due to complex fission products, which result from time-evolving system chemistry and extreme operating environments. Here, we report a machine learning-enhanced approach that accelerates the characterization of spent nuclear fuels and improves the accuracy of identifying nanophase fission products and bubbles. We apply this approach to commercial, high-burnup, irradiated light-water reactor fuels, demonstrating relationships between fission product precipitates and gases. We also gain understanding of the fission versus decay pathways of precipitates across the radius of a fuel pellet. An algorithm is provided for quantifying the chemical segregation of the fission products with respect to the high-burnup structure, which enhances our ability to process large amounts of microscopy data, including approaching the atomistic-scale. This may provide a faster route for achieving physics-based fuel performance modeling.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Monte Carlo simulations of Cu/Ni–Si–Mn co-precipitation in duplex stainless steels

First-Passage Kinetic Monte Carlo (FPKMC) simulations of species migration in duplex stainless steels were performed in order to establish relationships between alloy content, segregation behavior, and the formation of Ni-Si-Mn rich particles in cast duplex stainless steels during thermal aging. The Ni-Si-Mn-rich second phase forms after extended aging at reactor operating temperatures and degrades alloy properties. Simulations of Ni-Si-Mn cluster formation were validated through comparison with experimental results obtained through Atom Probe Tomography (APT) on similar alloy compositions, identifying several trends. First, Cu promotes the formation of Ni-Si-Mn clusters, but only when Ni or Mn prefer segregation to the surface of Cu particles; without the segregation of these species, the critical composition for the clusters to form was not achieved. Second, the width of precipitate-denuded zones near ?/d interfaces increases with decreasing Cu content. This finding was in strong agreement with APT results, further validating our model. Finally, our model predicts that Ni-Si-Mn cluster formation will be the most extensive when the Si:Mn ratio is approximately 1:1 and the least extensive when one of these key elements is less concentrated (Mn = 0.5 at.% or Si = 0.5 at.%). The implications of these results on how to improve alloy properties are discussed.

Cu co-precipitation, Atom probe tomography (APT), ↗