NASA NTRS1992

Evaluation of high temperature dielectric films for high voltage power electronic applications

Three high temperature films, polyimide, Teflon perfluoroalkoxy and poly-P-xylene, were evaluated for possible use in high voltage power electronic applications, such as in high energy density capacitors, cables and microelectronic circuits. The dielectric properties, including permittivity and dielectric loss, were obtained in the frequency range of 50 Hz to 100 kHz at temperatures up to 200 C. The dielectric strengths at 60 Hz were determined as a function of temperature to 250 C. Confocal laser microscopy was performed to diagnose for voids and microimperfections within the film structure. The results obtained indicate that all films evaluated are capable of maintaining their high voltage properties, with minimal degradation, at temperatures up to 200 C. However, above 200 C, they lose some of their electrical properties. These films may therefore become viable candidates for high voltage power electronic applications at high temperatures.

Suthar, J. L.↗

NASA NTRS1992

Dielectric breakdown studies of Teflon perfluoroalkoxy at high temperature

Teflon perfluoroalkoxy (PFA) was evaluated for use as a dielectric material in high-temperature high-voltage capacitors for space applications. The properties that were characterized included the dc dielectric strength at temperatures up to 250 C and the permittivity and dielectric loss as a function of frequency, temperature and voltage. To understand the breakdown mechanism taking place at high temperatures, the pre-breakdown discharge and conduction currents, and the dependence of dielectric strength on thickness of the film were determined. Confocal laser microscopy was performed to diagnose for microimperfections within the film structure. The results obtained show a significant decrease in the dielectric strength and an increase in dielectric loss with an increase in temperature, suggesting that impulse thermal breakdown could be a responsible mechanism in PFA film at temperatures above 150 C.

Suthar, J. L.↗

NASA NTRS1992

High temperature dielectric properties of Apical, Kapton, Peek, Teflon AF, and Upilex polymers

Reliable lightweight systems capable of providing electrical power at the magawatt level are a requirement for future manned space exploration missions. This can be achieved by the development of high temperature insulating materials which are not only capable of surviving the hostile space environment but can contribute to reducing the mass and weight of the heat rejection system. In this work, Apical, Upilex, Kapton, Teflon AF, and Peek polymers are characterized for AC and DC dielectric breakdown in air and in silicone oil at temperatures up to 250 C. The materials are also tested in terms of their dielectric constant and dissipation factor at high temperatures with an electrical stress of 60 Hz, 200 V/mil present. The effects of thermal aging on the properties of the films are determined after 15 hours of exposure to 200 and 250 C, each. The results obtained are discussed and conclusions are made concerning the suitability of these dielectrics for use in capacitors and cable insulations in high temperature environments.

Hammoud, A. N.↗